Effect of oxygenation on electrocatalysis of La0.6Ca0.4CoO3−x in bifunctional air electrode

A vacuum-annealed La_0.6Ca_0.4CoO_3−x was consecutively oxygenated in air at temperatures decreasing from 800 to 100 °C, and its electrocatalytic activities for oxygen reduction and evolution were then measured as a function of the oxygenation temperature. The valence of Co cation, changing between +2 and +3, was found susceptible to annealing either in vacuum or air. The catalytic activities initially decrease monotonically as the oxygenation temperature was decreased from 800 to 300 °C, as a result of increasing oxygen content, and then rise abruptly with the oxygen reduction activity reaching a maximum at 200 °C and the oxidation activity at 150 °C. X-ray photoelectron spectroscopy analysis indicated that the enhancements by the low-temperature oxygenation involved increased OH coverage and less charged cations at surface. The results clearly reveal the importance of the post-calcination annealing process for optimizing the performance of La_0.6Ca_0.4CoO_3−x in air electrode applications.     

天然气空气绝热转化制合成气催化剂研究

制备了天然气空气绝热转化催化剂,采用固定床反应器进行稳定性评价试验,对反应前后的催化剂进行了分析表征。结果说明,天然气和空气绝热转化反应放热形成的高温对催化剂有烧结作用,使催化剂晶体结构发生了变化,起活性作用的金属镍和氧化铝载体转化为镍铝尖晶石结构的物质。进一步的试验表明,在1050～1300℃的温度可以把催化剂的晶体结构改变。     

一种制氢预转化催化剂还原的新方法

对上海高桥分公司2×10~4m~3/h(标准状态)制氢装置原设计的预转化催化剂还原流程进行了改进。先跳开预转化反应器,利用转化炉制取氢气,再用自产的高纯氢气代替重整氢,对预转化催化剂进行单独升温还原,避免了催化剂在还原初期因发生甲烷化反应而超温失活的问题,使催化剂具有更好的活性和稳定性。     

凝胶成型法制备加氢催化剂载体的研究与工业化生产

采用凝胶成型法制备加氢催化剂载体，并进行了工业放大试验。通过BET、NH3-TPD、H2-TPR等表征手段及实际的加氢反应性能评价对凝胶成型法制备的载体及加氢催化剂与常规方法进行对比分析，结果表明，采用凝胶成型法所制得的载体及催化剂均具有较高的孔体积和比表面积、较低的堆密度，其机械强度可满足工业要求，总酸量及中强酸酸量得到提升，催化剂活性组分与载体强结合力得到削弱，金属利用率提高，应用性能明显优于传统方法制备的加氢催化剂载体。通过该方法完成了加氢催化剂载体的工业生产，所生产的载体应用于天津院THDS-3加氢精制催化剂取得了良好的工业应用效果。     

Cd-ZSM-5沸石催化剂的制备、表征和芳构化催化性能

采用离子交换、浸渍和混合三种方法制备镉改性ZSM-5沸石催化剂,考察了改性方法和镉含量对催化剂的表面酸性和Cd状态以及芳构化性能的影响。结果表明,加入镉降低了B酸性,Cd~(2+)与沸石结合形成了L_(1612)酸中心,其生成量取决于改性方法和Cd含量,并与芳构化活性提高有直接关系。     

聚合物载体－稀土金属络合物的研究 ⅩⅢ．聚［苯乙烯－甲基丙烯酸β（甲基亚硫酰基）乙酯］的结构与其稀土金属络合物催化丁二烯聚合的活性

从测得的竞聚率计算了单体链节在聚［苯乙烯－甲基丙烯酸β（甲基亚硫酰基）乙酯］（ＰＳＭ）中的序列分布。苯乙烯（Ｓ）或甲基丙烯酸β（甲基亚硫酰基）乙酯（Ｍ）的长序列的概率随着ＰＳＭ中相应单体含量的增加而增加。对于Ｓ和Ｍ摩尔分数大致相等的ＰＳＭ，单体链节的长序列分布函数值相接近。用与此结构相近的ＰＳＭ合成的稀土金属络合物，其催化活性不佳。在Ｍ短序列分布和Ｓ长序列分布较高的情况下，络合物的催化活性最好。所得聚丁二烯的微观结构与ＰＳＭ中单体单元的分布无关。     

Nitric oxide reduction and carbon monoxide oxidation over carbon-supported copper-chromium catalysts

Carbon supported copper-chromium catalysts are shown to be very active for both the reduction of nitric oxide with carbon monoxide and the oxidation of carbon monoxide with oxygen. Mixed copper-chromium oxide active phases have good activity in the simultaneous removal of nitric oxide and carbon monoxide from exhaust gases. The influence of several catalyst variables has been investigated. The activity per volume of catalyst increases with increasing loading, while the intrinsic activity shows a maximum around C/M=100−50. An optimum catalyst for nitric oxide reduction and carbon monoxide oxidation has a copper/chromium ratio of 2/1. The apparent activation energy for the carbon monoxide oxidation over carbon supported copper-chromium catalysts is 77 kJ/mol, suggesting that the Cu---O bond rupture is the rate-limiting process. The reduction of nitric oxide takes place at higher temperatures. Since all catalysts have a low selectivity for molecular nitrogen formation at lower temperatures, the dissociation of nitric oxide is probably rate determining, resulting in a slightly reduced catalyst system. In an excess of carbon monoxide the reaction is first-order in nitric oxide and zero-order in carbon monoxide. Moisture inhibits the reaction by reversible competitive adsorption, whereas carbon dioxide does not. Oxygen completely inhibits the reduction of nitric oxide due to the more rapid reoxidation of the catalytic sites compared to nitric oxide. Therefore, the reduction of nitric oxide takes place only when all oxygen has been converted and, hence, is shifted to higher temperatures. As a possible consequence, the production of nitrous oxide is reduced. Nitric oxide and molecular oxygen react preferentially with carbon monoxide, so, in an excess of oxidizing component, gasification of the carbon support occurs at higher temperatures after carbon monoxide has been completely consumed.     

中变催化剂失活典型事例剖析

通过2起中变催化剂失活的事件，从理论上剖析其根源，并探讨防范的对策。     

沸石加氢处理催化剂的制备方法

考察了渣油加氢处理催化剂制备过程中引入一种低硅铝比沸石的情况，它不仅提高催化剂的酸性，而且由于引入的分子筛孔径集中，最终使催化剂具有集中的孔分布，弥补了制备高活性催化剂采用混捏法的不足，制备出来的催化剂性能更优异。     

合成直链烷基苯的锆磷铝固体酸催化剂 I.催化剂合成及其影响因素

合成了一系列用于苯与直链烯烃烷基化反应的含有杂原子的磷铝分子筛固体酸催化剂 (MeZrAPO 5 ) ,同晶取代磷铝分子筛骨架中磷和铝的杂原子包括锆和至少一种选自硅、硼、镓、锗、铁、镁、锡等的元素。考察了晶化温度、晶化时间、杂原子种类、铝源等因素对催化剂合成的影响 ,探索了合成样品中模板剂脱除的最佳条件。结果表明 ,晶化温度高于 15 0℃、n(TEA) /n(Al2 O3 )≥ 1 5以及加入Zr原子都有利于直接生成MeZrAPO 5晶相 ;用小晶粒和高结晶度的铝源合成时 ,分子筛的结晶度高。