Oxygen glow discharge experiment to remove deposited layers and to release trapped hydrogen isotopes in HT-7 superconducting tokamak

An experiment to remove re-deposited layers and to release hydrogen using a glow discharge in oxygen (O-GDC) has been performed in the HT-7 superconducting tokamak. In the absence of magnetic fields, the O-GDC wall conditioning had produced rapid, controlled co-deposit removal. Average removal rates, 5.2 × 10²² H-atoms/h, 5.65 × 10²¹ D-atoms/h and 5.53 × 10²² C-atoms/h, respectively, were obtained during 145 min O-GDC experiment in the pressure range 0.5-1.5 Pa. The corresponding removal rate of co-deposited films was ∼1.19 μm/day (26.5 g/day for carbon) based on an area of 12 m². Compared to thermo-oxidation and O-ICR experiment, high pressure O-GDC wall conditioning promoted the oxidation and improved the C and D atoms removal. In the O-GDC experiment, the removal rates of H-atoms and D-atoms as H₂O, HDO and D₂O were higher than that of H₂ and D₂ by factors of about 20 and 50, respectively. During the 145 min O-GDC experiment, about 14.5% O-atoms were converted into carbon oxides and hydroxides, and about 5.37 × 10²² O-atoms were adsorbed on the walls corresponding to a coverage of 4.5 × 10²¹ O/m² on an wall area of 12 m². In a 100 min helium glow discharge (He-GDC) following the O-GDC experiment, 1.53 × 10²² O-atoms, about 28.5% oxygen retained on the walls, were removed. The removal rate of H-atoms in He-GDC cleaning after O-GDC experiment was lower than that in He-GDC cleaning before O-GDC experiment, which indicates that the O-GDC wall conditioning had effectively reduced hydrogen retention on the walls.     

Influence of pH on the passivation behavior of 254SMO stainless steel in 3.5% NaCl solution

The potentiodynamic polarization measurement of 254SMO stainless steel (UNS 31254) was conducted in 3.5% NaCl solutions with pH ranging from 0.1 to 5. The results indicated that this stainless steel offered excellent pitting corrosion resistance in corrosive environments. Further, it also exhibited various features on the polarization curves in different pH solutions. The electrochemical constant-potential passivation treatment performed at different pH followed by XPS analysis revealed that the primary constituents of the outermost layer of the passive films formed in the weak (pH 5) and strong (pH 0.8) acid solutions are iron oxides and Cr₂O₃ and Cr(OH)₃, respectively. Molybdenum oxides, primarily in the six-valence state, existed in the outermost layer of the passive film. Only very weak signals corresponding to that of nickel oxides were detected in the film formed in the weak acid (pH 5) solution. The ICP-MS analyses indicated selective dissolution of a significant amount of Fe and a few Mo and Ni ions during the passivation treatment in the strong acid (pH 0.8) solution. No Cr dissolution was observed; this indicated that the Cr in the film is relatively stable. XPS depth profiling results showed that a similar bilayer-structured film was formed in both the solutions (pH 0.8 and 5); the outer layer of this film is primarily composed of Cr(OH)₃ and Mo(VI), and the inner layer, Cr₂O₃ and Mo(IV). The results of the examinations of passive film formations and dissolution by XPS and ICP-MS were consistent with the polarization curves.     

Pressure infiltration of boron nitride preforms with molten aluminum

The infiltration of compacted cubic BN (cBN) with molten aluminum has been investigated as a potential route for a cheap and easy method of manufacturing cBN/metal composites. CBN compacts have been infiltrated with molten Al at a temperature between 670 and 800 °C and pressure of 15 MPa in vacuum. At these temperatures no pronounced interactions between hexagonal and cubic BN with Al was observed, allowing the complete infiltration of cBN with 12 μm mean grain size. After infiltration at 800 °C, the temperature was increased without pressure to convert aluminum into borides and AlN. The hardness of the resulting materials depends on the content of hexagonal, cubic BN and the rate of conversion of Al into borides and AlN. The infiltration height of less than 1 mm obtained from infiltrating the 3 μm cBN powder green compacts gave a hardness of 22.0 ± 0.6 GPa after heat treatment.     

La doping effects on intergrowth Bi2WO6–Bi3TiNbO9 ferroelectrics

La doping effects on intergrowth Bi₂WO₆–Bi₃TiNbO₉ ferroelectric ceramics were studied by X-ray diffraction, electron probe microanalysis and dielectric spectroscopy. It was found that the La³⁺ distribution, ferroelectric phase transition and dielectric relaxation behavior are apparently affected by La doping. With increasing La³⁺ content, the site of dopant ion varies, the grain growth of Bi₅TiNbWO₁₅ is restrained, the Curie temperature is reduced and broadened. Furthermore, two dielectric relaxation loss peaks were observed both in temperature and frequency spectra. The calculated relaxation parameters revealed the oxygen vacancy related to the relaxation process.     

局域网语音实时传输的实现

语音实时传输是语音聊天软件的核心技术。文中在分析语音实时传输原理的前提下,探讨了局域网语音实时传输的设备的初始化、内存分配、语音录制、播放和传输等具体方法,并以C Builder6.0提供的控件为基础,以API函数给为工具,给出了局域网实时语音聊天的具体实例,实现了局域网用户间的语音实时传输。     

Kanga(ROO): Handling the micro-DST of the BaBar experiment with ROOT

A system based on ROOT for handling the micro-DST of the BaBar experiment is described. The purpose of the Kanga system is to have micro-DST data available in a format well suited for data distribution within a world-wide collaboration with many small sites. The design requirements, implementation and experience in practice after three years of data taking by the BaBar experiment are presented.     

基于DSP的实时地面裂缝检测系统平台的设计

随着我国高速公路建设的快速发展，公路的维护工作已变得十分重要。本论文针对如何在高速环境下实时地检测地面裂缝这一课题提出了基于单片先进数字信号处理器TMS320C6201的实时处理解决方案，并重点介绍了系统硬件平台及软件设计。     

基于IP视频监控系统云台控制的设计与实现

I2C总线和PCI_XIO是Philips公司最新DSP芯片PNX1302的两个常用接口.文中介绍了采用上述两个接口设计与实现基于IP视频监控系统的云台控制方法以及比较.基于I2C总线的云台控制方法是利用PNX1302 DSP芯片所集成的I2C总线,根据I2C总线的工作原理、传输速率以及云台控制信息比特数少的综合因素考虑实现的.基于PCI_XIO接口的云台控制方法是根据PNX1302 DSP芯片的PCI总线接口为实现8 bit数据传输而特别设计的PCI_XIO接口实现的.     

大功率柴油机连杆三维精细分析

连杆作为柴油机的关键零部件，其刚度和强度对于柴油机的性能和功率的提高起到至关重要的作用。采用MSC／MARC程序及三维多体接触的方法，对G32柴油机连杆的应力场和位移场进行了数值模拟。进而为降低机械负荷、改善应力分布和进一步强化奠定基础。     

Behaviour of ±45° glass/epoxy filament wound composite tubes under quasi-static equal biaxial tension–compression loading: experimental results

The primary aim of this paper is to present results describing in detail the behaviour of ±45° E-glass/MY750 (GRP) tubes, of various wall thicknesses, subjected to equal biaxial tension–compression loading, generated under combined internal pressure and axial compression. The role played by the non-linear lamina shear has also been assessed by comparing various shear stress–strain curves for embedded laminae (extracted from tests on ±45° tubes subjected to circumferential: axial stress ratios SR=1:0, 1:−1 and 2.3:−1) with that of an ‘isolated’ lamina (measured from torsion of 90° tubes). Extracted shear failure strains, for embedded laminae, were more than four fold larger than those measured at ultimate failure for an ‘isolated’ lamina. Soft characteristics were observed in the embedded lamina and these were believed to be due to interaction between early matrix damage initiation (and propagation) and shear. Factors affecting the behaviour of the tubes, such as bulging, scissoring, thermal stresses and stress variation through the thickness are discussed.