现场预制桥梁T梁开裂分析、处理及预防

对后张法现场预制T梁的裂缝进行描述,从混凝土的原材料、配合比、施工和养护,环境条件等方面分析引起T梁开裂的原因,提出了处理办法及预防措施.对指导施工具有积极意义.     

热障涂层的CMAS腐蚀失效及对策研究综述

研制具有长寿命、高性能的热障涂层（TBCs）,是制造我国大功率航空发动机、发展新一代超音速战机的一项十分紧迫的任务。由于外来沉积物CaO-MgO-Al2O3-SiO2（CMAS）渗入涂层而导致TBCs失效的现象越来越受到人们的重视,在过去的一段时间里,很多学者对CMAS渗入后涂层的失效机理进行了大量的研究并尝试了一些缓解CMAS渗入涂层的方法。本文针对当前应用最为广泛的“层状多孔结构”的等离子喷涂涂层及“细长柱晶结构”的电子束辅助物理气相沉积涂层,系统地梳理了近年来国内外学者对TBCs在CMAS渗入条件下的失效机制及涂层缓解CMAS渗入方面的最新研究成果,为制备高性能的TBCs提供帮助。     

Brazing of absorbers of planar solar heating collectors produced from materials of the Cu–CuZn system

The technology of brazing the absorber of planar solar heating collectors, consisting of a ray-receiving panel, produced from copper sheets with a composite selective coating and a tubular part, produced from L63 brass, is examined. The design of the absorber developed by the authors is described. The requirements on brazing technology to preserve the selective multilayer coating during heating of the Sun ray collector panel are determined. The experimental results are used for selecting the brazing alloys, fluxes and temperature–time parameters used in the development of the industrial technology of brazing the Sun ray collector panel of the absorber.     

30.4 nm Si/C多层膜反射镜的制备与测量

采用离子束溅射镀膜装置制备了一种新的材料组合Si/C多层膜 ,用于 30 4nm波段的正入射多层膜反射镜。并用软X射线反射率计测得其反射比最大值为 0 14。有效地抑制了 15 0nm处的二级衍射峰。     

SURFACE ROUGHNESS OF SPUTTERED SILICON. II. MODEL VERIFICATION

Experimental verification of the mathematical surface roughness model for sputtered silicon was performed. The beam shape and its significant level of intensity were determined first by measuring the topography of craters sputtered by focused ion beam (FIB). Then the beam function was generated for various combinations of beam parameters. The material function was developed both by theoretical and experimental analysis. These two functions were then used in the model to calculate the theoretical surface roughness. Microsurface analysis was formed by FIB sputtering of a (100) silicon wafer. The surface roughness at the bottom of the sputtered features was then measured using an atomic force microscope. The theoretical surface roughness was found to be within ±1 and ±5 nm of the measured surface roughness with the measurement uncertainty (standard deviation) of about ±0.36 and ±0.85 nm for R_a and R_t, respectively.     

Breakability analysis of the elastic rock beam based on the winkler model

Based on the Winkler model, a mechanic model was established with formulas derived concerned with the deformations before and after a roof breakage at places in front of and at the back of the working face. In accordance with the theory for rock beam breakage, the beam breaking position in front of the working face is specified. In addition, the formulas were developed for the velocity of the subsidence at observatory point A in front of the working face when the coal wall serves as the coordinate center and the advance distance at time t as the dynamic coordinate. In the application of the above-mentioned achievements to the practice of Xieqiao Mine and the mines of the Eastern Panji Company of Huainan Mining（Group） Co. Ltd., the results concerned with the velocity with which the roof stratum tends to subside before and after breakage as derived from the mechanic model are well compatible to the results based on in-situ observations and measurements.     

镀厚膜工艺技术研究

通过分析现有镀膜工艺设备的电子束加热原理、结构和热量损耗,并针对实际应用过程中镀膜存在的问题,提出了对现有设备的改进措施,开发出一种新的镀厚膜工艺,较好解决了芯片镀厚膜的工艺技术难题和存在的镀厚膜工艺质量问题,大大提高了镀厚膜工艺的工作效率,极大地改善了特高压超大功率电力电子器件的电性能参数,收到了良好的效果.     

耐候钢异型坯连铸保护渣的工业试验

为控制耐候钢粘结漏钢及其裂纹等质量问题,针对耐候钢异型坯连铸的特殊性专门设计了保护渣,主要从提高原有保护渣的碱度R或F-含量等来实现控热,增强保护渣润滑性能,同时进行了工业性试验。通过优化保护渣性能,漏钢发生率由使用前的约7%减少到〈0.1%,保证了8炉以上连浇,基本解决了耐候钢粘结漏钢问题。     

BEPC试验束数据获取系统改进及离线数据分析

运行在BEPC电子直线加速器上的试验束,主要利用在线探测器和离线数据分析选择单粒子事例,满足多种单粒子束流试验.本文介绍了试验束改进后的数据获取系统,以及离线数据分析中的飞行时间谱分析,单粒子判选和粒子击中位置定位等.     

具有边梁的悬臂矩形板的弯曲问题

本文建议一个求解具有边梁悬臂矩形板弯曲问题的解析解法。该法将有边梁和无边梁悬臂矩形板弯曲问题的解融为一体,在有边梁悬臂矩形板的解中令边梁弯曲刚度为零即得到无边梁悬臂矩形板的解。