镁质瓷泥浆流变性能的改进

滑石质瓷是一种高性能瓷的材料，但由于其泥浆的稠化性及泥料塑性差，阻碍了滑石质瓷的大量生产。实验表明：引入长石作助熔剂并加入适量粘土，可以改进泥料塑性及泥浆流变性能，使烧成变形度小，机械强度提高，能较好地满足制品成型的工艺要求。实验中设计了多组配料，分析比较烧后试样的性能测试结果，确定最佳配方及烧结温度。     

Microstructure and thermal behavior of Sn-Zn-Ag solders

The microstructure and thermal behavior of the Sn-Zn-Ag solder were investigated for 8.73–9% Zn and 0–3.0% Ag. The scanning electron microscopy (SEM) analysis shows the Ag-Zn compound when the solder contains 0.1% Ag. X-ray diffraction (XRD) analysis results indicate that Ag₅Zn₈ and AgZn₃ become prominent when the Ag content is 0.3% and above. Meanwhile, the Zn-rich phase is refined, and the Zn orientations gradually diminish upon increase in Ag content. The morphology of the Ag-Zn compound varies from nodular to dendrite structure when the Ag content increases. The growth of the Ag-Zn compounds is accompanied by the diminishing of the eutectic structure of the Sn-9Zn solder. Differential scanning calorimetry (DSC) investigation reveals that the solidus temperature of these solders exists at around 198°C. A single, sharp exothermic peak was found for the solders with Ag content less than 0.5%. Liquidus temperatures were identified with the DSC analysis to vary from 206°C to 215°C when the Ag content ranges from 1.0% to 3.0%     

Results of familiarization of and prospects for a procedure for the burning of wastes in a vortical fluidized bed

Problems that have arisen during tune-up of the production line for the thermal processing of solid household waste by the method of burning in a vortical fluidized bed (principally, a new technology for Russia), and means of their solution are presented. Investigative studies are cited. __________ Translated from élektricheskie Stantsii, No. 6, pp. 20–26, August, 2006.     

新型聚氨酯固-固相变储能材料的组成与热性能的关系

利用差示扫描量热仪、傅里叶红外光谱仪、广角X射线衍射仪研究了一种新型的以聚乙二醇为软段的聚氨酯相变储能材料。结果表明，当软段含量低于90％（质量分数，下同）时，即使温度高于聚乙二醇的熔点，此类材料仍不会熔化成液体，而表现出一种固-固相变行为。该聚氨酯储能材料相变焓较大，相变温度适中，且随着软段含量的减少，材料相变焓和相变温度呈递减趋势。其相变过程实质是聚氨酯软段聚乙二醇由结晶固态转变为无定形固态的过程。     

A study on the interaction between ibuprofen and bilayer lipid membrane

Ibuprofen is a well-known nonsteroidal anti-inflammatory drug, which can interact with lipid membranes. In this paper, the interaction of ibuprofen with bilayer lipid membrane was studied by UV-vis spectroscopy, cyclic voltammetry and AC impedance spectroscopy. UV-vis spectroscopy data indicated directly that ibuprofen could interact with lipid vesicles. In electrochemical experiments, ibuprofen displayed a biphasic behavior on bilayer lipid membrane supported on a glassy carbon electrode. It could stabilize the lipid membrane in low concentration, while it induced defects formation, even removed off bilayer lipid membrane from the surface of the electrode with increasing concentration. The mechanism about the interaction between ibuprofen and supported bilayer lipid membrane was discussed.     

Prenatal development of intrafetal and maternal-fetal synchrony.

Fetal and maternal data were monitored serially at 6 gestational ages from 20 to 38 weeks in 195 Peruvian fetuses. Digitized data included fetal heart rate and motor activity, as well as maternal heart rate and electrodermal conductance. Time series analysis evaluated the development of synchrony in 2 streams of fetal functioning and between mothers and fetuses. Intrafetal synchrony between heart rate and motor activity developed in an orderly fashion, with peak cross-correlation approaching an asymptote at 5 s at 28 weeks. Synchrony was not observed between fetal heart rate and maternal measures. Fetal motor activity exhibited synchrony with both maternal electrodermal and heart rate activity. Implications for revealing fundamental properties of neural development prior to birth are discussed. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Failure analysis of three reconditioned rail car couplers

Three reconditioned rail car couplers, arbitrarily identified as couplers, failed during service due to cracking of the front face. The three couplers were reportedly upgraded by quenching and tempering to enhance strength and toughness. The objective of this investigation was to determine the mode of crack propagation and the root cause of the observed failures. Verl E. (Bud) Kahle, P.E., was a professional failure analyst for more than forty years. After receiving his Bachelor of Science degree in physical metallurgy from Washington State University 1957, Bud was employed by the General Electric Company at a facility in Hanford, Washington. He later was employed by the Aerojet General Corporation and eventually was head of the Southern Pacific Materials Science Laboratory in Sacramento. After retirement from Southern Pacific he owned and operated his own firm, Kahle Metallurgical Consulting Services, for fifteen years. He came to be known as “the man with the answers” to clients in a variety of industries. Bud was a Life Member of ASM International. Many of Bud’s clients remarked on the high quality of his failure analysis case histories and encouraged him to have them published. After Bud passed away in 1999, his wife, Suzanne, approached ASM International to see if the society would be interested in publishing any of his work. Mrs. Kahle was able to supply a large number of reports, which Bud had carefully archived over the years. Journal of Failure Analysis and Prevention Associate Editor Michael Stevenson read through the collected case histories, selected the ones to be included in this issue, and edited them for journal publication. ASM International wishes to thank Mrs. Kahle for providing these case histories for publication.     

First-principle study of ferroelectricity in PbTiO3/SrTiO3 superlattices

We performed the first-principles calculation to investigate the electronic structure and polarization behaviors in PbTiO₃/SrTiO₃ (PST) superlattices. The DOS (density of state) profiles show that there are strong hybridizations of atom Ti–O and Pb–O which play very important roles on ferroelectricity of the PbTiO₃/SrTiO₃ superlattices. Comparing to the corresponding paraelectric phase, we find the electrons of the PT (PbTiO₃) layers occupy lower energy states and electrons of the ST (SrTiO₃) layer occupy higher energy states. It is shown that the polarizations of the superlattices decrease with proportion of SrTiO₃ increasing. The constant polarization of local layer indicates that PST superlattices with small modulation lengthen can be approximately considered as a single ferroelectric material. Furthermore, according to electrostatic model, we find that directions of internal electric fields in PT and ST layers are opposite. In PST superlattices, internal electric field in PT layer leads to the loss of polarization of this layer, but the polarization of ST layer is induced by internal electric field of this layer. Compared to the value of the polarization in bulk PbTiO₃, polarization of PST is smaller.     

Temperamental resistance to control increases the association between sleep problems and externalizing behavior development.

This study examined the moderating effects of temperamental resistance to control on the link between development of sleep problems and development of externalizing behaviors over a 5-year period. Resistance to control was assessed with mothers' retrospective reports of temperament in infancy, provided when children were 5 years of age. Sleep problems were assessed with mother reports on an annual basis from age 5 to age 9. Externalizing behaviors were assessed with teacher reports on an annual basis from age 5 to age 9. A cross-domain latent growth curve model indicated that sleep problem trajectories were positively associated with externalizing behavior trajectories only for children high in resistance to control. In addition, resistance to control was positively associated with initial (age 5) sleep problems and initial (age 5) externalizing behaviors. The authors speculate that the development of sleep problems promotes the development of behavior problems for resistant children, whose self-regulatory abilities are especially tenuous. Implications for prevention and treatment of conduct problems are considered. (PsycINFO Database Record (c) 2010 APA, all rights reserved)