硅粉/酚醛制备低成本碳化硅陶瓷复合材料

以低成本的硅粉和酚醛为原料 ,采用浆料浸渍 热压成型 反应烧结法制备了Cf SiC单向板 ,并对工艺条件进行了探讨。制备得到的单向板的弯曲强度达到 45 6 .8MPa ,断裂韧性达到 7.94MPa·m1 2 。     

内外齿复合冷挤压成型实验研究

通过对轿车转向盘毂件内外齿进行的复合挤压实验研究 ,得到了新式复动式复合挤压模具结构 ,并确定了一种合理的成型工艺方案     

纳米NiO粉体的制备及其表征

采用溶胶转化－凝胶法制备了纳米级NiO粉体。Ni(OH)2粉体的TG－DSC分析表明：在升温速率为10℃/min的条件下，粉体在489K时开始显著分解，626K时分解完毕。X－射线衍射分析表明：分解产物为纯净的NiO2。NiO粉体的化学成分分析表明：其纯度高于国家标准。TEM电镜分析表明：NiO粉体呈单分散的球形或棒状颗粒。对NiO粉体的热敏性能有待进一步研究。     

Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.     

Polygonal extrusion

A sweeping operation called polygonal extrusion is defined to improve the modeling power of CSG-based modeling. It is assumed that a 2D cross-sectional polygon (sweeping polygon) moves in space while its containing plane is kept orthogonal to the tangent direction of the trajectory curve, a planar polygonal chain having no self-intersections. The objective of the paper is to compute the boundary of the swept volume of the sweeping polygon as a set of polygons (or triangles). The most significant challenge to accomplishing this objective is the problem of trimming the swept volume. To solve the trimming problem, 2D-curve offsetting methods are employed. Two algorithms are presented for polygonal extrusion that are based on different offsetting methods, the Voronoi diagram and PWID offset. The proposed algorithms have been implemented and tested with various examples. Published online: 28 January 2003     

钛铁矿流态化氧化机理研究

对低品位钛铁矿进行预氧化、预还原等预处理后可满足硫酸法生产钛白粉工艺所需高品位钛铁矿的要求。本试验采用流态化预氧化方法处理风化程度低、含硫较高的钛铁矿。结果表明 :流态化氧化可大幅度地降低钛铁矿中硫含量 ;钛铁矿流态化氧化的适宜温度为 :80 0～ 90 0℃ ,且在此温度范围内 ,随温度的升高 ,钛铁矿的氧化速度增加 ,在 90 0℃时 ,5 0min钛铁矿基本能完成氧化     

单壁纳米碳管/纳米铝基复合材料的增强效果

用半连续氢电弧法和活性氢等离子蒸发法分别制备出单壁纳米碳管(SWNTs)和纳米A1粉体，然后用提纯后的SWNTs和纳米A1粉体制备出SWNTs含量(质量分数)分别为0、2．5％、5．0％、7．5％和10.0％的单壁纳米碳管／纳米铝基块体复合材料．SWNTs对高强度纳米A1基体具有显著的增强作用，当SWNTs含量小于5．0％时，材料的硬度随着SWNTs含量的提高线性上升．其中5％SWNTs和纳米A1的复合增强效果最好，其硬度可达2.89GPa，大约是粗晶A1(0．15GPa)的20倍．当SWNTs含量超过5．0％时，增强效果开始缓慢的下降．讨论了单壁纳米碳管增强纳米铝基复合材料的强化机制．     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

高压水射流技术粉碎原盐的研究

以原盐为被粉碎研究对象,通过对高压水射流粉碎原盐形貌的观察和成分分析、高压水射流原盐粉碎性能分析,以及高压水射流粉碎原盐各影响因素的正交分析,研究表明高压水射流粉碎技术对原盐具有良好的解理性且粉碎效率高、耗能低。各因素对原盐粉碎效果的影响顺序为:射流压力卤水喷嘴直径、料液混合喷嘴直径、靶面形状。     

汽轮机轴承烧瓦与轴颈的渗巴氏合金现象

简述轴承工作性质，巴氏合金应用与相组成的基本情况。论述汽轮机转子在两个电厂长期运行后，由于轴颈发生的不正常摩擦损伤，在大修改造中由无损检查、机械加工揭示出轴颈存在严重的渗巴氏合金现象，低熔点金属Sn、Sb与Cu向转子材料晶界的深层渗入最终导致了3根大型在投转子的严重开裂与报废。图11表2