Stored energy analysis of Zn—5Al eutectic alloy in superplastic deformation

The stored energy and the energy release during SPD(superplastic deformation)of a Zn-5Al alloy were studied.The alloy after rolling process gains more stored energy,and the as-rolled speciment can obtain maximum elongation and minimum flow stress without hot loding treatment before SPD.Experimental results show that stroed energy release process is along with SPD process and is also an impetus to SPD.The as -rolled Zn-5Al alloy has 48J/mol stored energy which was measured with DSC(differential scanning calorimeter)and conforms well to the calcuated value.The as-rolled Zn-5Al alloy after SPD with an elongation of 2500% releases 112J/mol stored energy,Analysis shows that the strain rate is in direct ratio to the rate of stred energy release.     

脱硫液中硫回收工艺的比较

通过对煤气湿法脱硫液中硫回收工艺的比较，冷回收工艺在煤气脱硫中的应用取得了巨大的经济效益和社会效益。     

高富氧喷煤高炉内焦炭质量劣化初探

实验表明，高炉高富氧喷煤条件下，炉内的温度分布，矿焦比，煤气成分与流量对焦炭的溶损量和热强度影响显著。煤气中ＣＯ或Ｈ２含量增加，会提高焦炭的溶损率和粉化程度；反应温度和矿焦比升高也有相同的结果。     

铸铁表面激光熔覆裂纹的形成原因

选用了三种铸铁基材和四种合金粉末，考察了激光能量密度以及各种基材与合金粉末搭配时对熔覆裂纹的作用。建立了一种定量评判基材与粉末材料相容性的公式，由该公式可计算出湿润角。θ和ｑ是控制裂纹形成与否的两个重要原因。     

升温还原过程中自熔性球团矿的高温特性

在载荷条件下用６种不同化学成分和物理性能的自熔性球团矿，进行了升温还原实验。高温区还原特征分为三类：缓慢还原，熔融还原和还原球团的熔融滴落。对被研究的球团矿精确的测定了还原的开始温度（ＳＳＲ）。一般趋势是ＳＳＲ随低温还原度的增加而增加，较高的ＳＳＲ熔融还原度较低。还原性随着气孔率增加而改善，气孔率随着烧结温度和形成的渣量（ＣａＯ，ＳｉＯ２，Ａｌ２Ｏ３和ＭｇＯ组分的量）的增量加而下降。并且发现与高炉     

喷煤时高炉内炉料的行为

喷煤操作引起高炉内矿焦比升高，某些喷吹的煤粉沉积在炉内成为未燃半焦。因此，高炉操作不稳定，与喷煤操作相适应的炉内煤气流控制是必须的。通过一系列实验说明了矿焦比对软熔带化学反应的影响：（１）由于矿石层厚度增加，软熔带矿石的速 原是受通过软熔煤气流阻力影响的；（２）未燃半焦比焦气化更快，因此，焦炭分解减少。     

W—CeO2合金的烧结与加工缺陷的研究

本文研究了Ｗ－ＣｅＯ２合金在制备过程中工艺参数的选择及其对产品质量的影响，系统地探索了粉末粒度、装粉量、成形压力、垂熔电流、坯条密度及ＣｅＯ２含量之间的相互关系，从而确立了最佳的制粉、压制、垂熔、加工工艺。文中也分析了产品缺陷产生的原因，提出了避免缺陷的办法。     

注塑件熔接缝形成机理和减小其损害的措施

注射模塑零件的熔接缝是注射模塑零件中最常见的质量缺陷之一。文章在对熔接缝形成机理从五个方面具体地进行分析的基础上，针对工厂生产实际提出了避免或减轻熔接缝的相应措施。