高铝高炉渣系的熔化特性

 为了掌握高Al₂O₃条件下(w(Al₂O₃)为15%以上)高炉渣系的熔化特性,利用差式扫描量热仪分析了不同w(MgO)/w(Al₂O₃)、碱度(R)以及w(Al₂O₃)对高铝高炉渣的熔化温度及熔化热的影响。试验结果表明,炉渣熔化开始温度为1 248～1 291 ℃、熔化结束温度为1 432～1 485 ℃、熔化热为137～211 J/g;当w(Al₂O₃)=15%、高w(MgO)/w(Al₂O₃)时,发生了共晶逆反应,导致高炉炉渣熔化开始温度逐渐降低,但由于高炉炉渣的液相线温度基本未变,所以炉渣熔化结束温度基本未发生改变;w(Al₂O₃)为20%时,随着w(MgO)/w(Al₂O₃)的增加,炉渣中易生成熔点较高的镁铝尖晶石,导致高炉炉渣熔化开始温度逐渐增大,与此同时,炉渣液相线温度逐渐降低,导致炉渣熔化结束温度逐渐降低;随着碱度R的增加,高炉炉渣中生成了具有高熔点的化合物、炉渣的液相线温度升高,使得高炉炉渣的熔化开始温度逐渐增加、炉渣熔化结束温度逐渐升高;随着w(Al₂O₃)的增加,发生了共晶逆反应,故炉渣的熔化开始温度逐渐降低,而随着w(Al₂O₃)的增加,炉渣中键能较大的Al—O键增多,需要在更高温度下才能实现炉渣的最终熔化,即熔化结束温度逐渐增加;随着w(MgO)/w(Al₂O₃)、R以及w(Al₂O₃)的增加,炉渣熔化热逐渐增多。分析认为,随着R的增加,炉渣中有高熔点化合物的生成,熔化热增加;随着炉渣中w(Al₂O₃)的增加,炉渣中Al—O键增多,解聚破坏熔渣结构消耗的热量增多;而随着w(MgO)/w(Al₂O₃)增加,高熔点化合物的生成或熔化开始温度降低,造成熔化热增加。     

Characterization of ultrafine La x Sr1−x MnO3 powder prepared by spray pyrolysis

The characterization of La _x Sr_1−x MnO₃ powders produced by spray pyrolysis using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observation, specific surface area (Brunauer-Emett-Teller), and particle size distribution measurements shows that the resultant large particles are loose agglomerates consisting of many small particles. However, the sintered tiny particles can form hard agglomerates, and the particle size increases remarkably. The structures of the powders before and after sintering were identified by x-ray diffraction (XRD). The study of the electrical property of the powder shows that the powder is a metallic conductor. In a reducing atmosphere, the powder can be decomposed. When the powder is cofired with yttria-stabilized zirconia 5% (YSZ) powder at 1200 °C for 5 h, no new phase is produced, and the powder remains a single provskite hexagonal-rhombohedral structure.     

基于图像识别的铜转炉吹炼造渣期渣含Fe预测模型研究

铜转炉吹炼是火法炼铜的关键工序,其终点判断与炉寿、铜产率和直收率紧密相关,目前现有人工经验、仪器测定和物料平衡法等终点判断方法均存在一定的局限性。理论上铜转炉吹炼造渣期终点与渣含Fe是否达标有关,而不同Fe含量渣样呈现不同的图像特征,鉴于此,基于图形识别的特征向量提取原理,分别采用卷积神经网络(CNN)算法与支持向量机(SVM)算法,构建了铜转炉吹炼造渣期渣含Fe预测模型,为图像识别技术在铜转炉吹炼终点判断中的应用奠定数模基础。两种模型的实例分析表明,卷积神经网络的训练集预测准确率98%,测试集预测准确率约50%;支持向量机模型的训练集预测准确率99%,测试集预测准确率62%。     

基于粗轧镰刀弯的精轧跑偏预控模型及应用

带钢热轧跑偏问题是影响带钢生产与板形质量的重要因素。轧制生产过程中,由于粗轧中间坯头部弯曲导致的精轧堆钢事故频发,不仅严重危害生产稳定性,还造成资源的严重浪费和企业的经济损失。为了解决上述问题,针对粗轧非对称板形影响因素,结合实测粗轧中间坯以及工艺过程数据,建立中间坯头部预控模型,并利用加权最小二乘法与模型自学习对模型增益系数进行优化,最终建立了基于粗轧镰刀弯的精轧跑偏预控模型。将模型计算值应用于现场生产后,有效降低了精轧带钢头部跑偏,具有较好的参考价值和指导意义。     

扫描电镜在质量事故分析中的应用

应用扫描电镜断口分析、能谱定性分析、光学显微形貌测试等方法 ,针对公司重要产品因细小裂纹而连续四炉产品全部报废的重大质量事故 ,分析了引起报废裂纹缺陷的性质及产生原因。结果表明 :缺陷主要是大量集聚分布的脆性Al2 O3 夹杂及其裂纹 ,属原材料缺陷 ,是冶炼时氧化还原工艺控制不当 ,或加Al量不均匀所致。据此立即采用了相应调整和改进冶炼工艺措施 ,有效消除了原始缺陷 ,迅速提高了产品质量和效益。     

Preparation and electrochemical performance of nanosized Co3O4 via hydrothermal method

The hydrotalcite-type cobalt compounds were prepared through oxidation of Co（OH）2 gel using NH4OH as precipitating agent and H2O2 as oxidant. These hydrotalcite-type cobalt compounds were transformed into Co3O4 through hydrothermal decomposition with nanostructural deformation. The precursor and product were characterized by Fourier-transform infrared（FT-IR） spectrum, X-ray diffractometry（XRD） and transmission electron microscopy（TEM）. The electrochemical performances of as-prepared nanosized Co3O4 as anode materials in lithium-ion batteries were tested by charge-discharge test in the voltage range of 0-3.0 V. The influence of morphology of Co3O4 particle on the capacity and cycling performance was studied. The results show that the shape and size of the final product can be controlled by altering cobalt sources. The irregular cubic Co3O4 with the average particle size of about 10 nm shows the best electrochemical performance. After 10 charge-discharge cycles, the specific charge capacity retains 555 mA.h/g.     

Synthesis of Ti3SiC2 by spark plasma sintering(SPS)of elemental powders

Ti3SiC2 materials have been fabricated by spark plasma sintering of the elemental powders with the addition of Al.At the heating rate of 80℃/min and under the pressure of 30MPa,the ideal synthesis temperature of Ti3SiC2 is in the range of 1150-1250℃.The addition of Al is in favor of the formation of Ti3SiC2.The synthesized compound has the molecular of Ti3Si0.8Al0.2C2 and lattice parameters of α=0.3069nm,c=1.7670nm.Its grain is plane-shape with a size of about 50μm in the elongated dimension.The prepared material has Vickers hardness of 3.5-5.5GPa(at 1N and 15s) and is as readily machinable as graphite‘s.     

Microstructure and mechanical properties of high strength as—cast Ti—15—3 alloy

The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as-cast Ti-15-3 alloy prepared by induction skull melting method were investigated.Results show that the microstructure of as-cast Ti-15-3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate.After solution treatment and different ageing treatment,alpha phase precipitates in grains interior as well as in grain boundaries.Due to the modification of the precipitate phase,the tensile stength and elongation of the alloy are improved simultaneously.A good combination of the values of 1.406GPa of σb and 4.5% of δ was obtained,which will be satisfied the use of this kind of alloy in critical areas.     

反求工程的产品几何建模技术研究

分析了目前在反求工程产品几何建模中广泛应用的曲面模型的局限性，指出反求工程为实现创新功能必须采用产品特征模型，提出了基于实体造型的特征建模方法。这种方法可以避免曲面模型的缺陷，拓宽反求工程的应用范围，是实现三维重构的新方法。探讨了有关的理论和关键技术。     

离心成型法制备Al2O3/Ni功能梯度材料及性能表征

用离心成型法制备了Al2O3/Ni功能梯度材料,并研究了料浆调制工艺、制备参数和梯度材料的力学性能.结果表明,良好的料浆的最佳流动性配比为粘结剂(聚乙二醇)含量为2 mass%、固相含量为63 vol.%、球磨时间为36 h.经离心成型-真空烧结(1400℃,2 h)可获得致密、组元宏观连续过渡的Al2O3/Ni梯度材料.该复合材料孔隙率低,力学性能好,抗弯强度可达321 MPa.