34CrNiMo钢齿轮轴开裂原因分析

对34CrNiMo钢齿轮轴的化学成分、金相组织及断口分析表明，其淬火开裂的主要原因是由于锻造温度过高，导致过热缺陷所致。     

Catalytic oxidation of hydrogen sulphide on activated carbons

Activated carbon is a suitable adsorbent for removal of hydrogen sulphide from natural, synthesis or other product gases. The process depends predominantly on physical adsorption, though catalytic oxidation is also involved. During catalytic oxidation the H₂S is converted in the presence of oxygen to elemental sulphur, which is adsorbed onto the internal surface of the activated carbon, thus leading to a sulphur load of up to 120% by weight. The oxidation rate depends on the partial pressure of both reactants, H₂S and O₂ and is largely controlled by the characteristics of the activated carbon. The activity of the catalyst can be improved by impregnating the activated carbon with promoters such as iron and iodine. The regeneration of spent carbon is currently carried out using hot gas desorption methods at temperatures around 450 °C.     

Fluor SOx净化工艺--为俄罗斯绿色环境开发的将SO2转化为元素硫的经济技术

Fluor公司开发的Fluor SO_2净化工艺具有广泛多样的工艺布局,可以通过经济的方式定制脱除烟气中的有害组成。该工艺几乎能去除全部SO_2并减少CO排放。Fluor SO_x净化工艺的主要步骤已在多套工业装置中得到成功的证实。除技术可行、经济合理之外,Fluor SO_x净化工艺不会产生任何有害副产物,也不会遇到与SO_3 有关的腐蚀问题。此外,该工艺生产高纯度可市售的元素硫。论述了Fluor SO_x净化工艺的特征、技术和成本优势、设计和操作的简易性以及实施的便利性。     

SOLUBILITY OF CO2 AND H2S IN A HINDERED AMINE SOLUTION

The solubility of H₂S and CO₂ in aqueous solutions of the sterically hindered amine, 2-amino-2-methyl-1-propanol (AMP), was determined at 40 and 100°C. Partial pressures of C)₂ ranged from approximately 2 to 6000 kPa and of H₂S from 2 to 2200 kPa. The solubility results were compared with previously reported acid gas solubilities in aqueous monoethanolamine (MEA) solutions.     

Polysulphone and poly(phenylene sulphide) blends: 1. Thermal characterization and phase morphology

The phase behaviour and morphology of injection moulded specimens of polysulphone (PSF) and poly(phenylene sulphide) (PPS) blends were studied by differential scanning calorimetry (d.s.c.), dynamical mechanical thermal analysis (d.m.t.a.) and transmission electron microscopy (TEM). The blends are phase separated regardless of the blend composition as revealed by d.s.c., d.m.t.a. and TEM. Upon annealing at 160°C for 2 h, d.m.t.a. results indicate that the PPS phase remains in the amorphous state at compositions <10%. At compositions between 20 and 35%, the PPS appears to be dispersed in a mixed mode of amorphous and crystalline domains. Above 35% the PPS phase appears to become fully crystallized upon annealing of the blends. At 10% PPS, TEM results showed 35–200 nm size dispersion both in the as-moulded and in the annealed specimens. At 20% the PPS phase varied widely in size, from 35 nm to tens of micrometres but remained as an included phase. TEM also revealed a compound morphology of the included phase at a composition of 50 wt% of each component.     

镉质量浓度和鱼尺寸对罗非鱼积累和转移镉的影响

为研究尺寸和镉(Cd~(2+))质量浓度对罗非鱼积累和转移水环境中Cd~(2+)的影响,用室内培养的方法,选取4种尺寸的罗非鱼,设置不同质量浓度Cd~(2+)的暴露试验,分别测定其半致死率、Cd~(2+)积累量和对Cd~(2+)的转移系数以及罗非鱼的相对增长率.结果表明:不同尺寸的罗非鱼对Cd~(2+)的响应不同,其中,幼龄鱼的LC50浓度最低,体长为31.5±3.4 cm的罗非鱼LC50最高;低质量浓度Cd~(2+)(0.5 mg/kg)处理下,罗非鱼尺寸不同,相同鱼组织对Cd~(2+)的吸收积累量差异显著(P0.05),而高质量浓度Cd~(2+)处理时,不同尺寸罗非鱼的同一组织对Cd~(2+)的积累量无显著性差异;除体长27.4±2.9 cm罗非鱼外,相同尺寸的罗非鱼Cd~(2+)转移系数都是低质量浓度显著大于高质量浓度(P0.05);高质量浓度Cd~(2+)处理对各种尺寸罗非鱼质量增加的抑制率显著高于低质量浓度Cd~(2+)处理的抑制率.此外,不同Cd~(2+)质量浓度对相同尺寸的罗非鱼也产生不同的影响.因此,罗非鱼的尺寸和Cd~(2+)质量浓度都对罗非鱼积累和转移Cd~(2+)产生影响.     

Development of compositionally modulated multilayer Zn-Ni deposits as replacement for cadmium

Compositionally modulated multilayer (CMM) Zn-Ni deposits were electrodeposited from single acidic bath (pH = 4.7) by using a potentiostatic sequence. The Zn and Ni composition in the alloy was tailored as a function of distance from the steel substrate. X-ray diffraction studies of the deposit showed the presence of γ-phase with a composition of Ni₅Zn₂₁. The corrosion properties of modulated multilayer coatings were studied in 5% NaCl solution using electrochemical corrosion techniques. The polarization resistance of the deposits varied as a function of Ni content between 1700 and 3440 Ω. CMM Zn-Ni with 20 wt% Ni exposed in ASTM B117 salt spray test did not show any red rust formation after 400 h.     

镍硫化物阳极溶解的电化学研究

研究了合成镍硫化物的阳极过程。Ni_3S_2,Ni_7S_6和NiS的活性溶解伴随着生成表面产物层,其反应机理与电极电位有关。根据三种不同类型产物层生成规律的电化学研究,Ni溶出表观电子数的测定,以及产物层相组成分析和相的元素分析,认为存在三组平行反应:直接生成HSO_4~-或SO_(4-)~2的反应,生成中间硫化物的反应及生成元素硫的反应,每组反应具有不同的优势发展电位区。NiS_2阳极溶解时,基本上为生成HSO_(4-)或SO_(4-)~2的反应。     

THERMODYNAMIC AND STRUCTURAL CHEMISTRY DISCUSSIONS FOR OXIDATIVE LEACHING OF Cu－Ni SULPHIDE ORE UNDER ATMOSPHERIC PRESSURE

ＴＨＥＲＭＯＤＹＮＡＭＩＣＡＮＤＳＴＲＵＣＴＵＲＡＬＣＨＥＭＩＳＴＲＹＤＩＳＣＵＳＳＩＯＮＳＦＯＲＯＸＩＤＡＴＩＶＥＬＥＡＣＨＩＮＧＯＦＣｕ－ＮｉＳＵＬＰＨＩＤＥＯＲＥＵＮＤＥＲＡＴＭＯＳＰＨＥＲＩＣＰＲＥＳＳＵＲＥ￥Ｗｕ，Ｗｅｎｊｉａｎ（Ｄｅｐａｒ...     

易切削钢硫化物特性分布数理统计分析

用定量金相对易切削钢硫化物特性——数量、面积、宽度、长度和长宽比进行数值分析，用数理统计频数分析对硫化物分布特性进行了表征，用聚类分析对易切削钢硫化物特性分布进行了分类。