硬质合金冷挤压凹模的热处理强化

本文叙述了ＷＣ－Ｃｏ硬质合金特别是ＹＧ２５牌号硬质合金的渗硼淬火热处理强化工艺和不同钴含量的合金的强化处理效果以及强化处理的合金应用效果，并对其强化机理进行了讨论。     

关于炭素厂阴极焙烧车间设计的探讨

根据近年来对国内炭素厂阴极焙烧车间设计中所作的优化和改进,提出了几个以增产、节能、节约投资和便于操作维修为目的的有效措施。     

Controlling the Cold Roll Forming Design Process

The cold roll forming process requires successive forming profiles to be determined and an appropriate number of profiled roll sets to be designed for the product to be rolled. This paper examines the design process and how one company has put in place a design-production control system that allows designs to be ranked in terms of quality and efficiency. In addition, consideration is given to the proportion of time given to each design task and how non-creative design activities can be automated.     

钛合金冷坩埚电磁约束铸造工艺研究

针对液态下化学性质相对活泼的钛合金,采用冷坩埚技术对电磁约束铸造工艺过程进行了试验研究,考察了工艺条件对成形坯件表面质量和内部组织的影响.结果表明:试样抽拉速度变化对表面质量和宏观组织的影响明显,加热功率虽然对组织变化影响不大,但对表面质量影响较为显著.通过优化工艺,可以获得既有较光滑铸造表面又具有一次定向凝固组织的钛合金铸件.讨论了铸造过程裂纹和组织缺陷的形成机理,获得到了表面光滑无裂纹,宏观组织为柱状晶的钛合金大尺寸圆坯.     

LiFePO4基正极材料容量的温度敏感特性及交流阻抗谱研究

采用原位碳包覆法制备了锂离子二次电池用LiFePO4／C复合正极材料。考察了环境温度对LiFePO4/C电池容量的影响，得到容量与绝对温度之间符合Arrhenius关系。运用交流阻抗谱分析了温度与电池电化学特性的关系，并对电极基于电荷和质量传递控制过程给出了一种新的模拟等效电路，通过Zview拟合软件得到了各个模拟元件的数值及变化趋势，从而定量地解释LiFePO4／C复合电极容量与温度的关系。     

铝电解槽TiB2涂层阴极技术

将含有ＴｉＢ２、碳纤维和热固性粘结剂的涂料，涂敷到铝电解槽的阴极基体上，制备出可润湿的阴极表面。经固化和碳化后，涂层和碳质基体材料的粘结力强，热膨胀匹配性好。每台硼化钛涂层阴极试验槽能节省ＮａＦ２５０～３００ｋｇ，试验槽的电流效率高出对比槽１．４４％，能耗降低１７５～２１１ｋＷ·ｈ／ｔＡ     

铝电解用TiB_2阴极涂层固化、炭化的升温制度

采用DTG ,DDTA等热分析手段 ,研究了高温固化、炭化过程中 ,铝电解用TiB2 阴极涂层糊料的质量和能量的变化速率 ,制定了涂层的变速固化、炭化升温制度 ;在此基础上 ,研究了升温制度对TiB2 阴极涂层性能的影响。结果表明 :变速升温制度优于匀速升温制度 ,采用变速固化、炭化升温制度所制备的涂层形变小、无裂纹 ,其抗拉强度达 3.13MPa,电阻率为 2 3.2 μΩ·m ;而采用升温速度为 10 .3℃ /h的匀速固化、炭化升温制度制备的涂层形变大、裂纹多 ,抗拉强度小 (2 .6 9MPa) ,电阻率大 (2 8.6 μΩ·m)。     

Ambient temperature cured TiB_2 cathode coating for aluminum electrolysis

1　INTRODUCTIONAluminumindustryhasbeendevelopingrapidlyinChinainrecentyears ,soderbergcellshavebeenre placedwithmodernprebakecellsinmanyaluminumsmelters,theaveragecelllifehowever ,forprebakecellsinourcountrywasonlyabout130 0d ,muchlowerthantheaveragecelllife ,i.e .above 2 5 0 0d ,forthecellsindevelopedcountries .TiB2 cathodecoating (TCC)couldbeoneofthesolutionstoreducegreatlytheopportunitytotheearlyfailureofcellsandextendthecelllifeofprebakecell[14 ] .Theconceptoftitaniumdiboride (TiB2 …     

Viscosity of compressed cold lake bitumen

Viscosity data over a temperature range of 37-115°C and a pressure range of 0-10 MPa gauge are presented for a Cold Lake bitumen sample. These data show that the compression of Cold Lake bitumen results in a significant increase in its viscosity. Results are compared with those from a similar study on an Athabasca bitumen sample. Also presented are two correlations for the effects of pressure and temperature on the viscosity of Cold Lake bitumen.     

In situ synchrotron X-ray studies on copper-nickel 5 V Mn oxide spinel cathodes for Li-ion batteries

Partial substitution of Mn in lithium manganese oxide spinel materials by Cu and Ni greatly affects the electrochemistry and the cycle life characteristics of the cathode. Substitution with either metal or a combination of both metals in the spinel lattice structure reduces the 3.9-4.2 V potential plateaus associated with the conversion of Mn³⁺ to Mn⁴⁺. Higher potential plateau associated with oxidation of the substituted transition elements is also observed. These substituents also significantly alter the onset of Jahn-Teller distortions in the 3 V potential plateau. Synchrotron based in situ X-ray absorption (XAS) was used to determine the exact nature of the oxidation state changes in order to explain the overall observed capacities at different potential plateaus. The studies on LiCu_0.5Mn_1.5O₄ show single phase behavior in the 4-5 V potential region with a good cycle life. Lower cycle life characteristic observed in cycling LiNi_0.5Mn_1.5O₄ and LiNi_0.25Cu_0.25Mn_1.5O₄ versus Li metal are ascribed to coexistence of several phases in this potential region. However, LiCu_0.5Mn_1.5O₄ shows onset of Jahn-Teller distortions in the 3 V potential plateau, in contrast to LiNi_0.5Mn_1.5O₄ and LiNi_0.25Cu_0.25Mn_1.5O₄ cathode materials.