Influence of post‐treatments on the properties of porous poly(vinyl alcohol) membranes

Porous poly(vinyl alcohol) (PVA) membranes were prepared by a phase‐inversion method. The influence of chemical crosslinking and heat treatments on the swelling degree, resistance to compaction, mechanical strength, and morphology of porous PVA membranes was extensively studied. The crosslinking degree and crystallinity of the membranes, calculated from IR spectra, increased with the treatment time. The porosity, calculated on the basis of swelling experiments, showed a decreasing trend for heat‐treated membranes but remained almost at a constant value for crosslinked membranes. Such a change was further proved with scanning electron microscopy pictures. The behavior was explained by the rearrangement of PVA chains during the heat‐treatment process, which led to morphological changes in the membranes. The mechanical properties of the porous membranes in dry and wet states were measured, and a great difference was observed between crosslinked and heat‐treated membranes in the dry and wet states. The crosslinked membranes showed good mechanical properties in the dry state but became fragile in the wet state. On the contrary, the heat‐treated membranes were more flexible in the wet state than in the dry state. This change was explained by the turnaround of inner stress in the systems during the swelling process. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis and applications of heterobifunctional poly(ethylene oxide) oligomers

Poly(ethylene oxide) (PEO) oligomers are employed extensively in pharmaceutical and biomedical arenas mainly due to their excellent physical and biological properties, including solubility in water and organic solvents, lack of toxicity, and absence of immunogenicity. PEO can be chemically modified and reacted with, or adsorbed onto, other molecules and surfaces. Sophisticated applications for PEO have increased the demand for PEO oligomers with tailored functionalities, and heterobifunctional PEOs are often needed. This review discusses the synthesis and applications of heterobifunctional PEO oligomers possessing amine, carboxylate, thiol, and maleimide functional groups.     

Shear-induced crystallization of poly(phenylene sulfide)

The crystalline morphology of poly(phenylene sulfide) (PPS) isothermally crystallized from the melt under shear has been observed by polarized optical microscope (POM) equipped with a CSS450 hot-stage. The shish–kebab-like fibrillar crystal structure is formed at a higher shear rate or for a longer shear time, which is ascribed to the tight aggregation of numerous oriented nuclei in the direction of shear. The crystallization induction time of PPS decreases with the shear time, indicating that the shear accelerates the formation of stable crystal nuclei. Under shear, the increase of spherulite growth rate results from highly oriented chains. The melting behavior of shear-induced crystallized PPS performed by differential scanning calorimetry (DSC) shows multiple melting peaks. The lower melting peak corresponds to melting of imperfect crystal, and the degree of crystal perfection decreases as the shear rate increases. The higher melting peak is related to the orientation of molecular chains. These oriented molecular chains form the orientation nuclei which have higher thermal stability than the kebab-like lamellae that are developed later. A new model based on the above observation has been proposed to explain the mechanism of shish–kebab-like fibrillar crystal formation under shear flow.     

Nonisothermal melt-crystallization kinetics of isotactic polypropylene synthesized with a metallocene catalyst and compounded with different quantities of an α nucleator

The nonisothermal crystallization kinetics of a metallocene-made isotactic polypropylene (m-iPP) and its compounds with 0.1 wt % and 0.3 wt % of a sorbitol derivative [1,3:2,4-bis(3,4-dimethylbenzylidene)sorbitol (DMDBS); an α nucleator] were investigated by differential scanning calorimetry at different cooling rates from the melt. The nucleation efficiency was proved by a significant increase in the crystallization temperatures (accompanied by a slight augmentation of the degree of crystallinity and a decrease in the crystal sizes). This increase in the crystallization temperatures led to higher amounts of fractional content in the γ polymorph, even though DMDBS was supposed to be a nucleator for the α form. The Avrami and Ozawa methods effectively described only the early stage of crystallization, whereas a combined Avrami–Ozawa method was valid for the whole crystallization process. The values of the exponent for this method decreased for nucleated samples in the later stage of crystallization, especially in the case of m-iPP with 0.3 wt % DMDBS added (m-iPP03). The activation energy of the process and the surface free energy were also estimated. The production of considerable proportions of the γ polymorph in m-iPP03 corresponded to higher values of the activation energy and lower values of the surface free energy. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Accelerated wear testing with a microfabricated surface to evaluate the lubrication ability of biomolecules on polyethylene

Wear of ultrahigh‐molecular‐weight polyethylene (UHMWPE) and wear‐particle‐induced osteolysis and bone resorption are the major factors causing the failure of total joint replacements. It is feasible to improve the lubrication and reduce the wear of artificial joints. We need further understanding of the lubrication mechanism of the synovial fluid. The objective of this study is to evaluate the lubricating ability of three major components in the synovial fluid: albumin, globulin, and phospholipids. An accelerated wear testing procedure in which UHMWPE is rubbed against a microfabricated surface with controlled asperities has been developed to evaluate the lubrication behavior. An analysis of the wear particle dimensions and wear amount of the tests has provided insights for comparing their lubrication performance. It is concluded that the presence of biomolecules at the articulating interface may reduce friction. A higher concentration of a biological lubricant leads to a decrease in the wear particle width. In addition, in combination with the wear results and mechanical analysis, the roles of individual biomolecules contributing to friction and wear at the articulating interface are discussed. These results can help us to identify the role of the biomolecules in the boundary lubrication of artificial joints, and further development of lubricating additives for artificial joints may be feasible. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Changes in the thermomechanical behavior of epoxy glasses under the state of strain aging

Changes in thermomechanical behavior with structural relaxation taking place in epoxy glasses were studied. Differential scanning calorimetry measurements and thermostimulated strain recovery tests were performed for specimens deformed and then aged under fixed strain. In the course of heating, the specimens started to absorb thermal energy, whereas plastic strain was still stable. At higher temperatures, plastic strain started recovery, which was accompanied by exothermic behavior of the specimen. With an increase in the aging duration, the endothermic peak signified and moved to a higher temperature. These results indicated that the longer the aging duration was, the harder the plastic strain and strain energy were frozen in the glassy structure. This freeze‐strain phenomenon was observed for crosslinked epoxy glass, as well as polymeric glasses with linear molecular structures, aged under strain. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Antimicrobial finishing of regular and modified polyethylene terephthalate fabrics

An effective two-stage method has been developed for imparting antimicrobial properties to regular polyethylene terephthalate (R-PET), polyethylene glycol modified polyethylene terephthalate (PEG-M-PET), R-PET/Cotton blend (R-PET/C) and PEG-M-PET/Cotton blend (PEG-M-PET/C) fabrics. The method consists of partial hydrolysis of the fabrics to create carboxylic groups in PET macromolecules followed by subsequent reaction with dimethylalkylbenzyl ammonium chloride (DMABAC) under alkaline conditions. The reaction conditions such as pH, reaction temperature and time, carboxylic content, and DMABAC concentration were studied. Characterization of the finished fabrics was carried out through scanning electron microscopy (SEM) and Fourier transform infrared spectra (FTIR). All the modified PET fabrics showed excellent antibacterial activity towards Gram-positive (Bacillus mycoides), Gram-negative (Escherichia coli), and nonfilamentous fungus (Candida albicans). The achieved antimicrobial functions on the PET fabrics are durable in repeated laundering processes. Even after laundering 10 times the fabrics could still provide more than 85% of its antimicrobial activity against B. mycoides, E. coli, and C. albicans. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Structure and processability of iodinated poly(vinyl alcohol). IV. Drawability of the films iodinated at solution before casting

The drawability of iodinated at solution before casting (IBC) polyvinyl alcohol films prepared by casting aqueous solutions of 10 wt % PVA containing 15.2, 39.8, 83.2, 117.0, and 140.1% was examined with a tensile tester at 20–60°C. The tensile behavior of IBC films showed that the yield and breaking loads were much lower, and the breaking elongation was even higher than those of the unoriented iodinated after casting (IAC) films as well as the untreated PVA films. The maximum draw ratios of the films with the weight gain of 15.2, 39.8, 83.2, 117, and 140.1% were 4.5, 5.5, 8.5, 8.0, and 7.5, respectively, which were achieved at 20°C in all. The crystallinity of all films increased by the maximum draw, regardless of crystallinity before drawing. The crystalline structure was recovered to the original PVA crystalline lattice by deiodination. Amorphous orientation and initial moduli increased with the maximum draw ratio, while the orientation of crystals was constant. The orientation and moduli increased up to the weight gain of 83.2%, whose highest draw ratio and initial modulus were 8.5 and of 7.1 GPa, respectively, and then decreased. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Semiflexible random thermotropic copolymers from 8‐(3‐hydroxy phenyl) octanoic acid and 3‐chloro‐4‐hydroxy benzoic acid/3,5‐dibromo‐4‐hydroxy benzoic acid

Two series of semiflexible random thermotropic copolymers containing 8‐(3‐hydroxy phenyl) octanoic acid (HPOA) with either 3‐chloro‐4‐hydroxy benzoic acid or 3,5‐dibromo‐4‐hydroxy benzoic acid were prepared by melt polycondensation techniques. The copolyesters were characterized with Fourier transform infrared spectroscopy, dilute solution viscometry, hot‐stage polarized light microscopy, differential scanning calorimetry, thermogravimetric analysis, and wide‐angle X‐ray diffraction. Studies revealed that the amount of HPOA as a disruptor incorporated into the backbone of substituted 4‐hydroxy benzoic acids had a detrimental effect on the liquid‐crystalline behavior. Mesophase‐transition temperatures were observed between 210 and 250°C, and the optical textures were of typical nematic phases. The degree of crystallinity decreased with an increase in the HPOA content. The thermal stability of the copolymers was in the range of 310–370°C. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Effects and properties of poly(arylene ether benzonitrile)s of various molecular weights blended with sulfonated poly(ether ether ketone)

Poly(arylene ether benzonitrile) (PAEBN) was synthesized with 2,6‐dichlorobenzonitrile and biphenol. PAEBNs with various molecular weights (MWs), 1,640,000 and 185,000 g/mol, were synthesized by control of the stoichiometry of the monomers and were blended with sulfonated poly(ether ether ketone) (SPEEK). The effects of MW on the water uptake, swelling, methanol permeability, and proton conductivity of the SPEEK/PAEBN blend membranes were investigated. The molecular mobility of the SPEEK/PAEBN blends was also examined in this study. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008