Flexible and light weight copper indium diselenide solar cells on polyimide substrates

Thin film flexible CuInSe₂ (CIS) solar cells have been fabricated for the first time on light-weight polymeric substrates. Evaporated Cu---In alloy precursors were selenized in H₂Se atmosphere at around 400°C to grow the CIS absorber layers. Low temperature techniques which are compatible with the polymeric substrates were used to deposit the window layers of CdS and ZnO. The demonstrated active area conversion efficiency of 9.3% makes this light-weight device very attractive for many terrestrial and space power generation applications where high specific power and mechanical flexibility are needed.     

1422轧机滑块式万向接轴的故障及处理

以热轧板厂粗轧主传动滑块式万向接轴为例，分析了该接轴及接轴平衡机构的常见故障及其排除方法，提出了日常维护措施。     

铜萃取剂BK992和LIX984的性能研究

研究羟肟类铜萃取剂的结构与性能的关系。试验研究了铜萃取剂BK992和LIX984的对比萃取及混合萃取性能指标 ,试验表明BK992与LIX984的使用性能相当 ,两种铜萃取剂相互混合不影响使用性能指标。     

Copper bioavailability from breakfasts containing tea. Influence of the addition of milk

The influence of drinking tea on copper bioavailability is unclear, particularly when tea is consumed with food. A breakfast meal containing white bread, margarine, strawberry jam, cheese and tea, with or without milk, was digested in; vitro and the dialysis of copper investigated. Reference breakfasts were prepared with water and water with milk. Copper dialysability (percentage of copper dialysed) was markedly increased by tea. The influence of adding milk to tea was not significant. A second study was carried out in rats using the breakfasts containing tea and water. They were spiked with ⁶⁴Cu and given orally to the animals in a single dose. Whole-body ⁶⁴Cu retention was measured over a 4-day period after administration. In order to determine the true absorption of ⁶⁴Cu a control group of rats received the dose intraperitioneally. The results in vivo indicate a tendency to higher absorption and retention of ⁶⁴Cu with tea. Liver ⁶⁴Cu retention was significantly elevated by tea. Therefore, the presence of tea in a breakfast meal favours the formation of soluble low-molecular-weight ligands which can be absorbed and retained by rats. The concomitant increase in liver copper retetition may be associated with higher bioavailability and/or lower copper mobilisation.     

含微量元素铜焊锡丝的研制

在６０／４０的锡铅焊料中加入０．２％左右的铜，凝固后具有均匀细小的共晶组织，其熔点为１８３℃，焊点强度和扩展率均高于未加铜的６０／４０锡铅焊料，并且含铜的锡铅焊料在焊接时，对铜烙铁头和微细铜线了小的熔蚀性。     

Promising alloys for intermediate-temperature solid oxide fuel cell interconnect application

The formation of a low Cr-volatility and electrically conductive oxide outer layer atop an inner chromia layer via thermal oxidation is highly desirable for preventing chromium evaporation from solid oxide fuel cell (SOFC) metallic interconnects at the SOFC operation temperatures. In this paper, a number of ferritic Fe–22Cr alloys with different levels of Mn and Ti as well as a Ni-based alloy Haynes 242 were cyclically oxidized in air at 800 °C for twenty 100-h cycles. No oxide scale spallation was observed during thermal cycling for any of these alloys. A mixed Mn₂O₃/TiO₂ surface layer and/or a (Mn, Cr)₃O₄ spinel outer layer atop a Cr₂O₃ inner layer was formed for the Fe–22Cr series alloys, while an NiO outer layer with a Cr₂O₃ inner layer was developed for Haynes 242 after cyclic oxidation. For the Fe–22Cr series alloys, the effects of Mn and Ti contents as well as alloy purity on the oxidation resistance and scale area specific resistance were evaluated. The performance of the ferritic alloys was compared with that of Haynes 242. The mismatch in thermal expansion coefficient between the different layers in the oxide scale was identified as a potential concern for these otherwise promising alloys.     

等离子喷涂燃料电池连接板LSM薄膜的性能研究

采用等离子喷涂法在SUS 430连接板基体上制备了LSM(La0.8 Sr0.2 MnO3)薄膜。用X射线衍射仪、扫描电镜和电子探针分别研究了喷涂前后LSM的相组成、薄膜的表面形貌和元素分布。用图像分析法计算了薄膜的孔隙率。二支点法测量了有与无LSM薄膜的SUS 430基体在130～800℃时的电导率。结果发现,薄膜与基体结合良好,薄膜孔隙细小,均匀分布,且非连通;LSM的相组成在喷涂前后保持一致;当温度<330℃时,有LSM保护膜的连接板的电导率小于无LSM薄膜的连接板的电导率;温度>330℃,结果相反。有LSM保护膜的连接板在空气中,130～800℃下,最大电导率为0.60Ω-1·cm-1。     

不甩线圈的多星形移相变极

对于某些槽数和极数比的多星形移相变极电机,提出与前人不同的是在两种极数下均不甩去线圈的绕组方案,使绕组利用率高,且线圈及其联接都较简单.这种绕组方案在一种极数下并联支路略有不平衡,其所引起的电机定子铜耗的增加是极其有限的,不致影响电机的正常运行.     

ULSI中的铜互连线RC延迟

随着ULSI向深亚微米特征尺寸发展，互连引线成为ULSI向更高性能发展的主要限制因素。由互连引线引起的串扰噪音及RC延迟限制了ULSI的频率性能的提高，同时考虑到电迁移和功率损耗，人们开始寻找新的互连材料；低电阻率的铜互连材料和低介电常数介质的结合可以有效地发送互连线的性能，主要讨论了互连延迟的重要性以及发送和计算延迟的方法。     

Optimization of anodic oxidation and Cu–Cr oxide catalyst preparation on structured aluminum plates processed by electro discharge machining

This paper describes the optimization of three processes applied in fabrication of a microstructured reactor for complete oxidation of volatile organic compounds. The first process involves the optimization of the electro discharge machining (EDM) method to produce a set of microchannels with a high length to diameter ratio of 100, with a standard deviation from the average diameter below 0.2%, and with a surface roughness not higher than 2.0 μm. To satisfy these criteria, fabrication of microchannels must be carried out with two machining passes in the Al51st alloy. Then, the effect of several parameters on the anodization current efficiency with respect to oxide formation was studied. The best process conditions to get a 30 μm porous alumina layer in a 0.4 M oxalic acid electrolyte, were found to be a temperature of 1 °C, an anodic current density of 5 mA/cm², and 23 h oxidation time. At last, the resulting coatings were impregnated with an aqueous solution of copper dichromate followed by drying and calcination at 450 °C to produce active catalysts. The effect of a copper dichromate concentration, number of impregnation cycles (1 or 2), and different after-treatments on catalytic activity and stability in complete oxidation of n-butane were studied. The catalytic activity of the obtained coatings is superior to that of alumina supported pelletized catalysts even at much lower loadings of active metals.