The measurement of the diffusion coefficient and the sorption isotherm of water in paint films

An experimental technique together with a numerical model is proposed with which the diffusion coefficient and the sorption isotherm of water in paint can be measured. Inside a closed vessel, paint films are on stainless-steel plates. Water is present as water vapour in the air and in the paint. After blowing dry or wet air through the vessel for some time, the situation moves to a new equilibrium. The relative humidity of the air inside the vessel is measured as a function of time. From fitting the theoretical/numerical model against the experimental values, follow the diffusion coefficient and the sorption isotherm of water in the paint. The results show large scattering. When the independently measured sorption isotherm is used as an input parameter in the model, the fitting procedure gives much smaller scattering for the diffusion coefficient.     

Scale Up from Small Oven-Drying Tests of Mineral Concentrate to Pilot-Scale Drying with a Heated Pad

While Fickian diffusion models are commonly used in other applications, there are few reports of them being applied to the batch drying of a mineral concentrate. Diffusion coefficients estimated from small-scale oven-drying tests were used to predict the drying behavior of a concentrate sample 1 m × 1 m in area and 50 cm deep, with a heated bottom pad. These pilot-scale tests included both daily turning of the sample and turning every three days. The excellent quantitative agreement between the predicted and observed pilot-scale behavior gives a high level of confidence in the model predictions and suggests that a Fickian diffusion model is adequate to predict the behavior of mineral concentrates at the low moisture contents used here.     

Oxidative regeneration of sulfided sorbent by H2S without emission of SO2

Much SO₂, another perilous air pollutant, was emitted during the oxidative regeneration of sulfided sorbent by H₂S. In order to prevent emission of SO₂, we carried out oxidative regeneration with the physical mixture of CaO and sulfided sorbent and investigated the effect of regeneration temperature and oxygen concentration on the reactivity of CaO with S0₂. The effluent gases were analyzed by G.C. and the properties of sorbent were characterized by XRD. SEM, TG/DTA and EPMA. Deterioration of reactivity of CaO with S0₂ resulted in increment of emission of SO₁₂ due to the structural changes of CaO above 750°C and that at 850°C was more severe. Furthermore EPMA and XRD analysis revealed that product layer diffusion through the solid product, CaSO₄, was the rate limiting step for CaO sulfidation. The reaction of CaO w:.th SO₂ was first order approximately and that was accelerated by high O₂ concentration.     

野外大气扩散试验中四面体气球示踪实验的初步评价

1985年11月在瑞士北部进行了一次以探讨“冷池”条件下的扩散和湍流特征为目的的国际野外大气试验,本文介绍其中的四面体气球示踪实验的结果。一共进行了三次由雷达跟踪的四面体示踪实验,释放了10个四面体球。按多轨迹法和单轨迹法分别估算并比较了其中两次示踪实验得到的水平扩散参数σ_y,探讨了风摆效应的贡献。采用“体源模式”并结合单轨迹法估算了微弱风场不定风向条件下的扩散参数,分析了静风,弱风条件下的水平风向标准差和湍流强度。     

Nucleation Mechanism for Bainite

Based on the experimental results that solute-depleted zone was observed in Cu-28Zn-4AI (mass fraction) at 523 K, AG is calculated as a positive according to the thermodynamic criteria for the spinodal decomposition of a ternary systems. So, the solute-depleted zone cannot be formed by spinodal decomposition. Dislocation density required by the formation of solute-depleted zone is estimated greater than 7.89×109 cm-2, according to the segregation of solute atoms around dislocations, which is not consistent with the practical situation for the alloy at 523 K. Associated with the internal friction experimental fact that internal friction peaks appear within the incubation for bainitic transformation in Cu-Zn-AI alloy, the equilibrium temperature, TO, is evaluated as 433 K for solute-depleted Cu-25Zn-3.4AI, which is lower than the experimental temperature 523 K. Thus, nucleation by shear mechanism is impossible in this circumstance. Therefore, it is concluded that, like bainite in steels and Ag-Cd, bainite in     

Growth of β-FeSi2 layers deposited from a molten salt

β-FeSi₂ layers have been successfully grown using a molten salt method for the first time. It was found that single phase and homogeneous β-FeSi₂ layers with a columnar domain structure can be grown on FeSi substrates. The layer thickness was demonstrated to be controllable by the growth temperature and time, and was diffusion controlled. It was shown that the layers were void- and crack-free compared to similar layers grown on Fe substrates: this difference is explained in terms of Fe diffusion. This vacuum-free simple growth technique is useful for the fabrication of large area semiconductor devices at low cost.     

复合布尔函数中含某单乘积项的快速判定算法

引入了布尔函数的基本积、单乘积项等概念，通过实例剖析了复合布尔函数中是否含某一单乘积项的一般判定方法，在该基础上提出了一种快速判定途径，并给出了快速判定算法的具体描述，同时对算法进行了实验，结果表明该算法快速有效。     

InxGa1−xAs ohmic contacts to n-type GaAs with a tungsten nitride barrier

Significant reduction of the contact resistance of In_0.7Ga_0.3As/Ni/W contacts (which were previously developed by sputtering in our laboratory) was achieved by depositing a W₂N barrier layer between the Ni layer and W layer. The In_0.7Ga_0.3 As/Ni/W₂N/W contact prepared by the radio-frequency sputtering technique showed the lowest contact resistance of 0.2 Ωmm after annealing at 550°C for 10 s. This contact also provided a smooth surface, good reproducibility, and excellent thermal stability at 400°C. The polycrystalline W₂N layer was found to suppress the In diffusion to the contact surface, leading to improvement of the surface morphology and an increase in the total area of the In_xGa−As between metal and the GaAs substrate. These improvements are believed to reduce the contact resistance.     

Zr-2/Cr反应扩散研究

研究了Zr-2/Cr扩散偶在1023－1123K范围内的反应扩散，用扫描电镜观察反应宽度，用能谱仪（EDS）测定了反应层Zr,Fe和Cr沿扩散方向的浓度分布，研究了反应层的生长动力学，结果表明，反应层生长基本符合抛物经规律，生长过程受扩散控制，用Boltzman-Matano-Heumann模型计算了Cr在反应层Zr（Fe,Cr）2中的互扩散系数D，得到了互扩散系数D与温度的Arrhenius方程，由计算的扩散数据与Cr在Zr中形成稀固溶体时Cr的扩散数据比较可知，Cr在金属间化合物Zr（Fe,Cr）2中的扩散比在稀因溶体中的扩散快5个数量级。     

基底元素表面富集与扩散阻档层

根据An－Ag系统以及An－Cu系统的扩散系数计算，提出了扩散阻挡层模型。利用这个模型对Au－Ag系统进行有关实验，得利了较好的验证。