Adhesion Mechanisms of Polyurethanes to Glass Surfaces. III. Investigation of Possible Physico-Chemical Interactions at the Interphase

Surface free energies of polyurethanes made from toluene diisocyanate and 1, 4 butanediol-based hard segments and caprolactone polyol-based soft segments were calculated using additive functions. Good agreement was found between the calculated values based on additive functions and the calculated values based on contact angle measurements. The phase-separated polyurethanes were found to have a higher polar surface free energy component (γ^P). This was linked to the preferential segregation of butanediol/butanediol-derived moieties to the polyurethane surfaces due to phase separation. The adhesion values of these polyurethanes to soda-lime glass were correlated with their respective γ^P values and a linear relationship was found. It was also shown that the adhesion values of the low γ^P polyurethanes improved substantially when the glass surfaces were coated with a thin layer of butanediol prior to the bonding. The modulus of the interphase region rich in butanediol was evaluated. Although a modulus increase was found at the interface, this increase was found to play a secondary role in the adhesion. The chemical interactions at the polyurethane/glass interphase were investigated by pre-treating the glass surfaces with methyl-trimethoxysilane and trimethylchlorosilane prior to adhesion testing. The adhesion data showed no significant difference between the uncoated and the silane-treated glass substrates. Based on this experimental evidence, the possibility of any covalent or ionic bonding at the polyurethane/glass interphase was assumed negligible. It was determined that the mechanism of adhesion between the polyurethanes and the glass surface could be through the formation of an interphase region in which hydrogen bonding between the butanediol-rich interphase region and the hydroxylated glass surface plays a key role.     

掺Tb_2O_3法拉第旋转玻璃

本文研究了掺Tb_2O_3的法拉第旋转玻璃的组成、物理化学性质及制备技术,实验结果表明维尔德常数V随着Tb_2O_3浓度的增大而增大,硼硅酸盐玻璃中Tb_2O_3含量大于20％(mol)时,维尔德常数可以达到-0.0030min/A/m·cm,从熔制试验结果0.5L铂坩埚可以获得质量较好的φ50×25mm的样品。     

气垫性能及平板玻璃缓冲包装

对我国发明的缓冲包装气垫进行静态试验,测其载荷-变形曲线,表明它属于正切型;对气垫作为内衬的PZOV型平板玻璃包装件进行冲击和振动试验,证明具有优良的防震缓冲性能,适于平板玻璃的运输包装。     

新型梳形电缆防火墙的应用

通过新型梳形电缆防火墙的实施，有效地限制了电缆火灾范围，增强了电缆防火、隔火能力，并详细地介绍了梳形电缆防火墙的原理结构、安装使用和注意事项。     

Effect of Post Annealing on the Microstructure and Magnetic Properties of NdFeB/α-Fe/NdFeB Thin Films

A series of nanocomposite thin films, composed of Nd2Fe14B and α-Fe, has been prepared by DC-magnetron sputtering combined ion beam sputtering onto Si (100) substrates. The effects of post annealing on the microstructure and magnetic properties of [NdFeB/α-Fe/NdFeB]-type thin films have been investigated. The X-ray diffraction (XRD) study showed that annealing of the films for 30min at temperatures 550,600,650,700℃ resulted in the appearance of diffraction peaks, characteristic for Nd2Fe14B tetragonal structure, α-Fe and Nd2O3 phases. The investigation using the Vibrating Sample Magnetometer (VSM) with a maximum applied field of 2 T indicated that with the increase of the annealing temperature, the magnetic properties of the multilayer films were improved and reached peak value at 650℃ (Hci=41.72kA·m-1, Mr/Ms=0.4, (BH)max=30.35kJ·m-3), after which the magnetic properties were decreased greatly. Along with the increase of the thickness of α-Fe layer from Tα-Fe16nm, the coercivity Hci, saturation magnetization Ms, and remanence ratio Mr/Ms all declined. As the Atomic Force Microscope (AFM) indicated, after being annealed at 650℃ for 30min, the sample was showed fine surface morphology with grain size 60nm≤dα-Fe≤80nm and 100nm≤dNdFeB≤150nm.     

电容器介质吸收电流的测量和表征

在外电场作用下，电容器介质的吸收电流和漏电电流混杂而难以分开，但外电场除去后吸收电流对电容器放电总电荷所贡献的百分比具有确定值，吸收电流的释放遵从自由弛豫规律。可用响应时间ｒ’表征。实验给出了一些常见介质的吸收电流表征参数。     

填充HDPE复合材料基体结晶形态的控制因素

本文以HDPE/玻璃微珠和HDPE/CaCO₃体系为研究模型,通过扫描电镜、红外光谱、偏光显微、小角激光散射和材料力学性能实验等方法考察了这两种体系的界面粘结性、填料含量、粒径及试样成型冷却速率等与其材料性能及基体结晶形态变化间的关系。实验结果表明;在复合材料试样成型过程中,因基体树脂冷却收缩而产生的界面应力可干扰基体中球晶的生长环境,应变诱导填料颗粒周围基体树脂的结晶,促使其表面伸展链晶体结构的形成,并由此而明显改变了复合材料的耐热性;复合材料的界面粘结性是产生这种应变诱导作用,并控制异相结晶的关键。     

Study on ancient Chinese imitated GE ware by INAA and WDXRF

Imitated GE ware was one of the most famous products of Jingdezhen porcelain field in Ming dynasty (AD 1368-1644). The exterior features of its body and glaze are very marvelous. Black foot, purple mouth and crazing glaze are the main features of imitated GE ware. Until now, the key conditions of resulting these features are not clearly identified. In order to find the critical elements for firing these features, instrumental neutron activation analysis (INAA) and wavelength-dispersive X-ray fluorescence (WDXRF) were used to determine the element abundance patterns of imitated GE ware body and glaze. The experimental data was compared with that of imitated Longquan celadon and of Longquan celadon. The analytical results indicated that Fe, Ti and Na were the critical elements. The body of imitated GE ware which contains high Fe and Ti are the basic conditions of firing its black body, black foot and purple mouth. The glaze of imitated GE ware which contains high Na is the main condition of producing its crazing glaze. Na is the critical element which enlarges the difference in expansion coefficients between the glaze and body of imitated GE ware. Furthermore, Zijin soil was added into kaolin to make the body rich in Fe and Ti. And something which was rich in Na was used to produce crazing glaze in the manufacturing process of imitated GE ware.     

LD泵浦的声光调Q腔内倍频激光器

研制成用ＬＤ泵浦的声光调Ｑ的Ｎｄ：ＹＶＯ４－ＫＴＰ腔内倍频激光器，得到了ＴＥＭ００模、频率高达１００ｋＨｚ的稳定的５３２ｕｍ绿激光脉冲系列输出，阈值泵浦功率为２７ｍＷ；在连续５７０ｍＷ的泵浦功率下，绿激光脉冲的峰值功率达１１００Ｗ，脉宽为４．６ｕｓ；输出功率稳定，在±５℃的工作温度变化下，输出功率变化小于±２％。此种器件可望得到广泛的应用。