本文报道了应用环境扫描电镜（ESEM）和同步辐射X射线白光形貌术对采用提拉法生长出的Nd:YVO4晶体进行的形貌及生长缺陷的分析,获得了该晶体的开裂表面的ESEM形貌像以及取自晶体肩部和中间部位的（001）面的同步辐射白光形貌像,观察到了位错、包裹物等缺陷,可为生长高质量的Nd:YVO4晶体提供重要的启示.     

BaFe12O19/SiO2-B2O3微晶玻璃陶瓷的制备和微波性能

采用柠檬酸sol-gel工艺合成了BaFe12O19/SiO2-B2O3微晶玻璃陶瓷，研究了SiO2-B2O3玻璃的含量，Ba/Fe原子比和热处理温度对体系析出晶相的影响，以及介电常数和磁异率在1MHz-6GHz频率范围的变化规律，结果表明，休系中SiO2-B2O3玻璃的含量和Ba/Fe比越高，BaF312O19相的析出越困难，前驱体合适的热处理温度为1000℃，介电常数和磁导率基本上随测试频率的增而加下降；介电损耗的最大值为0．43，磁损耗较小。     

Effects of solvent and temperature on the coupling agent/epoxy resin interface

Increased wetting of the coupling agent/epoxy resin interface was observed when γ-glycidoxypropyltrimethoxysilane, polyfunctional aminosilane and γ-aminopropyltriethoxysilane were applied respectively from methyllethylketone, dimethylformamide and water on woven glass cloths which had been cleaned at 300°C. However, when factory-applied coupling agents were burnt off the woven cloths and fresh coupling agents re-applied, it was found that the nature of the factory-applied coupling agent influenced subsequent wetting. Thinner glass fibres showed a greater improvement in wetting rate than thicker fibres in those solvents identified to be good for improved wettability, irrespective of the heat-cleaning temperature.     

Physical Aging of Amorphous Fructose

ABSTRACT: Physical aging of amorphous anhydrous fructose at temperature 5 °C and at 22 °C was studied using differential scanning calorimetry (DSC). The dynamic glass transition temperature, T_g0 for unaged samples was 16 °C and 13.3 °C for heating rate of 10 °C/min and 1 °C/min, respectively. The fictive temperature, T_f0 for unaged samples calculated by Richardson and Savill method was 12 °C, which is close to the dynamic value obtained from the lower DSC heating rate. The fictive temperature T_f of the aged fructose glasses at temperatures both below and above the transition region was fitted well by a non-exponential decay function (Williams-Watts form). Aging above the transition region (22 °C) for 18 d increased both the dynamic glass transition temperature T_g and the fictive temperature T_f. However, aging below the transition region (5 °C) for 1 d increased the dynamic glass transition temperature T_g but decreased the fictive temperature T_f.     

JOINING MECHANISMS OF β''''-Al2O3 CERAMIC AND PYREX GLASS TO Al MATRIX COMPOSITE

The bonding of β'-Al2O3 and pyrex glass to Al matrix composites by anodic bonding process is achieved. The microstructure of the bonded interface and the joining mechanisms are analyzed with scanning electron microscope (SEM), energy dispersive X-ray fluorescence spectrometer (EDX). It is observed that the bonding region across the interface consists of the metal layer, oxide transitional layer and the ceramic layer, with the transitional layer composed of surface region and sub-surface region. The bonding process can mainly be categorized into anodic bonding process and solid state diffusing process. The pile-up of the ions and its drift in the interface area are the main reasons for anode oxidation and joining of the interface. The temperature, voltage and the drift ions in the ceramic or glass during the bonding process are the essential conditions to solid state diffusing and oxide bonding at the interface. The voltages, temperature, pressure as well as the surface state are the main factors that influence the anodic bonding.     

太钢不锈冷轧工程防腐蚀施工技术

防腐蚀施工工艺掌握的好坏，直接影响到工程投入生产后的使用寿命，为保证工程质量，以太钢不锈冷轧改造工程冷线防腐为例，对其常发生的质量通病进行认真分析，总结出一套行之有效的施工技术。     

Improved direct bonding method of Nd:YVO4 and YVO4 laser crystals

We succeeded in the fabrication of bonded laser crystals composed of a neodymium-doped YVO₄ laser crystal (Nd:YVO₄) and its host crystals YVO₄ by a newly developed dry etching technique using an argon ion beam. The optical distortion caused by the bonded interface of size 5 mm × 6 mm was estimated to be 0.05λ at 633 nm. From the comparison of laser performance pumped by a laser diode, the bonded crystals could increase the laser output power by nearly twice that of the non-bonded crystals with the same degree of polarization of 99.2%. To analyze the mechanism of the enhanced reduction of the thermal load in the bonded crystals, numerical simulations with a finite-element method were also performed.     

石英玻璃结构调整和二阶非线性光学效应产生机制的理论研究

从非谐振动理论观点出发．考虑到玻璃在外场及加热条件下结构取向调整和弛豫，对外部静电场和加热的温度及加热时间对其信频光产生的影响进行了探讨性理论研究，结果较好地解释了有关实验现象。     

A simple modification to the LKB 7800 series Knifemaker and a balanced-break method to prepare glass knives for cryosectioning

A novel method of using the LKB 7800 series Knifemaker to produce glass knives using a balanced break is described. The method produces knives of sufficient quality to section aldehyde-fixed, sucrose-cryoprotected, frozen biological material in a cooled cryochamber of an ultramicrotome. The modifications to the Knifemaker are minimal and, if required, the machine can be returned easily to its normal state after use.     

Entropy,Free Volume,and Cooperative Relaxation

The high frequency end of the relaxation spectrum for polymer molecules involves the rotation of the segmental bonds. This fast relaxation process, however, cannot take place easily in the condensed state crowded by the densely packed conformers, necessitating the slower cooperatively synchronous relaxation. As the temperature is lowered, the domain of cooperativity grows towards the infinite size at the Kauzmann zero entropy temperature, though actually the system deviates from the equilibrium as the glass transition intervenes typically at 50 K above that temperature. The excess enthalpy and entropy drop faster than predicted by the rotational isomeric states which would reach zero only at 0 K. The real ΔC_P is greater than that of the RIS value. The actual volume in excess of the crystalline lattice volume, however, points towards zero at 0 K. Thus, a polymer with higher T_g typically exhibits a lower density and modulus in the glassy state. Since the configurational entropy associated with the free volume is proportional to the logarithm of the latter, the Kauzmann temperature can be scaled by ln M, where M is the algebraic average of the conformer molecular weight. The temperature dependence of the most dominant, i.e., the largest equilibrium domain size will result in the Adam-Gibbs and Vogel equations for the characteristic relaxation time. The cooperative domain distribution leads to the relaxation spectrum that follows a power law. The relationship between the characteristic relaxation time and the rate of physical aging is derived.