Possibilities and extension of XRD material response analysis in failure research for the advanced evaluation of the damage level of Hertzian loaded components

Due to clearly distinguishable damage symptoms, it is differentiated between the surface and sub‐surface failure mode of rolling bearings. Material states red out by X‐ray diffraction (XRD) residual stress measurements point to a variety of loading conditions especially at raceway surfaces that are associated with several competing failure mechanisms. The corresponding lifetime reduction can range from the lower fatigue strength region to material ratcheting in extreme cases. Relevant position of the microstructural changes and nature of the failure mechanisms are characterized. The time alteration of the XRD material parameters measured at or near the surface and at the depth of the maximum equivalent stress correlates, in a different manner, with the statistical parameter of the 10 % bearing life. Both failure modes are illustrated by concrete examples. Contaminated lubricant and boundary lubrication, which represent practically important surface‐induced failures, are discussed in more detail. Gray staining, i.e. shallow pitting, often occurs without distinct indication of global material aging by means of XRD characteristics. Here, scanning electron microscopy observations and electron microprobe analyses point to corrosion fatigue as acting surface failure mechanism. The interaction between material and lubricant under complex loading regimes particularly of mixed friction and corrosion opens further failure research areas in the field of tribology.     

Cu－MnO_2同槽电解半工业试验研究

提出了Ｃｕ－ＭｎＯ＿２同槽电解的新工艺，在同一电解槽同时得到电铜和电解二氧化锰两种产品，该新工艺具有低电耗、低酸雾污染和低酸耗等优点．     

Relationship between CO2 Sensor Voltage Response and Phase Equilibrium of Solid Electrolyte Na, K-β/β"-Al2O3

A type of CO2 sensor based on oxygen concentration cell was designed as following: Cell I: Pt | Au, O2,CO2|Na2CO3(Au)|NKBA(Au)|YSZ|O2, CO2|Pt or Cell Ⅱ: Pt|Au, O2, CO2|K2CO3(Au)|NKBA(Au)|YSZ|O2, CO2|Pt.(Na,K-β/β″-Al2O3 is named by NKBA). The sensor signal is consistent with the Nernstian slope within the region ofphase equilibrium for Na, K-β/β"-Al2O3 material. The relationship between CO2 sensor voltage response and phaseequilibrium of solid electrolyte Na, K-β/β-Al2O3 is discussed in this paper.     

Phenol novolac/poly(4- hydroxyphenylmaleimide) blend hardeners for DGEBA-type epoxy resin

Phenol novolac/poly (4-hydroxyphenylmaleimide) (PHPMI) blends were used as an epoxy resin hardener. The curing behavior of the above system and the thermal and mechanical properties of the cured epoxy resin were studied. It was not necessary to use a curing accelerator for this system, because PHPMI caused acceleration of the curing reaction. The curing mechanism of this system was investigated by using model compounds. Test pieces from the neat resins and the glass fiber reinforced resins were evaluated in terms of thermal and mechanical properties, respectively. It was found that heat resistance and mechanical properties were improved by increasing the amount of PHPMI in the hardener.     

含H2S井完井液用除硫剂和缓蚀剂

含H_2S井完井液对井下金属管串具有腐蚀性。采用锌基或铁基螯合物除硫剂及咪唑啉缓蚀剂可有效地防止这种腐蚀的发生。本文对H_2S的腐蚀、除硫剂和缓蚀剂产品及其对产层的损害作了介绍与探讨。     

TiB2和SiCW对Al2O3陶瓷材料高温摩擦磨损特性的影响

研究了Ａｌ２Ｏ３、Ａｌ２ｏ３／ＴｉＢ２和Ａｌ２Ｏ３／ＴｉＢ２／ＳｉＣＷ三处陶瓷材料在不同条件下的擦靡损特性。结果表明：三种陶瓷材料与硬质合金摩擦副的摩擦系数随温度温度的增加有不同的变化规律，摩擦表面的Ｘ射线衍射分析表明，摩擦系数的变化与陶瓷物膜的和结构有关，在高温下Ａｌ２Ｏ３／ＴｉＢ２陶瓷材料摩擦表面形成了具有优良的高温润性的ＴｉＯ２氧化膜，因而ＴｉＢ２的加入明显改善了Ａｌ２Ｏ３陶瓷材料 摩擦磨损     

自韧Si3N4陶瓷的显微结构及其性能研究

利用热压的方法制得室温断裂韧性和抗弯强度分别为１１．２ＭＰａ·ｍ￣（１／２）、８２３ＭＰａ，高温（１３５０℃）断裂韧性和抗弯强度分别为２３．９ＭＰａ·ｍ￣（１／２）、６３０ＭＰａ的自韧Ｓｉ＿３Ｎ＿４陶瓷。研究了显微结构和力学性能之间的关系。结果表明：玻璃相的含量、β－Ｓｉ＿３Ｎ＿４的长径比等对性能有重要影响。分析了自韧Ｓｉ＿３Ｎ＿４陶瓷的增韧机理，通过ＳＥＭ明显观察到Ｓｉ＿３Ｎ＿４中存在裂纹偏转、分支和β－Ｓｉ＿３Ｎ＿４拔出现象。     

A Study of the Specific Heats of the Compounds in the Sm_2O_3-BaO-CuO System

By means of X-ray diffraction and adiabatic scanning calorimeter,the specific heatsof five compounds in the Sm_2O_3-BaO--CuO system,such as Sm_2BaO_4,Sm_2CuO_4,BaCuO_4,Sm_2BaCuO_5,SmBa_2Cu_3O_(7-x),from -150℃ to 800℃ have been measured.It is found that the specific heats ofthese compounds increase smoothly with the increase of temperature.