自动焊技术在涩宁兰输气管道X70钢试验段上的应用

通过涩宁兰输气管道X70钢试验段的施工,进一步探索和完善自动焊接技术在高强钢管道焊接中的应用。文章介绍了该试验段施工的焊接设备、焊材和焊接工艺,可为同类焊接工程提供借鉴。     

Metallurgical failure analysis of cold cracking in a structural steel weldment: Revisiting a classic failure mechanism

Cold cracking of structural steel weldments is a well-characterized, well-documented, and well-understood failure mechanism. Extensive effort has been put forth to recognize the welding and materials selection parameters that are conducive to cold cracking; however, these engineering efforts have not fully eliminated the occurrence of such failures. This article describes cold cracking failure specifically related to the construction industry. This particular failure was successfully identified prior to final erection of the structural member, and the weld was successfully reworked. These actions potentially prevented a serious catastrophic event that could have occurred have occurred either later in the construction process or possibly during the use of the building. Individual welding parameters, such as electrode/wire selection, joint design, and pre/postheating, played a role in the failure, and a number of human factors relating to the actual fabrication practices also contributed to the failure process.     

WC对铜基和镍基喷焊覆层材料耐气蚀性能的影响

在CuNiSiB,NiCrSiB自熔合金粉末中添加WC陶瓷颗粒，利用氧乙炔焰粉末喷焊工艺制备覆层材料，用超声波振动气蚀仪对覆层材料进行耐气蚀性能研究，用扫描电子显微镜对覆层材料表面气蚀破坏形貌进行观察，结果表明：复合覆层材料的耐气蚀能力比基体强；提高CuNiSiB覆层材料耐气蚀能力的途径是强化晶界，还探讨了覆层材料的气蚀破坏机理。     

HSLA-80/100钢的焊接

对ＨＳＬＡ－８０／１００钢的焊接性、焊接材料及焊接工艺进行了综述，并指出了现存在的主要问题。     

Planning the GMAW process by constraint propagation

Although the gas metal arc welding (GMAW) process is widely used for joining metals, its planning is still a cumbersome task. The planning procedure involves many complex interrelationships among the process variables and depends heavily on empirical knowledge. Therefore, a solution method that allows a convenient way to represent the domain knowledge and evaluate the process variable relationships is needed. Further, the lack of a strong domain theory to quantify these interrelationships is a deficiency in the planning of the GMAW process. This paper presents a solution method that overcomes this deficiency and introduces a convenient knowledge representation scheme. The solution method considers the planning procedure to be a constraint satisfaction problem (CSP). The AC-4 algorithm is used to obtain arc consistency among nodes in the constraint network and the PC-4 algorithm is applied to obtain path consistency in the network. A modified version of the AC-4 algorithm is developed to reduce the search space and correspondingly reduce the computation time. An example is presented to demonstrate the capability of the method and its potential to reduce lead time.     

Ti-23Al-14Nb-3V合金氩弧焊接头的显微组织及其力学性能

研究了预热对Ｔｉ－２３Ａｌ－１４Ｎｂ－３Ｖ合金焊接性，特别是对消除氩弧焊冷裂纹的作用以及对接头显微组织和力学性能的影响。结果表明，焊前预热可有效降低该合金的冷裂倾向。经预热处理后，焊缝区的结晶层状线消失，热影响区的硬度峰得到缓和，整个焊缝的显微硬度分布趋于均匀，但焊缝区的枝晶发生粗化，热影响区有所扩大。焊件接头的拉伸试验表明，预热可使焊缝区的接头强度系数增加，但无论预热与否，接头强度均低于母材强度，且不显示宏观塑性。     

Friction Stir Welding of Ceramic Particle Reinforced Aluminium Based Metal Matrix Composites

The mechanical and microstructural properties of 6061+20% Al₂O_3p and 7005+10% Al₂O_3p aluminium based metal matrix composites joined by friction stir welding were analyzed in the present study. The two materials were welded into the form of sheets of 7 mm thickness after T6 treatment and were tested in tension at room temperature. The microstructure of the joints was observed by optical microscopy and the fracture surfaces were analyzed by employing a scanning electron microscope equipped with field emission gun in order to study the micromechanisms involved during the deformation.     

Microstructural changes accompanying repair welding in 5xxx aluminium alloys and their effect on the mechanical properties

At the shipyards, the aluminium alloy 5083 is welded with a multi-pass sequence using the metal inert gas technique. If, while checking the weld integrity either after welding or during service, defects are detected in the vicinity of the weldment, repairs are usually employed to extend the service life.

The repair method involves removal of the upper passes, depending on the thickness and re-welding under the same conditions.

Purpose of this paper is to examine the microstructural changes accompanying repair welding, define their effect on properties of primary importance and set, if possible, an upper limit as far as the number of repairs is concerned.     

覆膜滤料的滤尘性能测试方法研究

由于覆膜滤料的结构和性能有别于普通滤料，因而普通滤料的滤尘性能测试方法不完全适用于覆滤料。本文作者在总结实践经验的基础上，提出了在覆膜滤料的滤尘性能测试中应注意的一些问题和应增加的测试项目。     

WDB620高强钢应用于大型蜗壳的焊接制造工艺研究

2005年初,水电十四局承担了漫湾二期水电站和小湾水电站蜗壳的制造任务。蜗壳钢材选用国产600 MPa级别高强钢,为了全面综合地考核该级别钢种的材料强度和安全裕度,检验模拟大型蜗壳焊接制造工艺的可靠性。对国产的WDB620高强钢进行了可焊性和制造工艺性试验研究,并在国内首次设计、制造模拟压力容器并对其进行水压试验和爆破试验。研究成果通过中国水电集团公司鉴定,结论为该课题研究成果达到国内选进水平。