Investigations of surface degradation of high‐density polyethylene materials resulting from tracking,using physicochemical analysis

In the present work tracking phenomena were studied with high‐density polyethylene (HDPE) materials under dc voltage, with NH₄Cl and acid rain as contaminants. It was determined that the tracking time of the material depends on the conductivity and flow rate of the contaminant. Furthermore, physicochemical analysis by wide‐angle X‐ray diffraction studies, differential scanning calorimetry, and luminescence spectroscopy was carried out, whereupon it was concluded that the tracking process is a surface‐degradation process. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 2843–2849, 2002; DOI 10.1002/app.10260     

Surface Areas of Nitrated Hydrotalcites

Hydrotalcites in the nitrate form were prepared using microwave irradiation in the hydrotreatment step. The surface area (BET) of nitrated hydrotalcites was evaluated. Solids were characterized by atomic absorption, X-ray diffraction and BET analysis. Thermal pretreatment temperature determined the surface area of the hydrotalcites.     

聚硅氧烷-丙烯酸酯共聚物互改性产物的表面特性

通过测定参照液体在固体表面的接触角，计算固体的表面能及固体／液体接触体系的粘附功，考查了聚硅氧烷-丙烯酸酯共聚物互改性产物的表面特性及其对粘接性能影响。     

Zinc Coated Steel/Epoxy Adhesive Systems: Investigation of the Interfacial Zone by FTIR Spectroscopy

The present study takes advantage of the ability of Fourier Transform Infrared Spectroscopy (FTIR) for the analysis of ultrathin organic films on metals. FTIR in the reflection mode (IRRAS) is used in order to study the interaction of ultrathin films of dicyandiamide (hardener of most one-pack epoxy resins) with various substrates, model ones such as gold or zinc and industrial ones such as steel and zinc-coated steels.

Pure zinc surfaces and, to a lesser extent, zinc-coated steels are shown to react with dicyandiamide after heating at 180°C, as evidenced by the frequency shift of the absorption band (at about 2200 cm^-1) characteristic for nitrile groups. As real systems consist of thick layers of a fully formulated adhesive cured onto a metallic substrate, the direct investigation of such a buried interphase is no longer possible by FTIR and by most of the known spectroscopies. Some mechanically tested specimens are then analysed, after failure, by FTIR microspectrometry. The spectra obtained, corresponding to the fracture initiation zone which is about 100 μm in diameter, advocate for the presence of an ultrathin layer of modified polymer still covering the substrate.     

HEAT TRANSFER BETWEEN ROUGH SURFACES IN CONTACT OVER A HIGHLY ELLIPTICAL CONTOUR AREA: COMPARISON OF EXPERIMENTAL AND NUMERICAL RESULTS

This paper describes experimental and numerical studies of heat transfer between surfaces in contact over a highly elliptical area in a gas or in vacuum. Measurements of the steady-state thermal resistance of a high aspect ratio contact formed between cylindrical steel surfaces with widely different radii of curvature (76 cm vs 0.95 cm) are reported for two levels of surface roughness (0.05 μm and 1.0 μm rms) and compared to 3-D numerical results obtained with the multigrid method. Theoretical results obtained by evaluating the contact conductance acting over each surface element within the contour area with a method developed previously for rough but nominally flat surfaces are shown to be in excellent agreement with the rough surface experimental data.     

Preadhesion Laser Treatment of Aluminum Surfaces

An excimer laser may be used for preadhesion treatment of aluminum alloys. This method presents an alternative to the use of ecologically unfriendly chemicals involved in conventional anodizing pretreatments.

Experimental results indicate that preadhesion laser surface treatment significantly improved the shear strength of modified-epoxy bonded aluminum specimens compared with untreated and anodized substrates. The best results were obtained with laser energy of about 0.2 J/Pulse/cm² where single lap shear strength was improved by 600-700% compared with that of untreated Al alloy, and by 40% compared with chromic acid anodizing pretreatment.

The mode of failure changed from adhesive to cohesive as the number of laser pulses increased during treatment. The latter phenomenon has been correlated with morphology changes as revealed by electron microscopy, and chemical modification as indicated by Auger and infrared spectroscopy.

It can be concluded that the excimer laser has potential as a precise, clean and simple preadhesion treatment of Al alloys.     

采用表面粘涂技术提高设备的抗腐蚀性能

通过表面粘涂，对受到腐蚀、冲蚀、气蚀的设备进行表面修补与防护，可提高设备的使用寿命。     

高速气流冲击式粉体表面改性装置——HYBRIDIZATION系统及应用

利用高速气流冲击法进行粉体/粉体系表面改性技术,是迄今为止各种粉体材料开发中最为引人注目的技术之一。HYBRIDIZATION(下称HYB)系统是利用高速气流冲击法对微粉体进行干式/机械化处理,是使材料复合化的最实用的装置,可对各类有机物、无机物、金属等进行广泛组合,通用性很强,适用于许多行业领域。从本文所述的系统构成、型式,有关的典型球形化处理的运转特性,利用复合化高温粉体测定被处理粉体表面温度,利用颜料改变色调等的处理特点及该系统的适用性等(一部分是从已发表的学术论文及专利上摘录的),可以说明HYB系统的概况。     

IR study of the interaction of hydroxyl groups of silica gel with Cr species of Phillips' type catalysts

Spectroscopic evidence for the interaction of hydroxyl groups and chromium ions was obtained using a catalyst prepared from chromyl chloride. A new OH peak, observed at 3705 cm^–1 after pumping away CO gas, is attributed to the direct interaction of OH with the low-valent chromium. This peak shifts to 3590 cm^–1 on contact with O₂ at room temperature and it is assigned to a hydroxyl interacting with the oxidized chromium. New assignments are also proposed for IR bands of CO presorbed on the catalyst. The peak due to CO at 2188 cm^–1 decreases as the OH intensity at 3705 cm^–1 increases, suggesting that the former peak arises from adsorption on Cr(II) species to which two oxygen atoms are attached.