综述了低熔封接玻璃的组成特点，给出了大量低熔玻璃组成实例，批出了低熔封接玻璃的封接低温化和无铅化发展方向，磷酸盐玻璃是首选组成之一。新的制备工艺和新的玻璃形成体系将对封接玻璃发展起着十分重要的作用。     

Preparation of ultra-fine copper powder and its lead-free conductive thick film

In this paper, non-agglomerated monodispersed ultra-fine copper metallic powders have been synthesized with chemical reduction method. Fine lead-free glass powders were also prepared by solid synthesis process. Thick film paste prepared by above-mentioned copper metallic powders and lead-free glass powders was applied as conductive paste of MLCC. Mixture of glass and zinc oxide give the thick film a high adhesion strength which is attributed to the rough interface from interfacial reaction between glass and chip, and a good densification. Diffusion of metal between copper thick film and nickel thick film is clear. Ni-Cu solid solution appears under high temperature firing.     

尖晶石型纳米钴蓝陶瓷颜料的制备

采用化学共沉淀法作为钴蓝颜料的制备方法,探讨了主要工艺因素对制备钴蓝颜料性能的影响,对制备的样品进行了测试与表征。结果表明:Co2+和Al3+物质的量比为1∶2.5时,制备的钴蓝样品颜色饱和度与明度最高,沉淀剂为尿素时制得的样品的粒度最小,粒度分布比较均匀。前驱体的洗涤过程采取水洗加醇洗的方法可有效减少样品的硬团聚现象,且前驱体的最佳煅烧温度为950℃左右。     

溶胶-凝胶生物玻璃多孔材料显微结构和生物活性的扫描电镜及红外光谱分析

本文利用溶胶．凝胶法制备了CaO-P2O5-SiO，系统生物活性玻璃，并以其为原料制备了用于骨修复及骨组织工程支架的块状生物活性材料。利用体外实验方法(invitro)结合x射线衍射(XRD)、扫描电子显微镜(SEM)和傅立叶变换红外光谱分析(FTIR)技术对不同烧结工艺制备的材料结构、晶相和生物活性的影响进行了分析研究。研究表明，经800℃和1100℃烧结5min的两种材料均有硅磷酸钙Ca5(PO4)2SjO4微晶相析出。烧结温度越高，析出微晶相的体积比例越大，材料的生物活性则越低。在模拟生理溶液中碳酸羟基磷灰石(HCA)只在烧结体中的玻璃颗粒表面形成，而在其硅磷酸钙Ca5(PO4)2SiO4微晶相表面未发现HCA形成。     

动态陶瓷微滤膜净化沐浴污水实用研究

利用自制的动态陶瓷微滤膜对沐浴污水进行了处理,根据处理水质指标及膜操作参数的比较,发现在0.15MPa以下时,膜通量随压力的升高明显增加,大于0.15MPa时,压力对膜通量的影响不明显。合适的操作压力是0.1～0.15MPa,稳定通量为90～110L/m2·h。不同压力出水CODCr去除率达87%～98%、浊度从120°降到3°以下,处理后颜色为无色。并根据实验结果进行了工程化工艺初步设计和经济分析。     

Thermally stimulated discharge current (TSDC) and dielectric constant of semiconducting glasses

In this paper the results of thermally stimulated discharge current (TSDC) and dielectric constant for 40PbO-60Bi₂O₃ glass thermoelectrets are presented. Measurements of TSDC and dielectric constant, ǵe, have been carried out in the temperature range 30–300°C. The thermoelectrets were prepared at different polarizing fields. The various observed peaks in the thermograms are discussed on the basis of space charge polarization. The trap energy is evaluated from the Garlick-Gibson plot of initial rise method. Similarly other parameters such as relaxation time, charge release etc are evaluated.     

转动玻璃圆筒激光器

本文介绍了转动玻璃圆筒激光器的设计及实验结果,得到了脉冲能量为13J,重复频率为15Hz的激光输出。电光转换效率为2.2％,斜效率为3.4％。     

Combined PIXE and SEM study of the behaviour of trace elements in gel formed around implant coated with bioactive glass

Bioactive glasses are used as coating biomaterials to facilitate anchorage of metallic prostheses implanted into the body. The aim of this work is to study the behavior of gel formed in contact with alloys and BVA and BVH bioactive glasses implanted. Cylinders of metallic implants composed by Ti, Al and V, are coated with bioactive glass. Three sheep were implanted for different time length: 3, 6 and 12 months in the femoral epiphysis. Results obtained with particle induced X-ray emission and scanning electron microscopy show that BVA coating induces a better contact between the metallic implant and bone. On the other hand, BVH coating prevents corrosion from the metallic implant.     

分割电极片状压电致动器——(二)位移特性及狭缝宽度对其影响的实验研究

研究了悬臂梁式分割电极片状压电致动器的位移特性。理论分析表明，分割电极狭缝宽度会减小致动器自由端的位移输出，但当狭缝宽度小于致动器电极宽度的１０％时，可忽略狭缝宽度的影响。致动器端部位移的测试结果大于理论计算值。与现有磁头悬浮臂尺寸相近的致动器，在２０Ｖ～５０Ｖ的电压驱动下均可获得１μｍ～２μｍ的致动位移。对９８５０道／厘米的密度磁盘，该位移能覆盖至少一个磁道宽度，满足磁头定位两级伺服系统对第二级致动器位移的基本要求。     

Crystallization of glass in fireclay refractories; part III: Detailed study on the mullite crystal size in the ‘synthetic’ glass

Poor-grade fireclay products contain substantial amount of glass. A glass of similar composition was synthesized, nucleated and heat-treated for crystallization of mullite. The size and size-distribution of mullite crystals, the rate of change of size and the aspect ratio of the crystals were investigated in relation to the nucleating agents and temperature.