采用正变试验法，探讨了稀土变质剂对铸造结合金ZL102性能提高的可行性．试验选用了不同的稀土添加量，考察了不同的变质时间及热处理制度对ZL102的强度、硬度、流动性以及重熔性等性能的综合影响规律．试验表明，稀土是铸造铝合金的优良变质剂，并且添加单一稀土的变质效果优于混合稀土．     

用红外热象技术研究有凸台热源倾斜板的散热

本文介绍红外热象技术在工程热物理研究中某些应用的探索。作为实例，通过热象技术，实验研究了具有水平凸台离散热源的倾斜板的散热，在研究它的自然对流换热部份结合利用激光全息干涉技术。此间着重于分析倾斜角对散热的影响。     

Hybrid gas-to-particle conversion and chemical vapor deposition for the production of porous alumina films

Porous alumina films can be found in a wide variety of materials, including filters, thermal insulation components, dielectrics, biomedical and catalyst supports, coatings and adsorbents. Production methods for these films are as equally diverse as their applications. In this work, a hybrid process based upon chemical vapor deposition and gas-to-particle conversion is presented as an alternative technique for producing porous alumina films, with the main advantages of solvent-free, low substrate-temperature operation. In this process, nanoparticles were produced in the vapor phase by reaction of aluminum acetylacetonate in the presence of oxygen. Downstream of this reaction zone, these nanoparticles were collected via thermophoresis onto a cooled substrate, forming a porous film. Some deposited films were subjected to post-processing in the form of annealing in air. Fourier-transform infrared spectra and X-ray energy-dispersive spectroscopy analysis confirmed the production of alumina at processing temperatures above 973 K. X-Ray diffraction revealed that the films were amorphous. Film thickness, ranging from 30 to 250 μm, and the average deposition rate were determined from scanning electron microscopy results. From transmission electron microscopy, the average primary particle size was determined to be approximately 18 nm and the formation of nanoparticle aggregates was evident. Annealing of the films at temperatures ranging from 523 to 1173 K in the presence of air did not have an effect on particle size. The specific surface area of the powder composing the films ranged from 10 to 185 m² g⁻¹, as determined from nitrogen gas adsorption by the Brunauer–Emmett–Teller method.     

源气体流量比对F-DLC薄膜结构的影响

以高纯石墨作靶，CHF3/Ar作源气体采用反应磁控溅射法制备出了氟化类金刚石（F-DLC）薄膜。拉曼光谱表明，CHF3相对流量的增加会引起薄膜的D峰与G峰强度之比I（D）/I（G）减小，晶粒增大，芳香环结构出例下降。红外吸收光谱分析证实了这些推论，指出这是由于薄膜中氟含量上升的结果。     

高速电路中地电流的影响及其对策

从理论上分析了产生地电流干扰的原因，从而在实践上提出了一些经常被忽略，却是行之有效的方法来减小地电流的干扰，设计出高质量的电路。     

Study on Dihydrated Praseodymium Acetylacetonate by Photoacoustic Spectra with Broad Wavelength Range

Photoacousticspectroscopy (PAS)hasbeenusedtonondestructivelyinvestigatealmostallkindsofsam ples,whetherthesampleiscrystalline ,powderorgel .PAspectr oscopyisacalorimetrictechniquewhichmeasurestheenergyabsorbedandsubsequentheatingofthesamplesduetoanonradiativerelaxationpro cess .ThereforePAScanbeusedtostudyopaque ,highlyreflectiveandscatteringsamples ,whicharedif ficulttostudybyconventionalspectroscopytech niques[1] .Withouttheneedofsamplepreparation ,PASavoidstheriskofsamplealteration ,pre…     

燃气红外线辐射器的节能与环保特性分析

论述了燃气红外线辐射器的基本原理 ,对其节能与环保特性的分析表明 :与大气式燃烧器相比 ,红外线辐射器的燃料节约率为 15 %～ 45 % ,CO2 排放量减少率为 15 %～ 48% ,CO排放量减少率为 96.2 %～ 97.7% ,NOx 减少率为 94.9%～ 96.9% ,具有显著的节能与环保效果