Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。     

Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.