Composites based on eucalyptus tar pitch/castor oil polyurethane and short sisal fibers

Polymeric materials are being developed with renewable resources to promote industrial progress with environmentally friendly technologies. For this reason, polyurethane samples were prepared with 4,4′‐diphenylmethane diisocyanate (NCO/OH = 1), eucalyptus tar pitch (biopitch), castor oil as a polyol, and dibutyltin dilaurate as a catalyst. These materials were reinforced with different contents of short sisal fibers (0, 2.5, 5.0, 7.5, and 10.0%) and were prepared by resin‐transfer molding. The composites were characterized by IR absorption spectroscopy, thermal analysis (thermogravimetry and differential scanning calorimetry), impact resistance, scanning electron microscopy, and water absorption resistance. These materials showed hydrophobic characteristics, despite the addition of sisal fibers. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3797–3802, 2003     

Vinyl‐containing silicone resin as the crosslinking agent of heat‐curable silicone rubber

Heat‐curable silicone rubber (HCSR) was prepared by using vinyl‐containing silicone resin (VSR) as the crosslinking agent instead of polyvinylsilicone oil (C gum). Mechanical properties and crosslink density of the vulcanizates were measured. The results indicate that VSR is a good crosslinking agent for HCSR. The tensile strength, tearing strength, elongation at break, and hardness of the vulcanizate can reach 10.2 MPa, 29.1 kN/m, 720%, and 58 SHA, respectively. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 3123–3127, 2002; DOI 10.1002/app.10054     

Structure and properties of polyimide‐bonded magnets processed from prepolymers based on diacetyl derivatives of aromatic diamines and dianhydrides

We report a novel method of polyimide (PI) synthesis from prepolymers based on dianhydrides and diacetyl derivatives of aromatic diamines that facilitate the preparation of a melt processable mixture at 300 ± 10°C of the prepolymer and magnetic Nd‐Fe‐B alloy to provide PI‐bonded magnets with enhanced properties. It is shown that chemical structure of the prepolymers strongly influences viscosity behavior via crystallization of the oligoimide in the melt, leading to formation of PI with rigid‐rod like structure. This structural ordering of the prepolymers based on diacetyl derivative of diamine used in this study, if not controlled, leads to exponential increase of melt viscosity with time, making it practically impossible to prepare melt processable mixture of the magnetic particles and the PI prepolymers at elevated temperatures. The results obtained demonstrate that appropriate dianhydrides and diacetyl derivatives of diamines that do not lead to crystallization of oligoimides in prepolymer mixture can be used under controlled processing conditions to prepare melt‐processable PI‐bonded magnets containing rigid‐rod like PI structure that significantly increases thermal stability of the magnets. The temperature dependencies of the magnetic properties of the PI‐bonded magnets under conditions that they are likely to encounter during their service life were found to be remarkably similar to that of commercial thermoplastic magnets such as injection‐molded nylon magnets. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 478–485, 2006     

Evaluating the 1931 CIE color‐matching functions

The use of colorimetry within industry has grown extensively in the last few decades. Central to many of today's instruments is the CIE system, established in 1931. Many have questioned the validity of the assumptions made by Wright¹ and Guild,² some suggesting that the 1931 color‐matching functions are not the best representation of the human visual system's cone responses. A computational analysis was performed using metameric data to evaluate the CIE 1931 color‐matching functions as compared to with other responsivity functions. The underlying assumption was that an optimal set of responsivity functions would yield minimal color‐difference error between pairs of visually matched metamers. The difference of average color differences found in the six chosen sets of responsivity functions was small. The CIE 1931 2° color‐matching functions on average yielded the largest color difference, 4.56 ΔE. The best performance came from the CIE 1964 10° color‐matching functions, which yielded an average color difference of 4.02 ΔE. An optimization was then performed to derive a new set of color‐matching functions that were visually matched using metameric pairs of spectral data. If all pairs were to be optimized to globally minimize the average color difference, it is expected that this would produce an optimal set of responsivity functions. The optimum solution was to use a weighted combination of each set of responsivity functions. The optimized set, called the Shaw and Fairchild responsivity functions, was able to reduce the average color difference to 3.92 ΔE. In the final part of this study a computer‐based simulation of the color differences between the sets of responsivity functions was built. This simulation allowed a user to load a spectral radiance or a spectral reflectance data file and display the tristimulus match predicted by each of the seven sets of responsivity functions. © 2002 Wiley Periodicals, Inc. Col Res Appl, 27, 316–329, 2002; Published online in Wiley InterScience (www.interscience.wiley.com). DOI 10.1002/col.10077     

Decentralized weighted control for a class of large‐scale systems with multi‐modes

In this paper, the control synthesis problem for a class of large‐scale systems with multi‐modes that are called large‐scale switched systems is addressed. By introducing the concept of decentralized switching signal and the relevant decentralized average dwell time, the asymptotic stability and weighted ?₂ gain performance are investigated. It should be noted that the decentralized switching covers general switching cases for large‐scale switched systems, namely, it admits both time‐dependent switching signal and arbitrary switching signal blended in the decentralized switching. Then, on the basis of the analysis results, the decentralized weighted control scheme including state feedback controller gains and switching signals is studied. Several design algorithms are proposed to meet different controller design problems. Finally, numerical examples are provided to illustrate theoretical findings within this paper. Copyright © 2013 John Wiley & Sons, Ltd.     

Shape‐memory polyurethane/multiwalled carbon nanotube fibers

Shape‐memory polyurethane/multiwalled carbon nanotube (SMP–MWNT) composites with various multiwalled carbon nanotube (MWNT) contents were synthesized, and the corresponding SMP–MWNT fibers were prepared by melt spinning. The influence of the MWNT content on the spinnability, fracture morphology, thermal and mechanical properties, and shape‐memory behavior of the shape‐memory polymer was studied. The spinning ability of SMP–MWNTs decreased significantly with increasing MWNT content. When the MWNT content reached 8.0 wt %, the fibers could not be produced because of the poor rheological properties of the composites. The melt‐blending, extrusion, and melt‐spinning processes for the shape‐memory fiber (SMF), particularly at low MWNT contents, caused the nanotubes to distribute homogeneously and preferentially align along the drawing direction of the SMF. The crystallization in the SMF was promoted at low MWNT contents because it acted as a nucleation agent. At high MWNT contents, however, the crystallization was hindered because the movement of the polyurethane chains was restricted. The homogeneously distributed and aligned MWNTs preserved the SMF with high tenacity and initial modulus. The recovery ratio and recovery force were also improved because the MWNTs helped to store the internal elastic energy during stretching and fixing. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2007     

Characterization of konjac glucomannan–quaternized poly(4‐vinyl‐N‐butyl) pyridine blend films and their preservation effect

Novel polymer blends were prepared from a mixture of 2 wt % konjac glucomannan and 4 wt % quaternized poly(4‐vinyl‐N‐butyl) pyridine (QPVP) in aqueous solution and dried at room temperature for 72 h. Their structure and properties were studied by infrared, wide‐angle X‐ray diffraction, scanning electron microscopy, thermogravimetric analysis, and differential scanning calorimetry. Thermal stability in the dry state was reduced with increasing content of QPVP. Compared with QPVP film, the tensile strength of the films was improved in the dry state. The maximum value of 12.74% tensile break elongation was reached when the content of QPVP was 30%. Structural analysis indicated that clear phase separation was observed when the content of QPVP was only 50%. Results from the filmcoating preservation experiments with lychee showed that this blend film had water‐holding ability. The fruit weight loss rate and rot rate both decreased in various degrees. The potential uses of these novel polymer films could be as preservative films. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 1868–1875, 2004     

ZrO2对CaO-SiO2系玻璃析晶的影响

通过DSC曲线研究了不同含量的ZrO2对CaO-SiO2系玻璃析晶的影响,根据JMA方程计算动力学参数(如析晶活化能E、频率因子ν、晶化指数n)。从计算结果可以看出,随着ZrO2含量的增加,析晶活化能E减少,而频率因子ν和晶化指数n增加。当ZrO2含量为7%时,E值最小:235.58kJ/mol;n值最大:4.70。说明ZrO2在CaO-SiO2玻璃体系是有效的晶核剂。     

Factors influencing magnetic polymer microspheres prepared by dispersion polymerization

Magnetic iron oxide (Fe₃O₄) was prepared by a coprecipitation method. Core–shell composite magnetic polymer microspheres with carboxyl groups were synthesized by the dispersion polymerization of styrene and acrylic acid in the presence of magnetic oxide, and dibenzoyl peroxide was used as an initiator. The synthesized magnetic polymer microspheres were characterized with X‐ray diffraction, transmission electron microscopy, scanning electron microscopy, Fourier transform infrared spectroscopy, and so forth. The results indicated that the product was single‐phase Fe₃O₄, and its average size was about 10 nm. The configuration of the microspheres, which contained carboxyl groups, was spherical, and the average size was about 2 μm. The results of vibrating sample magnetometry tests showed that the magnetic powders produced by different surfactants had different saturation magnetizations. When poly(ethylene glycol) with a weight‐average molecular weight of 4000 was used as a surfactant, the saturation magnetization of the samples reached 69.2 emu/g. The factors that affected the shape, magnetism, size, and distribution of the microspheres were also studied. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

多种类病毒相互作用下网络信道破坏程度估计

在多种类病毒的相互作用下,网络信道破坏程度呈现较强的非线性特点,不能准确约束病毒在相互作用下的破坏性.传统的网络破坏程度估计的过程中,仅仅以单一病毒破坏程度叠加的方式去计算参数,计算具有较强的主观性,没有准确描述不同病毒的破坏作用,对评估结果误差影响较大.为解决上述问题,提出一种基于粒子滤波算法的多种类病毒相互作用下网络信道破坏程度估计方法,利用欧式距离方法对全部病毒进行分类,获取不同类型病毒的网络信道破坏程度值.通过粒子滤波算法对单一个体约束的优势,将每一个不同类型的病毒看作一个粒子,并进行训练.根据训练结果,利用粒子滤波算法对当前时刻网络信道破坏程度进行估计,完成整体评估.实验结果表明,利用改进算法进行多种类病毒相互作用下网络信道破坏程度估计,能够有效提高估计的准确率.