Effects of apitong (Dipterocarpus spp.) extractives on bond strength development and curing rate of adhesives

Emulsion polymer isocyanate ( ), polyvinyl acetate ( ) and resorcinol-formaldehyde ( ) adhesives were used to produce single lap shear specimens using resinous and non-resinous apitong (Dipterocarpus spp.) timbers. Tests showed that joints made with highly resinous apitong were about 40% weaker than similar joints made with non-resinous apitong. The resinous apitong was treated with different solvents to yield five different extractives which were characterized by infra-red analysis. Apitong extractives were then added to and adhesives and joints made with buna (Fagus crenata), a timber known to be low in extractives and easy to bond. Joints prepared using extractive-containing adhesives were generally weaker than those made with the unmodified adhesives. RF adhesives containing extractives cured more slowly than unmodified . It is thought that the acidic nature of the extractives changes the pH of the system sufficiently to affect the curing mechanism     

Rheology of cementitious paste with silica fume or limestone

The rheological behaviour of cementitious pastes where cement has increasingly been replaced by densified silica fume (SF), untreated SF or limestone has been studied. The effect of SF on the flow resistance, taken as the area under the flow curve, was found to depend on the dispersing ability of the plasticizer as illustrated by pastes with naphtalene sulphonate-formaldehyde condensate (SNF) and polyether grafted polyacrylate (PA).The gel strengths increased with increasing SF replacement of cement independently of plasticizer type. The cementitious gel strength was, however, depending on the type of SF since pastes with densified SF developed lower gel strengths than pastes with untreated SF. This phenomenon was attributed to agglomerates in the densified SF which remained unbroken by the mixing and measurement sequence.Both flow resistance and gel strength decreased with increasing limestone replacement. Thus, silica fume may have an advantage over limestone filler as stabilizing agent for self-compacting concrete preventing segregation upon standing and reduced form pressure due to a more rapid gel formation.     

树脂增强选择性激光烧结多孔金属件的研究

针对选择性激光烧结(SLS)间接方法成型的金属零件形坯,经脱脂和高温烧结后形成的零件存在大量孔隙和空洞,其致密度和强度都较低,不能满足实际应用要求的问题,采用改性耐高温环氧树脂浸渗零件烧结坯的方法,使多孔金属件致密化,并粘结内部金属网架,提高零件的机械性能.对浸渗烧结坯的拉伸强度的测试和扫描电镜(SEM)以及热失重(TGA)的分析结果表明,浸渗树脂后的烧结坯拉伸强度提高了约4倍;改性环氧树脂和金属网架粘结在一起,形成一个密实的网络结构,致密度大幅提高;零件可在200℃的温度下使用.该方法可以制造注塑模具和功能零件.     

Zonal disintegration phenomenon in enclosing rock mass surrounding deep tunnels -- Elasto-plastic analysis of stress field of enclosing rock mass

The zonal disintegration phenomenon (ZDP) is a typical phenomenon in deep block rock masses. In order to investigate the mechanism of ZDP, an improved non-linear Hock-Brown strength criterion and a bi-linear constitutive model of rock mass were used to analyze the elasto-plastic stress field of the enclosing rock mass around a deep round tunnel. The radius of the plastic region and stress of the enclosing rock mass were obtained by introducing dimensionless parameters of radial distance. The results show that tunneling in deep rock mass causes a maximum stress zone to appear in the vicinity of the boundary of the elastic and the plas-tic zone in the surrounding rock mass. Under the compression of a large tangential force and a small radial force, the rock mass in the maximum stress zone was in an approximate uniaxial loading state, which could lead to a split failure in the rock mass.     

大体积混凝土温升与强度增长的试验研究

针对大体积混凝土结构构件实体强度与普通标准养护试块强度发展规律间的差别等问题,通过研究实际工程尺寸试件温度场的分布和实验室混凝土变温养护试验,以不同养护制度下的试块强度得出了大体积混凝土结构实体强度的发展规律,为工程施工提供了依据,成功地解决了工期与质量的矛盾,取得了较好的技术经济效果.     

声参数的高性能混凝土强度推定模型

为研究高性能混凝土的声波传播特性及实现其强度的快速、准确、无损检测,基于超声波检测方法,应用嫩江、多宝山附近的沙石料,对高性能混凝土对声波的扩散性及其抗压性能与声参量之间的模型关系进行了研究.建立了高性能混凝土抗压强度与声速之间的多种数学模型.通过实测检测数据进行验证,满足精度要求.高性能混凝土的非均质性降低,其抗压强度与声速相关性较好,用超声的方法完全可以实现强度的快速推定.同时,也为将来高性能混凝土地区强度推定曲线的建立奠定了研究基础.     

改性纤维素增强丙烯酰胺水凝胶的合成与拉伸性能研究

采用水媒法制备了低取代度羧甲基纤维素,并用接枝聚合法制备了改性纤维素/丙烯酰胺水凝胶,考察了单体质量比、取代度等对水凝胶拉伸性能的影响.结果表明:对于接枝聚合反应,采用低取代度羧甲基纤维素可以提高纤维素的有效用量;当交联剂用量为180 mg/L、引发剂1 300 mg/L、低取代度羧甲基纤维素和丙烯酰胺质量比在1∶4 ～ 1∶4.5之间、单体质量分数为30%时,合成水凝胶的拉伸强度达到0.28 MPa;在此基础上,适量添加15%的淀粉可使水凝胶拉伸强度达到0.47 MPa;添加1%二氧化钛可使水凝胶拉伸强度达到0.38 MPa.     

高速钢表面PN＋PVD复合处理工艺和性能研究

采用多弧离子镀设备,在高速钢W18Cr4V上先进行等离子氮化,再沉积TiN薄膜,研究了不同渗氮温度和时间对PN＋TiN薄膜组织和性能的影响。结果表明,温度为500℃左右和时间为2h以上条件下对W18Cr4V进行渗氮处理后再沉积TiN薄膜,可以得到最佳的薄膜表面显微硬度（1800～2000HV0.05）和膜／基结合力（50N）,涂层耐磨性也得到明显提高。     

Oxidation and Fracture Strength of High-Purity Reaction-Bonded Silicon Nitride

Reaction-bonded Si₃N₄ (RBSN) made from high-purity Si powder is unusually resistant to degradation caused by exposures to air for up to 50 h at temperatures up to 1400°C. The weight gain during oxidation of this SiH₄-originating RBSN is approximately 10 times less than conventional RBSN. Contrary to normally observed strength degradations, room-temperature strengths of this high-purity, oxidized RBSN (avg = 435 MPa, max. = 668 MPa) remained at their unusually high, as-processed levels after 1000° and 1400°C oxidizing exposures. Fracture toughness values were unaffected by oxidation ( K _IC= 2.3 to 2.4 MPa · m^1/2). This superior oxidation resistance results from the high purity and the small diameter pore channels (0.01 to 0.06 μm) achieved in this SiH₄-originating RBSN.     

Loss of Curing Agent During Thin Film (Droplet) Curing of Thermoset Material

Recently, it has been reported by our group and others^1.2 that loss of curing agent is encountered during the curing of small droplets or thin films of amine cured epoxies. In our earlier study³ results were reported on loss of curing agent in small droplets used in conducting the rnicrobond, single fiber test for determination of interfacial shear strength (ISS). It was reported that use of a volatile curing agent (meta-phenylene diamine (m-PDA) with DGEBA resin) resulted in increasing amounts of curing agent being lost (as measured by T₈ of the cured droplets) with decreasing droplet size during the processing procedure. Droplets smaller than 150 micrometers were seen to lose up to 40% of the curing agent leading to alteration of the mechanical properties of the droplet and, therefore, causing measured values of ISS to be exceedingly low. Use of a less volatile curing agent (Jeffamine 700, a polyether diamine, Texaco Specialty Chemicals) in combination with DGEBA resin produced results which indicated that loss of curing agent was not occuring. This study was undertaken to show the relationships between film (or droplet) size and the amount of curing agent lost (during the processing) for three different aminecured epoxy systems.