紧固件表面锰系磷化膜的制备及摩擦磨损性能

为了提高核主泵紧固件的摩擦磨损性能,采用三种磷化工艺在40Ni Cr Mo7钢表面制备了锰系磷化膜.采用多功能材料表面性能测试仪进行了往复摩擦磨损试验,并研究了在有无润滑条件下,不同工艺对磷化膜摩擦磨损性能的影响.采用扫描电子显微镜和能谱仪表征了磨损前后磷化膜表面的组织形貌和化学成分,并分析了其磨损失效机制.结果表明,通过工艺Ⅱ制备的磷化膜具有最优的摩擦磨损性能.磷化膜特有的孔隙结构具有储油能力,有利于改善其摩擦学性能.随着法向载荷的增加,磷化膜的塑性变形增大,抗剪切强度降低,且摩擦系数呈先缓慢下降后急剧上升的趋势.     

用MPC黏结CFRP布约束混凝土柱轴压试验研究

为了解决传统纤维布(fibre reinforced polymer/plastic,FPR)加固都采用有机胶作为黏结剂,存在容易老化、不耐火等问题,将无机新型黏结材料磷酸镁水泥(MPC)与有机胶(EP)分别黏结碳纤维布(CFRP布)1~3层约束素混凝土柱进行了轴压试验,得出了破坏形态、受压强度模型、应力-应变规律.通过比较研究认为:磷酸镁水泥黏结CFRP约束混凝土柱与有机胶黏结时,受压破坏形态一致,受约束柱强度提高,应力-应变规律一致,且磷酸镁水泥作为黏结剂时,约束构件受压破坏过程中表现了较好的延性.     

AZ91D镁合金表面环保型钙系磷化膜的制备及其耐蚀性

采用化学转化处理的方法,在AZ91D镁合金的表面制备了均匀致密的钙系磷化膜,其中磷化液配方中不含铬、氟及亚硝酸盐等对环境有害的离子。通过场发射扫描电子显微镜和X射线衍射仪研究了磷化时间及温度对磷化膜结构和相组成的影响。结果表明:磷化时间为20min,磷化温度为40℃时,所得到的磷化膜的致密性和均匀性较好。与空白基体相比,经磷化处理后的镁合金在3.5%NaCl溶液中的耐腐蚀性能明显提高。     

高电压磷酸钴锂正极材料性能调控研究

高性能、高安全储能电池的迫切需求加速了橄榄石型高电压正极材料的研究步伐。为了改善高电压磷酸钴锂(LiCoPO₄)的综合电化学性能,采用溶剂热法研究了溶剂比、过渡元素(Fe、Mn)单掺杂和双掺杂(掺杂元素总量占10%)对正极材料形貌、尺寸、反位缺陷和电化学性能的影响。结果表明,当溶剂比为2.3时,未掺杂LiCoPO₄在0.1C下表现出163.1 mAh·g^-1的最高理论比容量;双掺杂LiCo_0.9Mn_0.05Fe_0.05PO₄正极材料具有突出的循环性能,在0.5C电流密度下,循环100圈后的容量保持率为78.9%,循环稳定性得到明显改善。     

Effect of ZrO<Subscript>2</Subscript> coating on<Emphasis Type="Italic">in vitro</Emphasis> formation of calcium phosphate

We prepared zirconia thin films on (100) Si wafer by using a chemical solution deposition with a zirconium naphthenate as a starting material. The films were pyrolyzed at 500°C for 10 min and finally annealed for 30 min in air at 500°C. Amorphous films after annealing had no distinct structure and were uniform along the cross section line.In vitro formation of the calcium phosphate was evaluated by the field emission-scanning electron microscope, energy dispersive X-ray spectrometer and Fourier transform infrared spectroscopy.     

ET-98无机磷酸盐富锌涂料的性能与应用

论述了国内首创的ET-98无机磷酸盐富锌涂料，该涂料克服了无机磷酸富锌涂料、无机富锌涂料喷砂、抛丸的缺点，简易可行，除锈、除油后即可涂刷，并能达到较好的防腐效果。     

Design of Bulk metallic glasses with high glass forming ability and enhancement of plasticity in metallic glass matrix composites: A review

To overcome some of the limits of existing metallic alloys, a new alloy design concept has been introduced recently in order to control the crystallinity, i.e. to utilize crystalline, quasicrystalline, and amorphous structures. In particular, bulk metallic glasses (BMGs) receive great attention because of their unique properties due to their different atomic configuration. Recently, significant progress in enhancing glass forming ability (GFA) has led to the fabrication of BMGs having potential for application as structural and functional materials. Moreover, successful design of BMG matrix composite microstructure suggests that the plasticity of BMGs can be controlled properly. In this review article, we introduce recent research results on the design of BMGs with high GFA and on the enhancement of plasticity in metallic glass matrix composites.     

Er-doped SiO2–Al2O3 thin films prepared by the sol–gel route

The synthesis of homogeneous and pure silica–alumina binary glasses doped with rare-earth (RE) ions such as Er³⁺ is currently a key challenge for the development of integrated optics devices such as lasers, optical amplifiers or waveguides. In this study Er³⁺-doped SiO₂–Al₂O₃ films were prepared by the sol–gel route. Aluminium sec-butoxide, Al(O-sec-C₄H₉)₃ (ASB), and tetraethoxysilane, Si(OC₂H₅)₄ (TEOS), were used as glass oxide precursors, whereas erbium was introduced as Er(NO₃)₃. The alumina content in the silica matrix was 10 at.%, while erbium doping ranged between 200 and 5000 ppm. The preparation of the starting sol–gel solution and the layer deposition by a dip-coating procedure were performed in dry-box under nitrogen atmosphere. The obtained films were subsequently annealed in air between 300 and 1000 °C. After treatment at 500 °C, layers 200 nm thick were obtained. The composition, microstructure and surface morphology of the films were investigated by X-ray photoelectron spectroscopy (XPS), secondary-ion mass spectrometry (SIMS), glancing incidence X-ray diffraction (GIXRD) and atomic force microscopy (AFM). Crack-free, transparent, high purity films were obtained, characterised by compositional and microstructural homogeneity.     

磷酸盐无机树脂铸造粘结自硬砂的性能研究

以磷酸盐无机树脂为粘结剂，对自硬砂的混砂工艺，粘结剂加入量，固化荆加入量，铸型脱模时间．型砂可使用时间，渍散性等进行了研究。结果表明磷酸盐粘结剂有良好的综合工艺性能，具有应用价值。     

Preparation and elements analysis of porous fluorescent glasses

A large variety of porous fluorescent glasses were prepared and the concentration of different elements in these glasses was analyzed. The start porous glasses were soaked in a solution containing soluble salts and then heated at 650 ℃ for 3 h to decompose the salts in the pores into oxides. Fluorescent agents, such as UO3, Eu203, were impregnated into the porous glasses to prepare the fluorescent glasses. The results show that soaking is a feasible method to prepare the glass sphere with compositions distinguishable from each other and easy to be located in a complicated background. Six or more components can be impregnated together into one glass sample and the concentration of them can be analyzed accurately. UO3 and Eu203 can be impregnated into porous glass to make the glass strongly fluorescent. Higher concentration of Eu203 produces stronger fluorescence while higher concentration of UO3 reduces the fluorescence intensity because of the concentration quenching effect.