微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。     

滑坡相似材料试验结果优化分析研究

在运用模糊综合评判确定的滑坡相似材料试验配合比隶属度基础上，利用方差分析确定各因素的数学优化区间，结合变量有上下界的改进单纯形法，获得技术，经济上的最佳配合比，克服了统计优化理论不能在连续区间寻优的缺点，这对从事滑坡相似材料试验研究具有一定的实际意义。     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。     

CNTs/Polyester复合材料的微波吸收特性研究

研究了添加不同质量分数CNTs的聚酯基复合材料的电磁波吸收性能,初步分析了CNTs的螺旋结构和手征性质导致8～40GHz波段良好的吸收。其中厚度为1.40mm±0.05mm的CNTs/Polyester复合材料在25GHz有较强的吸收峰。     

Modeling of Material Deformation Kinetics in the Prefracture Zone

Based on the concept of complete stress–strain diagrams, we propose a new model describing the law of stress distribution in the prefracture zone in plastic materials in view of the type of the stressed state.     

Synthesis and luminescence of Sr2CeO4 fine particles

Fine particles of a blue emission phosphor Sr₂CeO₄ have been synthesized using a chemical co-precipitation technique, and the textual and luminescent properties were compared with the one synthesized by the conventional solid-state reaction method. Particle size and distribution of the Sr₂CeO₄ fine powder prepared by the co-precipitation process were smaller and narrower than those obtained by the samples prepared from the conventional one. The emission intensity of the fine particles was equal to that of the larger particles prepared from the solid-state reaction, on the contrary to the general tendency that emission intensity decrease with particle size reduction. Although no Ce³⁺ peaks were observed in EPR measurements, X-ray photoelectron spectra of the samples clearly elucidated the existence of Ce³⁺ only on the surface of Sr₂CeO₄.     

Failure analysis of a broken tooth

Several days after heart surgery, a patient discovered his upper right canine tooth had broken at the root. Such tooth damage, recognized post-operatively, is usually assumed to be caused by blunt mechanical force from an instrument used by the anesthesiologist during placement of a breathing tube at the start of surgery. In this case, the patient had saved the crown portion of the broken tooth, and it was possible to examine the root fracture characteristics. The curvature and direction of the crack path and natural tooth situation suggested that failure could be described through a cantilever beam model. This was confirmed when a whole extracted sample tooth was embedded and broken by a measured force in a manner consistent with the model. The resulting fracture surface matched that of the patient’s broken canine tooth. However, the high load and force direction necessary to fracture the root was inconsistent with forces applied during the anesthesia procedure. The failure analysis and further investigation indicated tooth clenching on the breathing tube during recovery was the likely cause of fracture. This paper presents an alternate explanation for intubation-related dental injury, demonstrates the practicality of fractographic analysis of biological materials, and introduces a methodology for simulating in vitro tooth settings for mechanical testing.     

The magnetic structure of TbNiSiD1.78

TbNiSiD_1.78 has been studied by powder neutron diffraction below 100 K. The compound takes the hexagonal room temperature structure at 100 and 50 K (P6₃/mmc). At 2 K, below the antiferromagnetic ordering temperature of 10 K, there is a small orthorhombic distortion of the lattice. The refined unit-cell dimensions at 2 K (space group Pnma) are a=7.9505(2), b=4.02502(14), c=6.9823(2) Å. The magnetic moments of Tb are 8.71(6) μ_B, and are ordered antiferromagnetically along a.     

欧洲轿车新战略决策——电压、阻燃材料与工作温度一并提高——兼论Synolite5001-T-1牌聚酯树脂的阻燃防火性能优于酚醛树脂

本文介绍了欧洲轿车新战略决策，也即：将要提高轿车的电池电压，，阻燃材料的比率和工作温度；Synolite5001-T-1牌聚酯树脂的阻燃防炎性能优于酚醛树脂。     

用于高频谐振器的PbTiO_3基压电陶瓷

传统的PZT压电陶瓷的相对介电常数较大,一般为1 000以上,用于高频谐振器不易与线路匹配;而PbTiO3基压电陶瓷的相对介电常数较小,一般仅为200左右,对于10 MHz以上频率的谐振器,用PbTiO3基压电陶瓷作为压电振子是最佳的选择。本文主要研究用于高频谐振器的MnO2和Nd2O3改性PbTiO3基压电陶瓷的性质。PbTiO3基压电陶瓷的性质的改善是与此种陶瓷的制备工艺,显微结构和电导机制紧密相关的。