Platinum nanoparticles decorated on graphitic carbon nitride-ZIF-67 composite support: An electrocatalyst for the oxidation of butanol in fuel cell applications

In the present study, we report an eco-friendly and simple route to design and synthesize novel nanocomposite catalyst based on platinum nanoparticles anchored on binary support of graphitic carbon nitride (g-C₃N₄) and cobalt-metal-organic framework (ZIF-67). For this purpose, ZIF-67 was prepared by precipitation method and g-C₃N₄ was prepared through thermal polymerization method. Later, ZIF-67 and g-C₃N₄ were hybridized through sonication to get homogeneous g–C₃N₄–ZIF-67 nanocomposite support material. Platinum nanoparticles (PtNPs) were uniformly deposited on g–C₃N₄–ZIF-67 by an electrochemical method. The as-developed nanocatalyst was characterized by morphological, structural and electrochemical techniques. The electrocatalytic activity of PtNPs@g–C₃N₄–ZIF-67 nanocatalyst towards butanol oxidation was evaluated via CV, CA, LSV and EIS in an alkaline medium. Results revealed that the proposed catalyst showed greatly enhanced electrooxidation of butanol in terms of high magnificent current density, lower oxidation potential, excellent long-term stability, large surface area, low charge transfer resistance and less toxic ability. Enhanced catalytic performance of the proposed catalyst could be ascribed to the synergistic effect of g–C₃N₄–ZIF-67 nanocomposite and PtNPs. The PtNPs@g–C₃N₄–ZIF-67 catalyst holds promising potential applications to be used as an anodic electrocatalyst for the development of high-performance alkaline fuel cells.     

Structural,magnetic, thermal and optical properties of Sn2+ cation doped magnetite nanoparticles

Tin doped nanomagnetites, Sn_xFe_3-xO₄, were synthesized with various concentrations of Sn²⁺ ion (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) by co-precipitation method. XRD, VSM, TG-DTA, SEM-EDX and UV–Vis were used to characterize and study the structural, magnetic, thermal, and optical properties of Sn_xFe_3-xO₄ nanoparticles. XRD confirmed the presence of cubic structure and spinel phase of tin doped magnetites. The d-spacing, lattice parameter, density, crystallite size and cation distribution were derived from the XRD analysis. The M − H curves exhibited changes in saturation magnetization (M_s), coercive field (H_c), remanent magnetization (M_r) and susceptibility (χ), with increasing concentration of non-magnetic Sn²⁺ ions. Differential thermal analysis was used to study the thermal stability of Sn_xFe_3-xO₄ nanoparticles. The SEM images revealed the surface morphology of the nanoparticles and the EDX spectra showed an increase in the Sn content and a corresponding decrease in the Fe content for the tin doped samples. The optical bandgap was found to be centered at 3.9 eV for the synthesized materials. This systematic study may be the first comprehensive report on synthesis and characterization of tin doped magnetites.     

Mutagenic Effects of Iron Oxide Nanoparticles on Biological Cells

In recent years, there has been an increased interest in the design and use of iron oxide materials with nanoscale dimensions for magnetic, catalytic, biomedical, and electronic applications. The increased manufacture and use of iron oxide nanoparticles (IONPs) in consumer products as well as industrial processes is expected to lead to the unintentional release of IONPs into the environment. The impact of IONPs on the environment and on biological species is not well understood but remains a concern due to the increased chemical reactivity of nanoparticles relative to their bulk counterparts. This review article describes the impact of IONPs on cellular genetic components. The mutagenic impact of IONPs may damage an organism’s ability to develop or reproduce. To date, there has been experimental evidence of IONPs having mutagenic interactions on human cell lines including lymphoblastoids, fibroblasts, microvascular endothelial cells, bone marrow cells, lung epithelial cells, alveolar type II like epithelial cells, bronchial fibroblasts, skin epithelial cells, hepatocytes, cerebral endothelial cells, fibrosarcoma cells, breast carcinoma cells, lung carcinoma cells, and cervix carcinoma cells. Other cell lines including the Chinese hamster ovary cells, mouse fibroblast cells, murine fibroblast cells, Mytilus galloprovincialis sperm cells, mice lung cells, murine alveolar macrophages, mice hepatic and renal tissue cells, and vero cells have also shown mutagenic effects upon exposure to IONPs. We further show the influence of IONPs on microorganisms in the presence and absence of dissolved organic carbon. The results shed light on the transformations IONPs undergo in the environment and the nature of the potential mutagenic impact on biological cells.     

Cellulose nanoparticles synthesised from potato peel for the development of active packaging film for enhancement of shelf life of raw prawns (Penaeus monodon) during frozen storage

In this study, the cellulose nanoparticles (CNP) isolated from potato peel were used for reinforcement of polyvinyl alcohol (PVA)-based active packaging film. The above film was used to pack the raw prawns (Penaeus monodon) at −20 °C, and the colour change, protein content, TVB-N, TMA and microbial analysis were done at regular interval for prawns stored in CNP-PVA active packaging film. A significant difference was observed in the quality of prawns stored in potato CNP-PVA film compared with prawns packed and stored in polyethylene film. The newly designed active packaging with CNP and fennel seed oil enhanced the shelf life of prawns up to two months for both HOSO (head on shell on) prawn and PD (peeled and deveined) prawn. Hence, the study recommends the potato peel CNP-PVA film with fennel seed oil as better choice to extend the shelf life of the prawns during storage compared with polyethylene packaging.     

Computational studies on the radiative and nonradiative processes of luminescent N-heteroleptic platinum(II) complexes

Three N-heteroleptic Pt(II) complexes, [Pt(C^C)(O^O)] [O^O = acetylacetonate, C^C = 1-phenyl-1,2,4-triazol-5-ylidene (1), C^C = 4-phenyl-1,2,4-triazol-5-ylidene (2), C^C = 2-phenylpyrazine (3)] have been investigated with density functional theory (DFT) and time-dependent density functional theory (TDDFT). The radiative decay rate constants of complexes 1–3 have been discussed with the oscillator strength (f_n), the strength of spin–orbit coupling (SOC) interaction between the lowest energy triplet excited state (T₁) and singlet excited states (S_n), and the energy gaps between E(T₁) and E(S_n). To illustrate the nonradiative decay processes, the transition states between triplet metal-centered (³MC) and T₁ states have been optimized and were verified with the calculations of vibrational frequencies and intrinsic reaction coordinate (IRC). In addition, the minimum energy crossing points (MECPs) between ³MC and ground states (S₀) were optimized. At last, the potential energy curves relevant to the nonradiative decay pathways are simulated. The results show that complex 3 has the biggest photoluminescence quantum yield because the complex 3 has the biggest radiative decay rate constant and the smallest nonradiative decay rate constant in complexes 1–3.     

Catalytic supercritical water oxidation of tri-n-butyl phosphate: Process optimization by response surface methodology and cytotoxicity assessment

Catalytic supercritical water oxidation (SCWO) of an organophosphate flame retardant, namely tri-n-butyl phosphate (TNBP) was studied. Firstly, copper oxide nanoparticles (NPs) were synthesized in SCW and their properties were characterized by various analyses. Afterwards, their catalytic performance was investigated under different conditions including reaction temperature (400–500 °C), TNBP volume percentage in the feed (1–4%), oxidant ratio (0–2) and reaction time (50–150 min) based on response surface methodology (RSM). The synthesized CuO NPs had an average particle size of 30 nm with a narrow distribution. According to RSM analysis, the reaction temperature and time are the most significant factors; whereas, the impact of the other factors, especially TNBP volume percentage in the feed, was found to be negligible. Overall, excellent performance was achieved under optimal conditions found by the RSM, which was reaction temperature of 500 °C, TNBP volume percentage of 4%, oxidant ratio of 1.5, and reaction time of 90 min. The TOC removal efficiency as an indicator of TNBP degradation was about 99%. Finally, in vitro cell viability assays for the cytotoxicity evaluation of fresh and SCW-treated solution were applied. The results of MTT showed that SCWO converts TNBP into by-product that did not induce any cytotoxicity.     

Influence of the dispersion of Nanoclays on the cellular structure of foams based on polystyrene

In the present work blends of polystyrene (PS) with sepiolites have been produced using a melt extrusion process. The dispersion degree of the sepiolites in the PS has been analyzed by dynamic shear rheology and X-ray micro-computed tomography. Sepiolites treated with quaternary ammonium salts (O-QASEP) are better dispersed in the PS matrix than natural sepiolites (N-SEP) or sepiolites organo-modified with silane groups (O-SGSEP). A percolated network is obtained when using 6.0 wt% of O-QASEP, 8.0 wt% of N-SEP and 10.0 wt% of O-SGSEP. It has been shown that multiple extrusion processes have a negative effect on the polymer architecture. They produce a reduction in the length of the polymeric chains, and they do not lead to a better dispersion of the particles in the polymer matrix. Foams have been produced using a gas dissolution foaming process, where a strong effect of the dispersion degree on the cellular structure of the different foams was found. The effects on the cellular structure obtained by using different types of sepiolites, different contents of sepiolites and different extrusion conditions have been analyzed. The foams produced with the formulations containing O-QASEP present the lowest cell size and the most homogeneous cellular structures.