高层建筑抗震设计中短柱问题的分析与处理

指出在诸如图书馆的车库、层高较低的储藏室、高层建筑的地下车库等处,由于使用荷载大,层高又较低,在设计中就不可避免地会出现短柱。而短柱的延性很差,尤其是超短柱几乎没有延性,在建筑遭受本地区设防烈度或高于本地区设防烈度的地震影响,很容易发生剪切破坏而造成结构破坏甚至倒塌。笔者在文中详细讨论了建筑中短柱的判别方法,及改善短柱抗震性能的几种措施。     

微波作用下铝酸钙炉渣非等温浸出动力学

研究了微波作用下铝酸钙炉渣非等温浸出动力学，考察了不同微波辐射功率对炉渣中氧化铝浸出率的影响以及相应微波功率下反应体系温度随时间的变化规律。结果表明：该浸出动力学过程的控制步骤为界面化学反应控制，表观反应活化能为40kJ／mol左右；微波作用可改变反应的频率因子，对反应活化能影响不明显；随着微波辐射功率的增大，频率因子增加，宏观表现出微波功率的增加对反应有促进作用。     

Effect of surface free energy of ceramic glaze on oil droplet shape and its behavior in water

A super-hydrophilic functional ceramic was prepared by adjusting the chemical components of ceramic glaze. Effect of surface flee energy of ceramic glaze on oil droplet shape and its behavior in water were studied. The results show that water can spread on ceramic surface with high surface free energy, and oil droplet can aggregate rapidly and separate from the ceramic surface in water. For the ceramic with lower surface free energy, the polar shares are dependant on its easy-cleaning property. The higher the polar shares, the better the easy-cleaning property, and the easier the droplet separates from the ceramic surface in water.     

Flow behavior and microstructure evolution of TB8 alloy during hot deformation process

Hot compression tests of metastable β titanium alloy TB8 were carled out using a Gleeble-1500 thermal simulation testing machine in the temperature range of 750-1 100 ℃, at constant strain rate from 0.01 s^-1 to l S^-1 and with height direction reduction of 60%. Flow stress behavior and microstructure evolution during hot compression of TB8 alloy were investigated. The hyperbolic-sine-type constitutive model of TB8 alloy was obtained to provide basic data for determining reasonable forming process. The results indicate that hot deformation behavior of TB8 alloy is highly sensitive to the temperature and strain rate. An analysis of the flow stress dependence on strain rate and temperature gives a stress exponent of n=3.416 19 and a deformation activation energy of Ω=227.074 4 kJ/mol. According to the deformation microstructure, no dynamic recrystallization happens below r-phase transus temperature and as a result dynamic recovery is the predominant softening mechanism. On the other hand, the main softening mechanism is characterized as dynamic recrystallization at a slow strain rate above r-phase transus temperature.     

双丝MAG焊工艺

双丝MAG焊接具有良好的发展前景，正广泛应用于各项工程领域之中，从其焊接设备的要求、保护气体以及其熔滴过渡控制、焊接过程等几个方面，详细介绍双丝MAG焊的工艺及其特点。     

Ag—Ln（Ln=La,Ce,Gd）液态合金短程有序性的热力学讨论

本文利用理想缔合液液模型，计算了１３００－１６００Ｋ温度范围内，Ａｇ－Ｌｎ（Ｌｎ＝Ｌａ，Ｃｅ，Ｇｄ）三个二元系的热力学数据；认为在液相中存在着Ａｇ３Ｌｎ和ＡｇＬｎ得缔合物，并利用浓度相互作用函数Ｓｃｃ（Ｏ）对这种短程有序性进行了讨论。     

硅酸铝/铝硅合金梯度复合材料的研究

采用挤压铸造技术制备硅酸铝短纤维增强铝硅合金梯度复合材料，研究了这类材料的凝固组织和基本热物理性能。结果表明，在复合材料中，基体组织细小，纤维与基体结合良好，并呈梯度状无序分布；梯度复合材料的热物理性能优异。     

CuxAlO2(0.92≤x≤1.0)陶瓷电输运性能

使用高温固相烧结法制备不同化学剂量比的CuAlO2陶瓷,研究CuxAlO2(0.92≤x≤1.0)中Cu、Al摩尔比的相对变化对其结构和导电性能的影响.结果表明:CuxAlO2(0.92≤x≤1.0)陶瓷片的结构和密度随着x值的增大,样品的结晶性逐渐变好,密度也逐渐增大,在x为0.98时,得到密度最大(5.02 g/cm3)且结晶良好的纯相CuAlO2;样品的光学带隙均约为3.44 eV;随着x值的增加,室温电导率先增大然后减小,在x为0.98时得到最大电导率为8.03×10-3 S/cm;电导率随温度的升高而显著增大,且曲线在100～300 K之间很好地符合Arrhenius关系,x为0.98时激活能最低,仅为0.085 eV;在所研究的成分范围内,CuAlO2陶瓷的导电能力主要取决于陶瓷片的致密度.     

40Cr钢的快速循环球化退火的研究

通过对40Cr钢的球化退火试验研究。推荐了一种适用于该材料的最佳快速循环球化退火工艺,不仅节能效果明显,而且工艺操作简单,质量稳定。     

短路过渡GMAW系统中参数变化的预测分析

在建立了短路过渡GMAW系统动态模型的基础上，研究了与GMAW短路过渡过程有重要关系的动态参数，特别涉及到一些无法通过试验获取的参数的动态变化，并进一步讨论了有关参数间的内在联系。焊丝熔化速度与焊接电流变化规律一致，但在燃弧和短路的交替瞬间发生跳变；焊丝熔化速度直接影响到焊丝干伸长的变化和短路液桥高度的变化；短路期液桥的体积同时受到焊丝熔化和液桥金属向熔池过渡的影响。