Al2O3对镁铬耐火材料致密化的影响

为了提高镁铬耐火材料的烧结性能,通过考察气孔率、体积密度和常温耐压强度与Al2O3加入量之间的关系,讨论了Al2O3添加剂对两种不同镁铬耐火材料致密化的影响.结果表明,镁铬耐火材料的骨料不同,Al2O3对其烧结性能和致密化的影响也不一样.     

烧结处理小矿山精矿的应用研究

研究小矿山精矿的性质，分析小矿山精矿对烧结过程的影响，提出了增加小矿山精矿配入量的途径及方法．     

W-35%Cu液相活化烧结工艺研究

本文从钨铜两相迁移机制和固溶扩散的角度 ,实验研究了钨铜复合粉的活化和常规烧结 ,分析了钨铜复合粉液相活化烧结过程中球磨时间、烧结温度、保温时间和升温速度对材料致密度的影响。结果表明 ,短时间球磨的钨铜复合粉具有良好的烧结性能 ,烧结温度和保温时间对材料致密度影响很大 ,活化烧结能有效降低烧结温度 ,提高烧结致密度     

降低烧结返矿率的途径与实践

通过对影响烧结返矿率的因素进行分析，从优化配料、强化制粒和造球、提高料层厚度、实现低碳低水均质烧结等几个方面着手，使烧结返矿率从1998年的23．6％降到了2003年的16．9％。     

Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.     

烧成及热处理工艺对钛酸锶铅基热敏材料性能及显微结构的影响

研究了烧成及热处理工艺对钛酸锶铅基热敏材料的阻温特性及显微结构的影响。通过扫描电镜（ＳＥＭ）和能量分散仪（ＥＤＡＸ）分析了材料的显微结构及不同形貌晶粒的成份。通过对组成、烧成及热处理工艺的控制，可得到具有Ｖ型ＰＴＣＲ特性的热敏材料。     

以YAG为添加剂的气压烧结氮化硅

本文以添加ＹＡＧ的反应烧结氮化硅（ＲＢＳＮ）为前驱体，采用气氛加压烧结的工艺，在０．５～９．０ＭＰａ氮气压力范围，研究了不同氮压对烧结体的密度、相组成、强度和显微结构的影响及其相互间的关系。研究表明，通过改变氮气压力能有效地调控材料的显微结构，材料的性能又受控于显微结构的变化。     

Reactivity of steam in exhaust gas catalysis III. Steam and oxygen/steam conversions of propane on a Pd/Al2O3 catalyst

A 1% Pd catalyst (38% dispersion) was prepared by impregnating a γ-alumina with palladium acetylacetonate dissolved in acetone. The behaviour of this catalyst in oxidation and steam reforming (SR) of propane was investigated. Temperature-programmed reactions of C₃H₈ with O₂ or with O₂ + H₂O were carried out with different stoichiometric ratios S(S =[O₂]/5[C₃H₈]). The conversion profiles of C₃H₈ for the reaction carried out in substoichiometry of O₂ (S < 1) showed two discrete domains of conversion: oxidation at temperatures below 350°C and SR at temperatures above 350°C. The presence of steam in the inlet gases is not necessary for SR to occur: there is sufficient water produced in the oxidation to form H₂ and carbon oxides by this reaction. Contrary to what was observed with Pt, an apparent deactivation between 310 and 385°C could be observed with Pd in oxidation. This is due to a reduction of PdO_x into Pd⁰, which is much less active than the oxide in propane oxidation. Steam added to the reactants inhibits oxidation while it prevents the reduction of PdO_x into Pd⁰. Compared to Pt and to Rh, Pd has a higher thermal resistance: no deactivation occurred after treatment up to 700°C and limited deactivation after treatment up to 900°C, provided that the catalyst is maintained in an oxygen-rich atmosphere during the cooling.     

BaTiO_3系PTCR热敏电阻器用烧结助剂的研究

研究了烧结助剂的作用，实验结果表明：如只引入半导化元素，不引入烧结助剂，则室温电阻率ρ２５很大，甚至是绝缘体。由于烧结助剂的加入，既改善了ＰＴＣＲ热敏电阻陶瓷的烧结性，又改善了其ρ２５、耐电压Ｖｂ、ＰＴＣ效应等特性，从而使产品的各种特性易于重复。烧结助剂昔日多用ＡＳＴ，现在常用ＳｉＯ２，其加入量ｘ宜小于２％。ＳｉＯ２的纯度、杂质等化学特性，与粒子形状、粒度分布、晶系等物理特性，对ＰＴＣＲ热敏电阻器的电性能有很大的影响。据此提出了ＢａＴｉＯ３系ＰＴＣＲ热敏电阻器用ＳｉＯ２的技术标准。     

抗高温磨损高铬铸铁的研究

经Mo、B、V、Ti合金化和RE变质处理的高铬铸铁，具有优良的抗高温磨损性能和强韧性，用于制造筛分高温烧结矿的振动筛筛板，使用寿命比ZG30Cr18Mn12Si2N耐热钢筛板提高2倍以上。多元高铬铸铁筛板制造工艺简单，成本低，值得在筛分领域推广使用。