颗粒尺寸对反应烧结碳化硅摩擦磨损特性的影响

研究了碳化硅颗粒尺寸对反应烧结碳化硅材料摩擦磨损性能的影响.结果表明:随着碳化硅颗粒尺寸的增加,不论干摩擦还是水润滑条件下,反应烧结碳化硅的摩擦系数和磨损率均表现为先增加,后降低的趋势.粒度为42μm的反应烧结碳化硅的摩擦系数和磨损率最大,而粒度为14μm的最小.水润滑时的摩擦系数和磨损率比干摩擦时的成倍降低.     

Tribological Properties of the Semi-metallic Friction Material with Nano-SiC

The tribological properties of the semi-metallic friction materials with nano-SiC were studied by the contrast experiments. The experimental result indicates that when the nano-SiC powder substitutes the generalSiC powder, the friction coefficient is not obviously improved. On the contrary, the wear rate increases a little.The friction surfaces and the mixed powder were examined by a scanning electron microscope and the experimental data were analysed. The main reason, which leads to the high wear, is found.     

微摩擦测试仪的研制

微机械构件表面的微摩擦不同于宏观摩擦．也不同于原子力／摩擦力显微镜探针与基片之间的微摩擦。因此。宏观或微观摩擦实验仪器对于微摩擦的研究有很大的局限．本文从实际出发．设计并研制了考虑微机械工况的销盘式微摩擦测试仪及其数据处理系统，采用微应变片获取摩擦力及载荷导致的变形信号，通过A／D卡采集数据．在数据处理系统中进行数据处理．从而获得微摩擦力和微载荷的数值．为微摩擦特性测试和分析提供一种手段。     

Compomer的摩擦磨损特性

采用Compoglass，F2000，Elan，Dyract AP4种牙科用复合体材料(Compomer)，对其玻璃颗粒含量和表面硬度进行了测量，并在球一盘往复摩擦磨损试验机上考察了它们的摩擦磨损特性。结果表明：F2000的摩擦系数最高，Elan的摩擦系数次之，Compoglass和DyractAP的摩擦系数分别为第三和第四．摩擦系数随玻璃颗粒含量的增加而增加．在同样试验条件下，低摩擦系数的DyractAP和Compoglass与高摩擦系数的F2000和Elan相比具有较好的耐磨性．磨损机理主要表现为由玻璃颗粒脆性断裂引起的玻璃颗粒脱落和磨粒磨损。     

铁镍稀土自熔性合金粉末研究与应用

研究应用成本较低的铁镍稀土自熔性合金粉末材料代替镍基自熔性合金粉末材料。通过对铁镍稀土自熔性合金粉末材料显微组织分析、摩擦性能和结合强度试验以及实际应用等工作，表明铁镍稀土自熔性合金粉末材料具有熔焊性能好、结合强度高、综合性能优良、成本低等特点。     

Triboluminescence of A New Europate Complex

A new europium (Ⅲ)complex Eu(HFNH)3Phen (HFNH: 4, 4, 5, 5, 6, 6, 6-heptafluoro-l-(2-naphthyl)hexane-1,3-dione ; phen : 1, 10-phenanthroline) was synthesized and its tribolumineseent phenomenon was observed. Photoluminescence and tfiboluminescence spectra were successfidly determined. The most intense tfiboluminescent emission originates from the transition of the central Eu^3 ion from ^5D0 level to ^7F2 level. The tribolunlinescent spectrum is basically similar to that of photoluminescence, which correlates with the disorders of F atoms.     

榫联接接触表面间的微动摩擦系数研究

利用解弹性接触问题的边界元法分析了榫联接的微动摩擦的接触状况，及其接触表面间的微动相对位移幅，正压力和摩擦力的大小和它们在接触表面上的分布。为联接的微动疲劳设计的计算提供了数据。     

径向柱塞泵中滑靴摩擦副的设计分析

该文介绍了静压支承工作原理，并利用静压支承原理对新型径向柱塞泵的滑靴结构进行了设计。分析了滑靴摩擦副的油膜刚度、漏损及影响油膜厚度的因素。     

库仑摩擦阻尼新型复合隔振器的摩擦副特性分析

本文针对模型平台系统的结构和受力情况,应用当量粘性阻尼理论,对基于摩擦耗能机理的导弹惯性平台隔振器中的一种具有振幅反馈机制的库仑摩擦阻尼隔振器进行了理论建模.推导了隔振传递率的一般公式,研究了系统共振传递率与摩擦副材料(即摩擦系数)之间的关系,给出了模拟值与试验值,验证了理论与试验的一致性.     

MoS_2对铝基材料摩擦磨损性能的影响

以Al,Fe,Zn等金属粉末和Si粉为原料,采用热压法制备MoS_2含量(质量分数)分别为0和3%的铝基复合材料,在滑动速度为0.377~1.131 m/s以及载荷为4~10 N的条件下进行摩擦试验,研究MoS_2对铝基复合材料摩擦磨损性能的影响。结果表明:在0.377 m/s的滑动速度下,3%MoS_2/铝基复合材料在10 N载荷下具有较低的平均摩擦因数0.4,比不含MoS_2材料的摩擦因数降低近一半;在0.755 m/s的滑动速度下,2种材料的摩擦因数和磨损率接近;在1.131 m/s的滑动速度下,载荷7~10 N时2种材料都严重磨损,3%MoS_2/铝基材料具有相对较低的磨损率,磨损机理为熔化磨损,未添加MoS_2材料的磨损机理为严重塑性变形磨损。添加3%MoS_2可显著改善铝基材料的摩擦磨损性能。