用高Nb的Ti-Al-Nb基合金作填充金属钨极氩弧焊TD3合金,探讨了焊后时效处理和焊后固溶 时效处理状态下母材及其接头显微结构和力学性能特点.结果表明:接头进行焊后固溶 时效处理相对较合理,热影响区、焊缝区分别为其室温、高温力学性能的薄弱区域;与焊后时效处理相比,焊后固溶 时效处理状态下母材力学性能较低,这主要归因于热处理过程中片状相粗化.     

再生SiC制造的新型耐火材料

评估了陶瓷工业用后的、硅酸盐结合SiC板重复使用于陶瓷工业和钢工业的情况。准备了几批含不同量矾土和硅灰的、使用过的SiC质板作试验料，加热到1400℃。通过检测体积密度和显气孔率来测试料的致密性。研究了这些烧结材料的矿物性能和显微结构，这些性能与30次热震实验后耐压强度同热震实验前的耐压强度比值有关。莫来石的形成、莫来石代替碳化硅和假碳化硅的生成、碳化硅的紧密结构和良好分布等都被记录。随着不断增加的莫来石含量直至40％，热震实验后强度同实验前强度相比有所增大。将料加热到950℃再用水冷处理，如此循环30次后观测发现，所有批次的料抗热震性能良好，没有剥落出现。     

氧化铝瓷的密度、磨耗与生产工艺

本文阐述了氧化铝瓷的密度、磨耗与生产工艺的关系，结合其显微结构分析了浆料、造粒粉料对产品质量的影响。     

Effect of Microstructure on Impact Wear Resistance Impact Fatigue Resistance and of Medium Cr-Si Cast Iron

A great amount of iron grinding balls in tube mills have been consumed. Under this impact abrasive wear working condition, the failure of wear resistant alloying white irons grinding balls is mainly caused by fatigue spalling. The impact wear resistance of martensitic high chromium cast iron （Cr of 15%） is not high sometimes, but its cost is not low. Thus, medium Cr-Si wear resistant cast iron is recommended. The influence of the iron on impact fatigue resistance and impact wear resistance is pronounced. Ball-on-ball impact fatigue test and high stress impact wear test of the grinding balls have been carried out. The results show that the impact fatigue resistance （IFR） and impact wear resistance （IWR） of medium Cr-Si cast iron are superior to those of martensitic high chromium cast iron （Cr of 15%）. The main reasons are that （1） the stress in medium Cr-Si cast iron is released in the as-cast state; （2） the matrix is fine pearlite with better toughness and plasticity; （3） the pearlite is more stable compared with a retained austenite under repeated impact load and less phase transformation can take place; （4） high silicon content im- proves the morphology of eutectic carbide; （5） there is no seeondary carbide which results in less crack sources. All these factors are beneficial to improvement of impact fatigue spalling resistance. The eutectic carbide M7C3 is the main constituent to resist wear.     

Corrosion Resistance of High-Alumina Graphite Based Refractories to the Smelting Reduction Melts

1 Introduction The corrosion resistance of the refractories is one of the imperative problems for the development of smel- ting reduction with iron bath[1 ~4]. The Al2O3-C based refractories have been widely and successfully used in the metallurgy industr…     

高红外发射率建筑陶瓷玻化砖的研制

通过分别在坯体中引入含镁原料和铜尾砂废料,制备了一种在常温下、8～141μm远红外波段具有较高发射率(e=0.867)的建筑陶瓷玻化砖.该材料集功能与环保为一体,将其运用到室内装饰中能起到一定的医疗保健功效.实验结果表明:显微结构物相中莫来石量的增加及其晶格的畸变、Fe2O3的存在、堇青石的形成有利于发射率的提高.     

烟草种子亚显微结构及分类学意义

应用环境扫描电镜(ESEM)研究了73种烟草种子的形态和种皮表面结构特征。结果表明:烟草种子为中型(0.3～2mm),外形多样,颜色有6种:土黄色、浅褐色、褐色、浅棕色、棕色、深棕色。所研究的烟草种子表面纹饰有11种类型。种子表面微形态作为属内种的鉴别具有一定价值,种皮表面纹饰、微观附属物为烟草种的区分提供了新的依据。期望逐步建立起烟草种子微形态谱库,对烟属植物做出更合理的属下等级划分,为我国烟草种质资源的保护、贮藏、利用、鉴别、流通、选种、配种、种子信息查询等提供方便。     

纳米陶瓷可以解决陶瓷的强化和增韧问题

利用纳米技术开发的纳米陶瓷材料是指在陶瓷材料的显微结构中，晶粒，晶界以及它们之间的结合都处在纳米水平（1-100mm），使得材料的强度、韧性和超塑性大幅度提高，克服了工程陶瓷的许多不足，并对材料的力学、电学、热学、磁学、光学性等性能产生重要影响，为替代工程陶瓷的应用开括了新领域。[第一段]     

美国Nano Steel公司推出新的表面硬化合金

美国Nano Steed公司推出了一种新的表面硬化合金SHS9700。这种合金在不添加镍、钼或钨的情况下可获得非常精细的晶状显微结构以及非常高的硬度（达到69RC）。公司称该合金具有极优异的耐磨损性能，优于碳化铬和其他复杂碳化物材料耐磨损性能的5倍。