纳米三氧化二铝对陶瓷烧结温度的影响

采用在普通陶瓷坯料上涂抹一层纳米三氧化二铝的方法进行分组烧结试验。利用纳米颗粒的奇异特性提高坯料表面的扩散速率,降低烧结温度,提升烧结产物的致密化程度。实验中通过控制纳米添加剂的剂量以及工艺优化,取得最佳的增强、增韧效果。运用SME、XRD等检测手段分析不同晶型、不同形貌的纳米氧化铝对烧结温度的降低程度以及力学性能的改善状况,为陶瓷制备提供实验数据储备。实验结果表明:在陶瓷坯料表面涂抹纳米三氧化二铝涂层既可节省纳米材料又能大幅度降低烧结温度,是提高力学性能的行之有效的措施。     

CrAIN／TiAIN纳米多层膜的微结构及其性能研究

采用磁控反应溅射法制备了不同调制周期的CrAIN／TiAIN纳米多层膜,并通过x射线衍射仪、显微硬度计、扫描电镜分析了调制周期对多层膜的微结构、力学性能和高温抗氧化性能的影响。结果表明：CrAIN／TiAIN纳米多层膜共格外延生长,呈现CrAIN（或TiAIN）面心立方结构,且呈（111）择优取向;CrAIN／TiAIN纳米多层膜在某些调制周期出现硬度异常升高的超硬度效应;CrAIN／TiAIN纳米多层膜比CrAIN,TiAIN单层膜具有更好的高温稳定性,高温时仍具有较高的硬度。     

纳米TiO2固载脂肪酶及其固载界面表征

以3种不同形貌的纳米TiO2为载体固定化脂肪酶,研究载体形貌、酶添加量、pH值、温度和时间对固载酶活性的影响.研究结果表明,纳米线形貌TiO2固定化效果最好,最优固定化条件为加酶量0.25g/25mL溶液、pH 7.0、固载温度40℃、固载时间6.3h.利用SEM、XRD、FT-IR等对固载酶及其界面进行表征,SEM和XRD结果表明,脂肪酶吸附于纳米线TiO2载体表面,且未改变纳米线TiO2的晶型结构;FT-IR表征表明固载酶含有脂肪酶的特征吸收峰;比表面积分析显示固定化后样品的BET明显减小,表明脂肪酶在纳米线TiO2表面进行物理型吸附.     

Upeonversion Emission and Paramagnctism of Colloid Ba2ErF7 and Ba2ErFT：Yb3＋ Nanoerystals Synthesized with Solvothermal Method

Ultrasmall near-monodisperse Ba2ErF7 nanocrystals with average crystal size 9.6 nm were synthesized with solvothermal method. The X-ray diffraction （XRD） and transmission electron microscopy （TEM） assays reveal that the as-synthesized Ba2ErF7 nanocrystals are of the cubic structure with the cell parameter of 5.943 A, instead of the reported orthorhombic and tetragonal structure. Two emission bands originated from 2Hwj4H3/2 → 4F5/2 and 4F9/2 ----＋ 4115,2 of Er3＋ can be observed under a 980 nm laser excitation. The magnetic mass susceptibility of the as-synthesized BazErF7 nanocrystals reaches 4.293 × 10-5 emu g-1 Oe-1.     

水热法制备锰锌铁氧体/碳纳米管磁性材料

采用成本低、污染少的水热法制备锰锌铁氧体包覆的碳纳米管磁性纳米复合材料,并对其进行表征.X射线衍射分析表明,180℃为制备复合材料的合适水温,所得粉体中含Mn0.5Zn05Fe2O4、碳纳米管和少量的γ-Fe2O3,升高反应温度并不能使γ-Fe2O3杂相消失.透射电镜及高分辨透射电镜分析表明,包覆在碳纳米管上的Mn0.5Zn0.5Fe2O4粒子为球形,粒径约为10 ～ 20 nm,Mn0.5Zn0.5Fe2O4粒子中含有少量方形的γ-Fe2O3.红外谱图分析表明,包覆前碳纳米管表面存在羟基、羰基和羧基等官能团,包覆后的复合材料在570 cm-1和1 388 cm-1处出现MnZn铁氧体的特征峰.磁滞回线结果表明,复合材料的饱和磁化强度值为1 145 364 A/m,剩余磁化强度值为438 517 A/m,矫顽力值为30 361 A/m,具有较好的铁磁性.     

Synthesis of Cu nano-particle in toluene used for conductive ink with a binder of polyurethane

Copper nanoparticles with a size of about 150 nm were prepared in toluene using oleic acid as protecting agent. The nanoparticles were used to prepare conductive Cu ink with a polyurethane binder. Oleic acid was used to prevent the nanoparticles from oxidization and agglomeration. The prepared Cu nanoparticles were characterized by X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The resistivity of the copper film on glass substrate that was prepared using Cu nanoparticle ink reached about 1.5× 10-4 2. cm-1 after it was annealed to 120 ~C. Both the nanoparticle ink and the films were characterized by XRD, fourier transform infrared （FT-IR）, and the thermogravimetry-differential scanning calorimetry instrument （TG- DSC）.     

ZnO纳米颗粒的分散及光致发光特性

利用火焰喷雾法成功制备了ZnO纳米颗粒,通过对样品的X射线衍射谱（XRD）和场发射扫描电子显微照片（FESEM）分析,发现制备的颗粒大小较为均匀,直径在10-20nm左右;结合多种物理方法对样品进行分散处理后,FESEM表征显示颗粒间的团聚得到较好改善;光致发光谱表明随着颗粒尺寸的减小,样品的紫外发光和可见发光的强度逐渐增强．     

激光辅助纳米压印填充过程有限元分析

随着光刻技术的发展,电子器件的尺寸越来越小,已经进入纳米量级.几十年来,光学光刻技术在半导体加工图形转移的过程中一直扮演着重要角色,纳米压印技术以产量高、成本低、工艺流程简单的优点逐渐在图形转移技术中崭露头角.介绍了一种新型的激光辅助纳米压印技术,基于有限元方法并借助ANSYS软件对压印过程中二维的熔融层填充过程进行模拟.Si基板在激光作用下形成熔融层时,采用Mooney-Rivlin模型表示熔融层的机械性能.通过试验分析了深宽比、转移图形宽度和占空比对聚合物变形的影响,总结了技术的可行性与优越性,为以后纳米压印过程的优化提供了参数支持.     

铈掺杂改性TiO2的光催化性能

采用溶胶一凝胶法制备稀土金属铈（Ce）掺杂改性纳米TiO2光催化剂。运用X-射线衍射（XRD）、紫外一可见漫反射光谱（DRS）、程序升温氧吸附一脱附、透射电镜（TEM）等手段表征催化剂的组成、结构特征及与光催化性能的关联;以催化剂上甲基橙的紫外光催化降解反应为探针,探讨了掺杂前后TiO2光催化剂在紫外光下的活性规律。研究结果表明Ce的掺杂有利于抑制TiO2晶粒生长和晶型的转变,提高晶体的热稳定性,提高TiO2催化剂的可见光吸收能力;由于Ce具有贮存氧的能力,有助于TiO2催化剂对氧气的吸附,其吸附量随Ce掺杂量的增加而增加。     

美国开发出热蘸笔纳米光刻技术

美国劳伦斯伯克利国家实验室和伊利诺伊大学香槟分校的科学家首次研究出了温度在蘸笔纳米光刻技术中的作用,并据此开发出了新的热蘸笔纳米光刻技术。利用该技术可在多种材料表面构造纳米结构,用于精确制造纳米设备,以及研究药物作用机理等。