Sensitizing Mechanism and Adsorption Properties of Dye—Sensitized TiO2 Thin Films

The dye-sensitized TiO2 complex films were prepared by the dye coat onto TiO2 surfaces,and the sensitizing mechanism and adsorption properties of the dye-sensitized TiO2 complex films were inverstigated.The influence of the application conditions of dye adsorbed on TiO2 films on the amount of dye adsorption was discussed.Experimental results show that the concentration,the temperature of dye solutions and the dipping time of TiO2 films in the dye solutions have a significant influence on the amount of dye adsorption.Cell test indicates that the conversion efficiency of light to electricity increases with the amount of dye adsorption.     

ITO导电薄膜的用途和制备方法

本文综述了ITO薄膜的应用领域和制备工艺。ITO薄膜主要用于光电器件中,例如用于液晶显示(LCD)。制造ITO薄膜的工艺方法很多,本文综述了磁控溅射法、CVD法、喷雾热分解法和溶胶—凝胶法4种制膜工艺。     

薄膜蒸镀光学控制中的一种现象的数学分析

证明了在连续蒸镀两层高，低折射率介质膜过程中，当第一层厚度不足λ／４厚时，刚开始蒸镀第二层膜时其反射率变化趋势与第一层膜相同，并由此展开，说明两层厚度不足λ／４的薄膜在很大程度上等价于一层λ／４的薄膜。     

一种聚酯衍生物的光衰减特性

具有１，６－地苯蒽发色基团的聚酯衍生物薄膜（ＰＥ０可产生较强的蓝绿色 ，同时在紫外光照射下出现光退化现象。ＰＥ的发光强度随着射时间的增加迅速减弱，然后逐渐地饱和，荧光光谱由５００ｎｍ逐渐蓝移至４５０ｎｍ；光退化了的聚酯衍生物薄膜经 热８０１－１００℃至少１ｈ的退火处理，发光强度可以恢复到照射前的水平，如果再经受紫外光照射，发光强度会再次降低，加热后发光强度又可以基本完全恢复如此过程可以反复多次。具     

含聚二甲基硅氧烷的聚醚聚氨酯膜透气性及表面性质研究

以聚二甲基硅氧烷（ＰＤＭＳ）／聚四氢呋喃（ＰＴＭＯ）为软段，４，４＇－二环己基甲烷二异氰酸酯（ＨＭＤＩ）为硬段（丁二醇ＢＤ为扩链剂）制成的多相嵌段共聚物作为基质材料，进行了气体（Ｏ２和Ｎ２）透过性试验，同时对膜材料进行了ＥＳＣＡ表面分析。结果表明，共聚物膜的透气性能取决于材料中连续相组分，随着软段中ＰＤＭＳ含量的改变而变化。当ＰＤＭＳ含量较高时，共聚物膜显示出ＰＤＭＳ均聚物的特性，具有较高的气体秀     

聚乙烯包装薄膜形变性能与微观结构的研究

采用拉伸实验，研究形变速率对聚乙烯包装薄膜力学性能的影响。采用Ｘ射线衍射方法，分析聚乙烯薄膜形变后微观结构的变化，得到了形变后材料内部的微晶尺寸和点阵畸变值。