Use of recycled copper slag for blended cements

Copper slag is a by‐product generated during smelting to extract copper metal from the ore. The copper slag obtained may exhibit pozzolanic activity and may therefore be used in the manufacture of addition‐containing cements. In this paper the effect of the incorporation of the copper slag in cement is measured. Blends of copper slag with Portland cement generally possess properties equivalent to Portland cement containing fly ash, but very different to the silica fume incorporation. Copper slag and fly ash reduce the heat of hydration more effectively than silica fume in mortars. The replacement of 30% cement by copper slag reduces the flexural and compressive strength in a similar way to fly ash; however, after 28 days, the reduction is less than the percentage of substitution. Hydrated calcium aluminate phases were analysed using scanning electron microscopy (SEM) and X‐ray diffraction (XRD) techniques. The pozzolanic activity of copper slag is similar to that of fly ash and higher than silica fume. In the presence of low water/cement ratios, certain pozzolanic materials produce a very compact cement paste that limits the space available for hydration products, a determining factor in the formation of hydrated calcium aluminates. SEM was found to be a useful analytical technique when aluminates are formed and can be clearly detected by XRD. Copyright © 2008 Society of Chemical Industry     

Preparation of multi-compositional gas sensing films by combinatorial solution deposition

Various compositions of gas sensing films were prepared by the combinatorial deposition of SnO₂, ZnO, and WO₃ sol solutions and their gas sensing behaviors were investigated. The film composition could be manipulated conveniently via the alternate dropping of different oxide sol solutions. From the correlation between film compositions and gas sensitivities, the selective detection of C₂H₅OH and CH₃COCH₃ in the presence of CO, C₃H₈, H₂, and NO₂ could be attained. In addition, the discrimination between C₂H₅OH and CH₃COCH₃, which is a challenging issue due to their similar chemical nature, becomes possible. This research demonstrates the precise design of the sensor-material composition for the selective gas detection via the combinatorial approach.     

Low temperature synthesis of aluminium titanate by an aqueous sol-gel route

Formation of aluminium titanate (AT) has been achieved at low temperature through sol-gel process using boehmite and titanium hydroxide as precursors by controlling the particle size at nanoscale followed by in-situ peptisation. The formations of AT phase, particle size distributions, sintering and thermal expansion characteristics, and microstructural features have been reported. DTA and XRD analysis have been performed to confirm the formation of AT. A 94% relative density was obtained for aluminium titanate sintered at 1550 °C with controlled grain size in the range of 2-3 μm.     

Growth of β-FeSi2 layers deposited from a molten salt

β-FeSi₂ layers have been successfully grown using a molten salt method for the first time. It was found that single phase and homogeneous β-FeSi₂ layers with a columnar domain structure can be grown on FeSi substrates. The layer thickness was demonstrated to be controllable by the growth temperature and time, and was diffusion controlled. It was shown that the layers were void- and crack-free compared to similar layers grown on Fe substrates: this difference is explained in terms of Fe diffusion. This vacuum-free simple growth technique is useful for the fabrication of large area semiconductor devices at low cost.     

Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.     

Electrical/electronic effects of titanium and iron impurities in EFG and FZ solar cell silicon: SPV/EBIC analysis

In this paper results on surface photovoltage (SPV) and electron beam induced conductivity (EBIC) studies of edge-defined film-fed growth (EFG) and floating zone (FZ) silicon solar cell materials (both p-type) are presented. A systematic comparison based on minority carrier diffusion length and carrier recombination is made between: (i) samples contaminated with Ti and/or Fe, (ii) samples gettered by phosphorous diffusion, and (iii) as-received samples. Deep level transient spectroscopy (DLTS) measurements, together with the iron-boron (FeB) pairing kinetics [1] have successfully been used to detect the presence of Fe in the samples. Even though this process is effective in revealing Fe impurities in p-type FZ silicon it is evidently not suitable for Fe identification in p-type EFG silicon. Ti, like Fe, is found to be a prominent lifetime-limiting metallic impurity in both EFG and FZ silicon. Phosphorous diffusion is proven to be an effective external gettering technique for fast-diffusing impurities such as Fe, but not for Ti.     

WC对Cu/WC_P复合材料性能及组织的影响