棕刚玉粉中Al2O3含量分析方法的探讨

对耐火材料——棕刚玉粉的质量分析控制，提出了用实用性的检测方法测定其Al2O3含量。通过与国家标准分析方法的对比试验，证实快速实用分析方法测定棕刚玉粉中Al2O3含量是可行的。     

钛铁矿流态化氧化机理研究

对低品位钛铁矿进行预氧化、预还原等预处理后可满足硫酸法生产钛白粉工艺所需高品位钛铁矿的要求。本试验采用流态化预氧化方法处理风化程度低、含硫较高的钛铁矿。结果表明 :流态化氧化可大幅度地降低钛铁矿中硫含量 ;钛铁矿流态化氧化的适宜温度为 :80 0～ 90 0℃ ,且在此温度范围内 ,随温度的升高 ,钛铁矿的氧化速度增加 ,在 90 0℃时 ,5 0min钛铁矿基本能完成氧化     

Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Two-phase (B2+L1₂) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni₃Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4-7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN₁.     

单壁纳米碳管/纳米铝基复合材料的增强效果

用半连续氢电弧法和活性氢等离子蒸发法分别制备出单壁纳米碳管(SWNTs)和纳米A1粉体，然后用提纯后的SWNTs和纳米A1粉体制备出SWNTs含量(质量分数)分别为0、2．5％、5．0％、7．5％和10.0％的单壁纳米碳管／纳米铝基块体复合材料．SWNTs对高强度纳米A1基体具有显著的增强作用，当SWNTs含量小于5．0％时，材料的硬度随着SWNTs含量的提高线性上升．其中5％SWNTs和纳米A1的复合增强效果最好，其硬度可达2.89GPa，大约是粗晶A1(0．15GPa)的20倍．当SWNTs含量超过5．0％时，增强效果开始缓慢的下降．讨论了单壁纳米碳管增强纳米铝基复合材料的强化机制．     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

深部调剖驱油交联剂的研究

为提高非均质性严重的地层原油采出率 ,合成了用于聚合物驱油的 4种交联剂 ,并对聚合物种类、用量和其与交联剂组成的体系进行了评价。 4 0℃下铝交联剂凝胶粘度低 ,酚醛树脂交联剂低温下不成胶 ,而有机铬交联剂 (J2 )和有机复合胺 (J3)交联效果好。当选用HPAM/有机铬交联剂 /有机酸交联体系时 ,其中HPAM相对分子质量为 2 1× 10 7,可通过改变体系pH值调节成胶速度 ,pH值 6 5时 ,14 0 0mg/LHPAM和 4 0 0mg/LJ2组成的体系在 4 0℃、30d可形成粘度为12 0mPa·s以上的凝胶 ,且热稳定性好 ,成胶时间能满足现场施工需要。 14 0 0mg/LHPAM和10 0 0mg/LJ3交联剂组成的体系 ,成胶时间长 ,有利于油田深部调剖驱油     

高压水射流技术粉碎原盐的研究

以原盐为被粉碎研究对象,通过对高压水射流粉碎原盐形貌的观察和成分分析、高压水射流原盐粉碎性能分析,以及高压水射流粉碎原盐各影响因素的正交分析,研究表明高压水射流粉碎技术对原盐具有良好的解理性且粉碎效率高、耗能低。各因素对原盐粉碎效果的影响顺序为:射流压力卤水喷嘴直径、料液混合喷嘴直径、靶面形状。     

汽轮机轴承烧瓦与轴颈的渗巴氏合金现象

简述轴承工作性质，巴氏合金应用与相组成的基本情况。论述汽轮机转子在两个电厂长期运行后，由于轴颈发生的不正常摩擦损伤，在大修改造中由无损检查、机械加工揭示出轴颈存在严重的渗巴氏合金现象，低熔点金属Sn、Sb与Cu向转子材料晶界的深层渗入最终导致了3根大型在投转子的严重开裂与报废。图11表2     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

低松装密度水雾化铜粉工艺的研究

本文研究了氧化 还原法生产铜粉的新工艺 ,该工艺是通过氧化还原将水雾化铜粉加以表面改性 ,形成海绵状的粉末 ,显著降低水雾化铜粉的松装密度 ,这种铜粉既具有电解铜粉低的松装密度 ,又具有水雾化铜粉高的流动性。讨论了氧化时间、氧化温度对铜粉松装密度的影响。本工艺是一种新型环保、节能、可替代电解法生产铜粉的先进工艺