Influence of accelerated ageing on methacrylate‐based denture resins heterogeneity as viewed by ESR‐spin‐probe method

The electron‐spin‐resonance (ESR) spin‐probe method, was used to study the heterogeneity of denture resins based on poly(methyl methacrylate). Results for three resins processed by microwave energy, conventional curing and cold curing (depending on the curing procedure and exposed to ageing in various environmental conditions) were compared. All three cured resins were stored over the same time (1200 h) in distilled water at ambient temperature and in artificial saliva at 348 K. The temperature‐dependent ESR spectra of a spin probe dispersed in the denture resins are analyzed in terms of line‐shapes and line‐widths. The appearance of two spectral components was taken as an indication of resin heterogeneity. The results reveal that the cold‐cured resin has a lower local density in comparison with microwave and conventionally cured resin. The amount of residual monomer also contributes to the local motion of polymer segments. The change of denture resins exposed to ageing is influenced both by the structure of the original resin and the ageing conditions. Restricted motion of a spin probe incorporated into the acrylic resins exposed to accelerated ageing suggests additional crosslinking of polymer chains. The differences are observed for all the investigated resins, but the highest change is observed with the cold‐cured resin. The ESR results are accompanied by T_g and T_m measurements. Copyright © 2005 Society of Chemical Industry     

A simple handling technique for mammalian oocytes and embryos during preparation for transmission electron microscopy

Due to their small size, mammalian oocytes and embryos pose unique problems during preparation for transmission electron microscopy. This paper outlines a method which combines protein embedding with centrifugation to locate the specimens on the face of a Beem capsule mould. This method facilitates both the processing of oocytes with minimal loss and rapid location of the specimens within the block for simultaneous sectioning, staining and examination.     

Colour Centres and Energy Transfer in BaF2-xClx:Eu2+ Phosphors

The optical absorption spectra of BaF2-xClx:Eu2 after ultraviolet (UV) light excitation were investigated.The differences between the absorption spectra after and before excitation (DAS) were observed.The DAS increase at both the high and the low energy side of F band in BaF2-xClx:Eu2 after 245 nm UV light excitation.The bleach effect of UV light and the absorption of electrons in the valence band may account for the former and the formation of Fa centres (association of F(Cl-) centres), whose absorption band matches the HeNe laser better, may explain the latter.In the write-in process, the transfer of electrons is via tunneling.In the readout process, the transfer of electrons captured in F(F-) and Fa centres is more likely via tunneling, and that of F(Cl-) centres is more likely via conduction band.     

Discrimination of B–C–N nanotubes through energy-filtering electron microscopy

Various multi-walled nanotubes in the B–C–N system are thoroughly investigated using a JEOL-3100FEF high-resolution field emission transmission electron microscope operating at 300 kV and equipped with an in-column built Omega filter. Spatially-resolved B, C and N elemental maps of the nanotubes are constructed. It is realized that a wide variety of tubular arrays composed of B, C and N atoms may exist in the system. Sandwich-like BN-rich and C-rich alternating tubular shells, graphitic C layers inside and outside of pure BN shells induced either by surface contamination, or electron beam irradiation, separation of C-rich and BN-rich tubes and/or BN particles within tubular bunches may take place. One should carefully take these effects into account while analyzing nanotube physical properties, e.g., electrical or optical, rather than simply rely on electron energy loss spectra typically collected from B, C and N containing nanostructures as a whole. Striking dependence of an individual nanotube electrical conductivity on tubular shell chemistry is demonstrated using I–V curve recording in an atomic force microscope.     

Fluorescence and IR characterization of epoxy cured with aliphatic amines

Cure reactions of the stoichiometric mixtures of diglycidyl ether of bisphenol A (DGEBA) and two very low molecular weight aliphatic polyether diamines (PED) were studied by using fluorescence and mid- and near-IR spectroscopic techniques. As the cure proceeded, the primary amine groups in PED are converted to the secondary and the tertiary amines. Near-IR spectral analysis was used to calculate the concentration of the three amine groups as a function of cure time. The decrease in the fluorescence intensity of DGEBA at about 307 nm was observed due to more effective quenching of the tertiary amine groups in PED, in comparison to the primary and the secondary amine groups. A large decrease in fluorescence intensity at 75 and 95 °C cure was observed. The amount of all the amine species was estimated from NIR spectra to shed light on the cure kinetics of PPO (polypropylene oxide) in comparison with PEO (polyethylene oxide) epoxy, as well as to explain their fluorescence behavior.The fluorescence intensity changes were correlated to the extent of epoxy reaction obtained by mid- and near-IR spectroscopy.     

Assessing organo-clay dispersion in polymer layered silicate nanocomposites: A SAXS approach

A SAXS method for the quantitative assessment of the morphology of polymer layered silicate nanocomposites is proposed. Fitting the SAXS patterns, the number of clay layers, the periodicity of the layers in the tactoids, the thickness of the regions interposed between the clay platelets and their distributions can be measured. A good agreement with TEM data was obtained, avoiding the inconsistencies with microscopical observations often reported in the literature.     

Catalytic properties and electronic structure of copper ions in Cu-ZSM-5

The effect of ion exchange conditions, such as Si/Al ratio, precursor copper salt, pH and concentration of the solution, on the catalytic activity in SCR of NO by propane and on the electronic state of copper ions in Cu-ZSM-5 has been studied. The NO conversion in NO SCR by C₃H₈ has been found to reach a maximum value at Cu/Al ratio about 0.37–0.4 and remain constant at higher Cu/Al.

ESR and UV–vis DR spectroscopy have been used to elucidate stabilization conditions of copper ions in Cu-ZSM-5 zeolites as isolated Cu²⁺ ions, chain copper oxide structures and square-plain oxide clusters. The ability of copper ions for reduction and reoxidation in the chain structures may be responsible for the catalytic activity of Cu-ZSM-5. These transformations of copper ions are accompanied by the observation of intervalence transitions Cu²⁺–Cu⁺ and CTLM of the chain structures in the UV–vis spectra.     

Life cycle of hydroprocessing catalysts and total catalyst management

Hydroprocessing catalysts based on Ni, Co, Mo and W are used in various refinery processing applications where several deactivation mechanisms become of importance (coke formation, active phase sintering, metals deposition, poisoning) in the catalyst's life cycle. The life cycle of commercial hydroprocessing catalysts is very complex and includes the catalyst production, sulfidation, use, oxidative regeneration followed by re-sulfidation and reuse or, if reuse is not possible, recycling or disposal. To understand the changes in catalyst properties taking place during a life cycle, the catalyst quality in the different stages can be best monitored by using advanced analytical techniques. The catalyst's life cycle is further complicated by numerous technical, environmental and organizational issues involved. In principle, different companies can be involved in each of the life cycle steps. Leading catalyst manufacturers, together with specialized firms, offer refineries a total catalyst management concept, starting with the purchase of the fresh catalyst and ending with its final recycling or disposal. Total catalyst management includes a broad range of services, ensuring optimal timing during the change-out process, reliable, smooth and safe operations, minimal downtime and maximum catalyst and unit performance.     

Structural properties of phosphorous-doped polycrystalline silicon

The structural properties and hydrogen bonding of undoped and phosphorous doped polycrystalline silicon produced by step-by-step laser dehydrogenation and crystallization technique were investigated using Raman spectroscopy and hydrogen effusion measurements. At low laser fluences, E_L, a two-layer system is created. This is accompanied by the change in hydrogen bonding. The intensity of the Si–H vibration mode at 2000 decreases faster than the one at 2100 cm⁻¹. This is even more pronounced in phosphorous-doped specimens. The laser crystallization results in an increase of the hydrogen binding energy by approximately 0.2–0.3 eV compared to the amorphous starting materials.