Influence of interfacial strength on the fracture toughness of glass-ceramic matrix composites

Nine kinds of glass-ceramic matrix composites with different compositions and interfacial strength (τ _s) were prepared. The influence of τ _s on the fracture toughness(K _1c) of composites was studied. It was discoved that, for the system no chemical reaction taking place at the interface, K _1c increased proportionally with τ _s increasing at the first stage, then decreased when τ _s reached a certain value. According to this result, a model of relationship between τ _s, thermal mismatch (Δα _r) and K _1c was built up. If a chemical reaction took place and a new phase was formed in the interface, the K _1c of composite was effected by the combination of τ _s, chemical bonding, radial interfacial stress and other factors. Project supported by the National Natural Science Foundation of China Synopsis of the first author Wang Lingsen, professor, born in 1938, current research field: special ceramic and ceramic matrix composite, etc.     

聚乙烯醇复合膜的制备

以亲水性的聚乙烯醇为原料，采用机械涂敷法制备复合纳滤膜．考查了基膜、聚乙烯醇的浓度、交联剂的浓度及配比、涂层厚度、交联时间以及热处理等对膜分离性能的影响，确定了最终制备条件．在一定的温度和湿度条件下，在截留相对分子质量为100000的基膜上，通过5％的聚乙烯醇溶液与1％的戊二醛的交联反应，研制了截留相对分子质量为600的PVA复合纳滤膜。     

正交试验优化复合纳滤膜复合条件

采用聚砜基膜，以哌嗪水溶液与均苯三甲酰氯正己烷有机溶液发生界面聚合反应，在聚砜基膜上形成一超薄脱盐层，从而制备聚哌嗪酰胺复合纳滤膜．制备过程中影响复合纳滤膜性能的因素是多方面的．着重讨论了水相浓度、有机相浓度、有机相处理时间的影响．采用正交试验法对制备条件进行优化，制得性能较佳的复合纳滤膜．     

渐开线齿轮点蚀位置的确定及其计算综合曲率半径的误差修正

依据赫兹强度理论 ,指出一对标准渐开线直齿齿轮啮合时 ,最大接触应力位于齿轮单啮合区靠近小齿轮处单双啮合区的分界线上。小齿轮点蚀发生在分度圆与齿根圆之间 ,大齿轮点蚀发生在分度圆与齿顶圆之间。并列举实例 ,证明目前传统设计方法计算点蚀处齿轮综合曲率半径误差较大 ,绘制出精确计算值与传统计算值的比值曲线 ,并给出结论 :传统设计方法得到的结果不安全 ,有误差 ;误差与齿轮模数无关 ,误差随着小齿轮齿数的增加渐小 ,误差随着齿轮齿数比的增大先渐大后渐小     

The effect of precipitation of Mg2Al3 and of MnAl6 on texture evolution during isothermal annealing and subsequently on formability of CC AA5182 Al alloy

Continuous cast (CC) AA5182 Al alloy with the precipitation of Mg₂Al₃ and of MnAl₆ was cold rolled to 70% reduction and then isothermally annealed in a salt bath at three temperatures (316, 343, and 371 °C) for different times. Texture evolution during recrystallization was investigated. It was found that the recrystallization textures of the material with intense Mg₂Al₃ precipitation along the grain boundaries exhibited weaker Cube, Goss and R/β fiber components than those of the material with the more uniform fine MnAl₆ precipitates. The opposite was true in the cold rolled condition, i.e. the material with MnAl₆ precipitation had weaker Cube, Goss, and R/β fiber components in the cold rolled condition than the material with intense Mg₂Al₃ precipitation. Thus, recrystallization textures of material with Mg₂Al₃ precipitation were weaker than material with MnAl₆ precipitation. This is due to the fact that large Mg₂Al₃ particles favor the nucleation of randomly oriented grains. When subjected to formability tests, the material with prior Mg₂Al₃ precipitation displayed a lower anisotropy in tensile yield strength, ultimate tensile strength, elongation, and strain hardening exponent than material with prior MnAl₆ precipitation. This is in accord with the texture results which indicated that the recrystallization textures of material with an initial Mg₂Al₃ precipitation were closer to those of a perfectly random sample than those of material with an initial MnAl₆ precipitation. On the other hand, the elongation and Olsen values were lower and the surface quality after bending tests was worse for material with Mg₂Al₃ precipitation. This is due to the non-uniform distribution of Mg₂Al₃ particles which precipitated primarily along the grain boundaries and caused an earlier formation and coalescence of the microvoids around the grain boundary precipitates. The forming limit diagrams (FLD) correlated well with the tensile, Olsen and bending results.     

High-Temperature Strength of Niobium Alloy 5VMTs with a Silicide-Ceramic Coating. Part 1. Short-Term Strength Characteristics

Experimental data on the short-term strength and plasticity of niobium alloy 5VMTs of the system Nb–W–Mo–Zr in its initial state, after annealing, and with a silicide-ceramic protective coating obtained by testing in vacuum, an inert atmosphere, and in air in the temperature range from 290 to 2270 K are analyzed. The process of microcrack initiation and propagation in the protective coating and matrix is investigated in high-temperature static tension. The limiting plastic strain values have been established at which the composite retains its load-carrying capacity in high- temperature aggressive and oxidizing gas atmospheres.     

组合把持器在封闭电炉中的应用

介绍了16．5MVA封闭炉的组合把持器，结构和所选择的电炉参数及运行情况。实践证明该设备是可行的。     

餐厨垃圾发酵生产乳酸的工艺优化

为提高餐厨垃圾发酵生产乳酸的效率,采用Plackett-Burman和中心复合两种统计试验方法对影响发酵的因素进行初筛和优化.Plackett-Burman实验的结果表明,影响乳酸发酵的正向显著性因素有乳酸菌TD175、糖化酶、吐温80、纤维素酶;灭菌是负显著性因素.通过中心复合试验设计,确定最佳发酵工艺:乳酸菌接种量6.6%,糖化酶160U/g,纤维素酶60U/g,吐温800.08%,温度45℃.最佳工艺条件下发酵40h,乳酸产量能达到66.13g/L,每克干垃圾产乳酸0.53g.餐厨垃圾的乳酸发酵无需灭菌、无需额外营养物,具有良好的经济效益和应用前景.     

几种聚乳酸／生物活性陶瓷复合材料细胞相容性的比较

采用溶解共混法制备含30%硅灰石的聚乳酸/硅灰石新型生物医用复合物膜.将大鼠成骨细胞ROS 17/28系种植在复合物表面使其存活,考察生长情况和复合物的生物活性,并与目前研究应用较多的聚乳酸/羟基磷灰石、聚乳酸/磷酸三钙及聚乳酸/珍珠层粉复合物进行比较.荧光染色实验及MTT测试表明,4种复合物膜表面细胞均可以正常的生长和增殖,且呈现出聚乳酸/珍珠层粉>聚乳酸/硅灰石>聚乳酸/羟基磷灰石>聚乳酸/磷酸三钙的结果,说明聚乳酸/硅灰石复合物材料具有较好的细胞相容性,适于应用在骨修复及骨组织工程领域.     

孔内深层超强夯法处理厚层人工回填土的应用研究

介绍了孔内深层超强夯法（SDDC）的基本原理,并将SDDC工法运用于处理某机场内厚层人工回填土地基,对无机固体废料进行了资源化回收利用。通过复合地基载荷试验、标准贯入试验和重型动力触探试验对SDDC施工质量进行检测,对SDDC桩体和桩间土的承载力效果进行评价。结果表明,经SDDC工法处理后的复合地基均匀性较好,承载力显著提高,达到工程使用要求。