Contact interaction of double titanium and chromium diboride with Fe-Cr alloys

The kinetics of wetting double titanium and chromium diboride by iron-based alloys with different chromium content is studied. It is shown that contact angles are formed in such systems over the range 0–10°. The energy parameters of wetting are calculated. It is established that chromium as a surface-active element promotes Fe-Cr alloy spreading on the diboride surface. The microstructure of the interaction area is studied. It is shown that terminal solid solutions and eutectics are formed in the TiCrB₂-(Fe-Cr) system. The optimum compositions of the metallic binder are determined for TiCrB₂-based composite materials. __________ Translated from Poroshkovaya Metallurgiya, Vol. 46, No. 1–2(453), pp. 109–115, 2007     

K_2O－B_2O_3－SiO_2玻璃成分对析晶性能的影响

本文利用ＤＴＡ、ＸＲＤ、ＴＥＭ、ＳＥＭ等技术研究了三种Ｋ２Ｏ－Ｂ２Ｏ３－ＳｉＯ２玻璃的析晶性能。结果表明，Ｋ２Ｏ－Ｂ２Ｏ３－ＳｉＯ２玻璃的析晶由分相引起，分相和析晶能力受成分影响较大。随Ｂ２Ｏ３和Ｋ２Ｏ含量增多及Ｋ２Ｏ／Ｂ２Ｏ３比值的降低，析晶加强。析晶中主晶相类别尚未查清，次晶相确定为α－方石英。     

测量高功率激光的体吸收能量计

叙述了体吸收激光能量计的特点，介绍了其标定方法，给出了其技术参数。体吸收激光地的推广应用取得了广泛的社会效益。     

金选别工艺的发展与深化

本文阐述了充分考虑矿石性质,探索出混合浮选的分步流程,恰当的施用多元扑收剂所产出的“协同效应”,稳定和强化选别工艺,收到提高选金技术指标的效果。     

Magnetic properties and microstructural characteristics of bulk Nd–Al–Fe–Co glassy alloys

Bulk Nd–Al–Fe–Co glassy alloys with diameter up to 5 mm were investigated by magnetic measurements, magnetic force microscopy (MFM) and high resolution electron microscopy (HREM) at room temperature. The results from the measurement of vibrating sample magnetometer show that these samples with compositions Nd₆₅Al₁₀Fe_25-xCo_x (x=0–10 at.%) and Nd₆₀Al₁₀Fe₂₀Co₁₀ display hard magnetic properties with H_C of 300 kAm⁻¹, M_S of 10 Am² kg⁻¹, and M_r of 7 Am² kg⁻¹. The MFM measurements of the Nd₆₀Al₁₀Fe₂₀Co₁₀ bulk metallic glass (BMG) reveal the existence of magnetic domains with a period of about 0.36 μm, and the ordered clusters with the averaged size of about 5 nm was observed by the HREM on the sample. The domain structure or cluster is believed to be associated with the appearance of hard-magnetic properties in this alloy system. The existence of the large-size domains demonstrates that magnetic moment of a great deal of ordered atomic clusters in the BMG has been aligned by exchange-coupling.     

含钴锆基块状非晶合金的制备与力学性能

采用水淬法制备了Zr—Ti—Cu—Ni—Be—Co块状非晶合金(BMGs)。使用XRD进行相分析，采用热分析仪进行玻璃转变温度、晶化温度和热稳定性等的测定，用SEM观察试样压缩后的外表面和断口形貌。研究了Co对Zr—Ti—Cu—Ni—Be合金非晶形成能力(GFA)、热稳定性及力学性能的影响。结果表明：含Co的所有Zr—Ti—Cu—Ni—Be BMGs都有1个明显的玻璃转变点和宽的过冷液相区(△T）。Zr38Ti17Cu10.5Co12Be22.5合金具有和Zr41Ti14Cu12.5Ni10Be22.5合金相当的△T；Co的添加明显提高Zr—Ti—Cu—Ni—Be BMGs的力学性能，含Co量大于10at％的Zr—Ti—Cu—Ni—Be BMGs的压缩断裂强度（σf）超过2000MPa，Zr38Ti17Co22.5Be22.5合金的σf达到2230MPa，比Zr41Ti14Cu12.5Ni10Be22.5合金的σf提高23％。     

含硼金刚石的金属包膜成分及其物相的研究

本文采用铁基触媒加入硼铁的方法，在高温高压条件下合成了含硼金刚石，利用电子探针（EPMA），透射电子显微镜（TEM）两种检测手段，分析了含硼金刚石金属包膜的微观组织结构，化学组成成分，各组成成分的物相及其可能形成的原因。研究结果表明：金属包膜的成分及其物相由正交立方结构的（Fe,Ni）3C，面心立方的γ-（Fe,Ni），面心立方的Fe23（C，B）。及少量的FeB,Ni3B组成，这些成份主要来源于原材料，其含量在高温压过程中是瞬间变化的。     

����ʽ��������ŵ���������մɲ��֯֯�������о�

 在大量科学试验基础上，提出一种金属表面形成金属陶瓷的新工艺方法。该方法具有放电电压低，陶瓷层结构致密与基体冶金结合，适用于多种金属材料等优点。文中利用光学显微镜和扫描电镜（SEM）观察了陶瓷涂层的显微组织，并通过X射线衍射和机械性能试验对其相结构和室温力学性能进行了探讨。结果表明：金属陶瓷涂层的晶粒细小，分布均匀，具有高的硬度及良好的耐磨性。     

Nd对块体Mg-Cu-Y-Nd非晶合金玻璃形成能力的影响

在非真空熔炼条件下采用工业纯原材料和负压铜模吸铸法制备Mg65Cu25Y10-xNdx(x=0,2,4,6,8,10)棒状试样,利用差示扫描量热(DSC)和X射线衍射(XRD)等方法分析Nd对Mg-Cu-Y-Nd非晶合金玻璃形成能力的影响。结果表明:Nd的含量(x)为0,4,6成分的合金试样具有完全非晶态组织,且x=4时具有最大的玻璃形成能力,其约化玻璃转变温度(Trg)为0.592,过冷液相区宽度(ΔTx)高达66 K;当x为2,8,10时,由于合金成分明显偏离共晶成分,玻璃形成能力降低,试样只含有少量非晶,且主要呈晶体组织特征。