Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

唐钢ER70S-6焊丝钢的生产工艺研究及质量分析

介绍了唐钢ER70S-6焊丝钢的特点，对盘条质量进行了分析。对该钢化学成分、冶炼和轧制工艺进行了优化研究，使其综合性能明显改善。     

钻机绞车滚筒体的窄间隙埋弧焊

针对钻机绞车滚筒体采用手工电弧焊工人劳动强度大、焊接效率低、质量不稳定及返修率高等问题,研制了钻机绞车滚筒体窄间隙埋弧焊专机。该专机由ESAB—A2埋弧焊电源和焊接小车、窄间隙焊头、滚轮架、防窜装置、旋转地线夹、三维焊接工作台、焊剂自动回收机组成。使用表明,采用该焊机焊接的滚筒体焊缝质量完全符合设计要求,合格率100%,焊接效率比原来提高6倍。每件滚筒体的焊接可降低人工成本约80%。     

爆炸焊接边界效应的力学能量原理

在爆炸焊接工艺中,存在一种称为边界效应的物理现象。即在一般情况下,在爆炸焊接后的复合材料中,会出现雷管区不复、其余周边被打伤、打裂和变形严重等问题。这些问题严重地影响着这类材料的质量。该文从传统的和经典的力学及能量原理出发,探讨了边界效应产生的力学 能量原理,并且提出了预防的措施。     

Bayesian and Dempster-Shafer fusion

The Kalman Filter is traditionally viewed as a prediction-correction filtering algorithm. In this work we show that it can be viewed as a Bayesian fusion algorithm and derive it using Bayesian arguments. We begin with an outline of Bayes theory, using it to discuss well-known quantities such as priors, likelihood and posteriors, and we provide the basic Bayesian fusion equation. We derive the Kalman Filter from this equation using a novel method to evaluate the Chapman-Kolmogorov prediction integral. We then use the theory to fuse data from multiple sensors. Vying with this approach is the Dempster-Shafer theory, which deals with measures of “belief”, and is based on the nonclassical idea of “mass” as opposed to probability. Although these two measures look very similar, there are some differences. We point them out through outlining the ideas of the Dempster-Shafer theory and presenting the basic Dempster-Shafer fusion equation. Finally we compare the two methods, and discuss the relative merits and demerits using an illustrative example.     

穿壁焊极柱合金探索

本文对起动用铅酸蓄电池穿壁焊极柱用合金配方进行了探索 ,并得到了良好的应用效果     

Finite elements in the analysis of pressure vessels and piping-a bibliography (1976–1996)

The paper gives a bibliographical review of the finite element methods (FEMs) applied for the analysis of pressure vessel structures/components and piping from the theoretical as well as practical points of view. The range of applications of FEMs in this area is wide and cannot be presented in a single paper; therefore the aim of this review is to give the reader an encyclopaedic view of the differnt possibilities that exist today for the finite element analysis in the fields of pressure vessels and piping. The bibliography at the end of the paper contains approximately 1900 references to papers, conference proceedings and theses/dissertations on the subject that were published in 1976–1996. These are classified in the following categories: linear and non-linear, static and dynamic, stress and deflection analysis; stability problems; thermal problems; fracture mechanics problems; contact problems; fluid-structure interaction problems; manufacturing of pipes and tubes; welded pipes and pressure vessel components; development of special finite elements for pressure vessels and pipes; finite element software; and other topics. Also finite element software, general purpose and special purpose codes, used for the analysis of pressure vessels and pipes are briefly discussed and presented.     

An investigation of pore cracking in titanium welds

Two welded Ti-6A1-4V pressure vessels leaked prematurely in service. The leaks were caused by cracks emanating from weld porosity. The cracks originated during fabrication, with subsequent growth in service leading to the formation of the leak paths. Pore cracking is thought to be caused by a mechanism that involves both sustained-load and cyclic contributions, with the former being the more prominent. It is shown that the tendency for cracking is influenced by pore position and that pore size is not a deciding factor in that regard. The factors that govern pore cracking are discussed, and the possible role of interstitial embrittlement is assessed.     

含钇奥氏体基堆焊焊条堆焊层研究

针对高温、磨损、热疲劳工况下服役零件的失效，研制了一种含稀土元素钇的奥氏体基沉淀强化型堆焊焊条，并对堆焊层组织与性能进行了较系统的研究。     

自动化加工过程的在线质量监测及管理平台的研究

以机器人焊接生产线质量的自动监测及管理为对象，探讨了流水线加工过程通用性质量监控平台的构建方法，采用基于网络的车间级前沿机及服务器，分别实现了现场单个质量监控点的微观质量监测及整个流水线的宏观质量管理；最后探讨了数据集市和数据挖掘技术系统在该系统的应用。