95W-Ni-Fe 合金工艺缺陷的 SAM 和 XPS 分析

藉助扫描俄歇探针、Ｘ射线光电子谱等分析了９５Ｗ－Ｎｉ－Ｆｅ合金碳污染和氧化的本质。发现，碳污染试样中碳的化学状态主要为石墨，少量为铁或镍的有机化合物，这些物质的界面富集使材料脆化。钨合金氧化后，氧大量富集于钨／粘结相界面，使沿着该界面的断裂更容易发生。     

声表面波可程序抽头延迟线研究

报道声表面波可程序抽头延迟线的研制情况。对该器件的总体结构，电路原理框图、声表面波可程序抽头延迟线结构作了一个扼要的概念。同时分别报道了我所研制的各类声表面波可程序抽头延迟线器件性能指标及相应的图片说明，最后对该器件仍存在的一些问题作了探讨。     

透水性沥青面层材料设计新法及应用

本文提出了一种根据主骨料空隙率设计透水性面层沥青混合料级配的新方法，根据这一方法设计的透水性沥青面层具有良好的路面使用功能，应用前景广阔。     

Interfacial activity and rate of palladium(II) extraction with decyl pyridine monocarboxylates

Decyl isonicotiniate and decyl nicotiniate permit a rapid extraction of palladium(II) from its hydrochloride solutions. Decyl picoliniate is not a suitable extractant. 4-Octylphenylamine can act as a phase transfer catalyst when its concentration in the organic phase is at least 2·5 × 10^?4 M . It seems that the interfacial adsorption of pyridine carboxylates and of 4-octylphenylamine is not the decisive phenomenon in palladium(II) extraction. The negligible protonation of the pyridine-type extractants and the phase transfer catalysis explains well the quick extraction of palladium(II) with the commercial and highly hydrophobic extractant ACORGA CLX-50.     

InGaAsP／InP PFBH激光器

采用Ｎ－ＩｎＰ衬底研制ＩｎＧａＡｓＰ／ＩｎＰ激光器和ＤＦＢ激光器在国内已报导过多次，本文介绍用Ｐ－ＩｎＰ衬底研制ＩｎＧａＡｓＰ／ＩｎＰ平面埋层异质结构激光器和ＤＦＢ－ＰＦＢＨ激光器，同时利用晶体生长和晶向的依赖关系，改进埋区的结构，使器件最高激射温度大于１００℃。     

利用分形几何确定多孔介质的孔尺寸分布

提出了利用分形几何确定多孔介质孔尺寸分布的方法。考虑多孔介质中孔间的屏蔽，采用此方法得到的孔尺寸分布范围比采用平行孔模型宽，分别采用本方法和平行孔模型测定γ－Al2O3催化剂的孔尺寸分布，构造简单立方体三维网络模型模拟压汞过程，并将模拟曲线与γ－Al2O3压汞实验曲线比较，结果表明，采用本方法所得孔尺雨分布优于平行孔模型所得孔尺寸分布。     

Dielectric behaviour of glasses and glass ceramics in the system BaO-PbO-TiO2-B2O3-SiO2

Glasses with varying molar ratios of PbO/BaO in the system BaO-PbO-TiO₂-B₂O₃-SiO₂ were prepared keeping (BaO + PbO)/TiO₂ ratio equal to one. The glasses were ceramized by two-stage heat treatment. X-ray diffraction indicates that PbTiO₃ crystallizes in lead-rich glasses while BaTiO₃ precipitates in barium-rich compositions. Solid solution (Ba, Pb)TiO₃ does not seem to crystallize over the entire range of compositions. Simultaneous presence of PbO and BaO in the initial glass composition reduces the yield of ferroelectric phase. Dielectric properties have been interpreted in terms of microstructural features.     

汽油机爆震强度的分析

分析了汽油机缸内气体爆震燃烧压力的频率特性并推导了爆震压力共振频率计算公式。研究表明：在爆震工况下，缸内压力在高频域中有几个共振峰，峰的大小表明了汽油机爆震强度。汽油机的表面振动在这些共振频率峰处也出现相应振动峰。表面振动峰与缸力压内峰值近似成正比。汽油机表面振动峰值可作为爆震强度的评价指标，该结论在ＣＡ１１０２汽油机上得到了证实。     

焊前处理方式对LF6铝合金扩散焊的影响

利用Ｇｌｅｅｂｌｅ－１５００热／力模拟试验机，研究了ＬＦ６铝合金的扩散焊工艺，通过对焊接温度、压力、时间的调整和选用不同的料前处理方法，确定了最佳的扩散规范，研究结果表明：在一定的温度和时间范围内，ＬＦ６５铝合金扩散焊接头的剪切哟度随焊接温度和时间的增加而提高；化学浸蚀法比机械打磨法能更有效的去除铝合金表面的氧化膜；在现有试验条件下，得到ＬＦ６铝合金扩散焊的最佳规范参数，搭接试扩散焊接头的剪切强度     

折反光学系统最佳红外像面位置的研究

较深入地研究了折反光学系统的红外像面,为确定实际的红外像面提出了一个新方法—计算从可见光边缘无色的弥散圆到红外最佳像面的距离。实践证明,这是确定这类光学系统最佳像面的一个方便、可靠的方法。