IF钢冷轧及再结晶初期微观组织的TEM研究

采用透射电子显微镜对不同压下量和再结晶初期的IF钢样品进行了研究．结果表明：无论是在较小形变量下还是在较大形变量下，形变不均匀性是普遍存在的；冷变形程度不同，织构组分不同，TEM形貌也不同；在再结晶的最初期，冷轧的形变组织演变为近乎等轴的亚晶，优先形成{111}〈uvw〉取向的晶核，晶核逐渐吞并周围的形变基体而长大，最终形成再结晶γ-纤维织构．     

Behaviors of concrete-filled steel tubular members subjected to combined loading

The present study is an investigation on the behaviors of concrete-filled thin-walled steel tubular members subjected to combined loading, such as compression and torsion, bending and torsion, compression, bending and torsion. ABAQUS software is used in this paper for the finite element analysis (FEA). A comparison of results calculated using this modeling shows generally good agreement with test results. The FEA modeling is then used to investigate the influence of important parameters that determine the ultimate strength of the composite members under combined loading, such as compression and torsion, bending and torsion, compression, bending and torsion. The parametric studies provide information for the development of formulae for calculating the ultimate strength of the composite members subjected to combined loading.     

Ennoblement of stainless steel in natural seawater – A new explanation

The ennoblement of corrosion potential (E_corr) of passive metal immersed in seawater was investigated with electrochemical technology and epifluorescence microscopy. The in situ observation showed that the bacteria number increased on the metal surface according to an exponential law which was in the same way with the ennoblement of E_corr. At the same time, the anodic polarization current of high‐Mo stainless steel decreased in the initial days. According to the mix‐potential theory and the characteristics of polarization curves of high‐Mo steel in natural seawater, the ennoblement of corrosion potential may be induced by the decrease of the passive current density.     

Cr对低碳Si-Mn系TRIP钢组织与力学性能的影响

主要研究了Cr对低碳Si-Mn系TRIP钢组织与力学性能的影响。首先利用Formastor-F型膨胀仪测定了含Cr和不含Cr两种低碳钢的连续冷却转变(CCT)曲线,分析指出了Cr对连续退火工艺的潜在影响;然后采用Gleeble-3800热/力模拟试验机对两种钢的薄板试样进行了连续退火模拟实验,并通过拉伸试验测定了力学性能;最后采用金相、扫描电镜、X-射线衍射分析等技术考察分析了两种钢的显微组织。结果表明:含Cr的TRIP钢的组织比较细小,铁素体晶粒近似等轴分布;两种TRIP钢的残余奥氏体含量相近,但含Cr钢的残余奥氏体中的含碳量较高。分析认为这是由于含Cr钢在热轧阶段较易生成细小的组织,而在热处理阶段则抑制贝氏体的生成,最终获得稳定的残余奥氏体。     

反应器和钢烟囱整体吊装的难点和对策

介绍了在金陵石化炼油厂200万t/a柴油加氢装置建设中,将质量为237t的反应器和高60m的钢烟囱成功进行整体吊装过程中的关键技术.通过此项工程实践得出以下结论象钢烟囱这样细长重物的整体吊装,由两台吊车抬立起后,再由主吊车独立吊装就位的施工方法简单易行,安全可靠,应用范围广;结构复杂细长杆的吊装强度和挠度计算比较复杂,在计算过程中可以忽略部分次要件的质量,分别以两吊点为支点计算上下吊点所受的力,然后再按比例放余量,使两吊点受力之和等于细长杆的重力,计算挠度时,可以适当地把问题夸大化,从而建立近似的力学模型;高压厚壁重型容器的吊装,宜直接设置专门吊盖与大法兰用螺栓把紧起吊;施工现场地基坚实是保证吊车站位和吊装施工的前提条件.     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

SLIMLINE+K型多功能撬装双滚筒试井绞车简介

SLIMLINE K型多功能撬装双滚筒试井绞车为整体式结构，多用于海上平台，可进行电子压力计和机械压力计试井，以及井下工具的投放、震击、打捞等完井作业。该试井绞车采用先进的数控技术，使起下纲丝／电缆实现自动化控制，该系统能够对斜井、定向井进行随钻测试。     

珠钢不锈钢冶炼技术探讨

本文阐述了不锈钢冶炼的关键技术，为生产准备提供帮助。     

乳化型轧制液的质量标准研究

对国内目前所使用的冷轧薄钢板(汽车钢板)轧制液母液和乳化液的质量指标及常用试验评定方法进行了考察，并对产品的性能要求进行了研究与分析，制订出一套标准以供参考，包括乳化液稳定性、润滑性、防锈性、抗泡性、使用周期及粘度、闪点等性能。     

IF板与08Al板的成形性能研究

通过模拟成形性试验，对新型超深冲用IF钢板和传统冲压用08Al钢板的冲压成形性能进行了研究．结果表明：IF板的拉深性能、扩孔性能、胀形性能以及“拉深-胀形”复合性能等均优于08Al板，其中，扩孔性能和平面各向异性的改善最为显著；各项试验中，IF板的成形力普遍小于08Al板。