高温型Mo-Al2O3金属陶瓷的研制

将Mo与Al2O3粉体按摩尔比为0．3、0．4、0．5配料，混合均匀后通过粉末冶金法制成3种Mo-Al2O3金属陶瓷试样。在1800℃，2h氢气气氛中烧结后，试样的气孔率随Mo含量的增加呈降低趋势，而强度呈增加趋势。同时，随Mo含量增加，金属陶瓷中Al2O3的晶粒尺寸减小，Mo的形态从以弥散状为主转变为以连续状为主。研制的高温型Mo-Al2O3金属陶瓷测温套管（金属与陶瓷摩尔比为0．4）在真空或N2保护条件下测量高温合金熔液温度时，平均使用寿命达到100次。     

Hot carrier magnetophonon spectroscopy of semiconductors in high magnetic fields up to 40 T

Hot carrier magnetophonon resonances of n-type Si, short channel InP and p-type InSb were investigated in pulsed high magnetic fields up to 40 T. Using a recently developed high resolution technique in pulsed high fields, many new features of the hot carrier-phonon interactions in high magnetic fields were found.     

Shape-Controlled Synthesis and Upconversion Luminescence of Y2O3:Yb, Er Microstructures

The Y2O3: Yb3 , Er3 microstructures were fabricated by a hydrothermal method without surfactants.The microstructures structure was characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM,KYKY 1000B).The up-conversion luminescence spectra were studied under 978 nm laser diode excitation.In Yb3 and Er3 codoped Y2 O3 microcrystals, the relative intensity of green emission became stronger as the morphology of sample changed from wires to films.     

棕刚玉粉中Al2O3含量分析方法的探讨

对耐火材料——棕刚玉粉的质量分析控制，提出了用实用性的检测方法测定其Al2O3含量。通过与国家标准分析方法的对比试验，证实快速实用分析方法测定棕刚玉粉中Al2O3含量是可行的。     

IPv6 delay and loss performance evolution

Although packet delay and loss are two important parameters of the Internet performance, to the best of our knowledge, the evolution of large‐scale IPv6 delay and loss performance has previously not been studied. In this paper, we analyze more than 600 end‐to‐end IPv6 paths between about 26 testboxes of RIPE Network Coordination Centre over two years, and compare the delay and loss performance over time with their IPv4 counterparts. We present and discuss the measurement methodologies and show that IPv6 paths have a higher delay and loss than their IPv4 counterparts. The main reason for the worse performance stems from IPv6‐in‐IPv4 tunnels rather than from native IPv6 paths and such tunnels are still widely used today. Copyright © 2007 John Wiley & Sons, Ltd.     

我国的锑深加工产品

介绍了目前我国锑深加工产品的种类、用途、主要生产厂家 ,以及某些产品的生产工艺和质量状况。并针对国内锑品现状 ,提出了几点建议     

Hydriding and Dehydriding Characteristics of Mechanically Alloyed LaMg_(17) Ni Composite Material

Magnesiumandmagnesiumalloyshavebeenin vestigatedashydrogenstoragematerialsforseveralde cadesbecausefarmorehydrogenbyweightcanbestoredinthemthaninmostoftheothercurrentlyknownhydrogenstoragealloys .Moreover ,thehighnaturalabundanceofMg ,itslightmassandenviron mentalcompatibilitypotentiallymakemagnesiumoneofthemostprospectivecandidatesforfuturehydrogenstoragematerials .Unfortunately ,thepracticalappli cationofMganditsalloyshasbeenlimitedonlytocertainstoragedevicebecauseoftheirpoorhydriding dehydr…     

Austenitizing treatment influence on the electrochemical corrosion behavior of 0.3C-14Cr-3Mo martensitic stainless steel

Effects of austenitizing treatment temperatures on aqueous corrosion properties of martensitic stainless steels were investigated by electrochemical tests (potentiodynamic test, potentiostatic test and electrochemical impedance spectroscopy), and surface analyses (optical microscopy and XRD). The results of potentiodynamic test revealed that the breakdown potential increased with the increased austenitizing temperature, indicating increased relative resistance to initiation of localized corrosion. EIS measurements showed that MSS3 (1030 °C) exhibits larger polarization resistance value than MSS1 (970 °C) and MSS2 (1000 °C) at passive and breakdown states. This was caused by decreasing the amount of Cr-rich M₂₃C₆ carbide which acts as preferential sites for pitting corrosion.     

兼容IPv4及IPv6的网络程序设计

介绍了在Window系统中设计兼容IPv4及IPv6的网络程序的方法,并给出了用WinsockAPI编程的具体步骤。     

TiSiW12O40/TiO2催化合成丙酸正丙酯

研究了固载杂多酸盐TiSiW12O40/TiO2催化丙酸与正丙醇的酯化反应，探讨了催化剂用量，反应时间及醇酸摩尔比对酯收率的影响。当醇酸摩尔比为1.3:1，催化剂的量为醇酸总质量的1.5%。反应时间为1.0h，酯产率可达71.4%以上，采用该催化剂合成丙酸正丙酯不仅酯化反应温度低，反应时间较短，催化剂用量少，而且可较好地回收利用，可降低成本；因此，TiSiW12O40/TiO2是合成丙酸正丙酯的优良催化剂，具有良好的应用前景。