Effect of heat treatment on thermal stability of Ti40 alloy

Five new heat treatment processes were designed, which were divided into three groups by their characteristics. The microstructures and mechanical properties of the alloy after the five heat treatments and thermal exposure at 500, 550℃ for 100 h were tested. The results indicate that a little differences exist in the performance of mechanical properties at room-temperature after the five heat treatments, and the thermal stability is the key factor for determining heat treatment process. Among the three groups of heat treatment processes, the best thermal stability is achieved after the first group of heat treatment. After annealing treatment at intermediate temperature, some defects and uneven grain boundaries are remained, which leads to the reduction fractions of precipitations on unit grain boundary and the harmful effect of precipitations on grain boundary is weakened. The process of annealing at 650 ℃for 4 h is recommended the best heat treatment process for Ti40 alloy.     

真空熔炼AZ91镁合金过程中Mg元素的蒸发行为

在真空Ar气氛中熔炼AZ91镁合金，测定了不同精炼温度下Mg元素的蒸发速率。结果表明，随着精炼温度的升高，Mg元素的蒸发量增大。通过计算可知，Mg的蒸气压是Al的10^9倍，是Zn的46倍，因此主要是Mg的蒸发而导致合金其他元素含量升高。XRD分析表明，蒸发物是Mg元素。结合Mg元素的蒸发机制，在该试验条件下推导出Mg元素蒸发率的计算公式以及Mg元素的表观传质系数、蒸发率与精炼温度的关系，计算得出Mg元素蒸发率为0．86×10^-3-1．35×10^3g／cm^2·s，Mg元素的表观传质系数在2×10^-5-24×10^-5cm／s范围内。     

坯料外形对镁合金矩形盒拉深成形的影响

用商业有限元软件模拟了在同一套模具和成形条件下不同毛坯外形的镁合金矩形盒拉深成形过程．依据数值模拟结果，分析了不同坯料外形对镁合金矩形盒拉深成形的影响。结果表明：使用矩形圆角坯料比其他坯料的成形性能好。     

用双层辉光等离子法在钛表面制备的Ti-Pd合金层性能研究

采用双层辉光等离子冶金技术在纯钛表面制备了Ti—Pd合金层。其深度大约为90μm，Pd含量呈梯度变化，并出现了TiPd3，TiPd2，Ti2Pd3，Ti3Pd5，TiPd，Ti4Pd等6种化合物相和Pd相。合金层在100℃的NaCl饱和溶液＋HCl溶液以及40℃的8．6％H2SO4溶液中的耐缝隙腐蚀性能优于Ti0．2Pd合金；在室温80％H2SO4的溶液中，腐蚀速率仅为0．682mm／a，是Ti0．2Pd合金的18．2％：在室温30％HCl的溶液中，表面Ti—Pd的腐蚀速率仅为0．004mm／a，是Ti0．2Pd合金的12．5％。     

铸造金属耐磨材料研究的进展

详细介绍了耐磨材料奥氏体锰钢、低合金钢和白口铸铁的成分、组织、性能及其应用进展,还对耐磨钢结材料和耐磨铸造复合材料以及新开发的高硼铸造耐磨合金进行了评述,期待为科学选择耐磨材料提供参考。     

BNi—2钎焊条的真空吸铸工艺

研究了ＢＮｉ－２钎焊条真空吸铸原理，并由试验得出：当ＢＮｉ－２合金加热到１５００℃，真空控制阀门开口为φ６ｍｍ以上，真空度５０ｋＰａ，铸型预热温度５００℃，并用φ内２ｍｍ×５００ｍｍ石英管进行真空吸铸时，吸铸高度可达到４０ｃｍ以上。     

AlSi7Mg合金半固态压铸件热处理强化机理研究

对AlSi7Mg合金(A356)半固态压铸件和液态压铸件进行了不同工艺的固溶与时效热处理，分析了其显微组织与疏松度，测定了硬度、拉伸强度及延伸率等力学性能。实验得出，铝合金半固态压铸件原始态的力学性能优于液态压铸件，并且半固态压铸件时效强化效果尤其明显，拉伸强度可达330MPa以上，延伸率10％以上。这主要是由于半固态压铸件比液压件具有更加致密，且为球状的非树枝晶组织。铝合金半固态压铸件时效强化，机理主要归于弥散析出Mg2Si强化相。     

变形镁合金熔焊接头组织特征分析

采用光学显微镜、X射线衍射仪(XRD)和电子探针(EPMA)等分析测试手段，对变形镁合金AZ31B的TIG焊接头进行了微观组织观察、相组成和微区成分分析试验。结果发现在熔焊条件下AZ31B镁合金焊缝附近的纤维组织消失，在焊缝区出现了细晶粒，而热影响区(HAZ)的晶粒明显粗大。进一步研究发现焊缝区的晶粒主要呈细小的等轴晶，室温组织是由δ—Mg相和γ—Mg17Al12化合物两相组成。分析还发现焊缝区的Mg含量低于母材，而A1的含量则高于母材；电子探针分析发现Mg、A1、Zn元素存在成分偏析现象。     

Modification effect of pure rare earth metal La on as-cast hypereutectic Al-17%Si alloys

1　INTRODUCTIONImprovedpropertiesandlightweightareincreas inglybecomingthemaingoalsofautomotiveandaerospaceindustries[1] .Forthesakeofachievingthesecharacteristics,manyeffortshavebeenfocusedonaluminumalloysandtheirpropertiesundersevereconditions.Applyingaluminumalloystoautomotivepartssuchaspistons ,cylinderliners ,engineblocksanddifferentpartsofthermalmotors ,combinativeimprovementofthestrengthtomassratio ,wearre sistance,heatresistance ,andlowheatexpansionisanimportantgoal[2 ] .Al Siallo…     

7075铝合金管材挤压成形及对性能影响

对7075铝合金管材挤压成形进行了实验研究，测试了管材挤压成形时挤压力变化规律和变形程度对挤压后管材力学性能的影响规律，指出，7075铝合金管材挤压成形时必须严格控制坯料温度，模具预温度，润滑方式，挤压速度，挤压比等工艺参数。