压力机气垫故障分析

介绍分析了机械压力机气垫通常出现的故障现象，以及应采取的排障措施。     

稀土元素Ce对纯铜导电性及力学性能的影响

在纯铜中加入稀土元素Ce,研究不同含量Ce及不同保温时间对纯铜的导电性、抗拉强度、硬度、耐磨性等的影响.研究发现在纯铜中加入Ce起到净化、去杂质的作用,改善纯铜的导电性;也可使晶粒细化,改善纯铜的抗拉强度及其它力学性能.且熔炼时加入稀土后的保温时间要适当.在试验的条件下保温时间以30 min为宜,稀土Ce的最佳加入量w为0.02%.     

Effects of annealing at high pressure on structure and mechanical properties of Al87Ni7Gd6 metallic glass

The effects of annealing and annealing with a superimposed pressure of 940 MPa on the primary crystallization behaviour of α-Al and the resulting micro-hardness have been studied for as-quenched Al₈₇Ni₇Gd₆ metallic glass. Isothermal annealing experiments were conducted for 30 min at 188 °C, 191 °C, and 205 °C in silicone oil maintained either at atmospheric pressure (i.e. 0.1 MPa) or at 940 MPa. XRD analyses detected the evolution of structure with annealing at 0.1 MPa, while specimens annealed with 940 MPa pressure exhibited sharper diffraction peaks than those annealed at 0.1 MPa. DSC measurements were conducted on the as-received amorphous ribbons as well as ribbons annealed at different temperatures at either 0.1. MPa or with 940 MPa superimposed pressure. Specimens annealed with 940 MPa pressure exhibited higher onset temperatures (i.e. T_x1) and temperatures for the first exothermic peak (i.e. T_p1) for primary crystallization. TEM measurements revealed an increase in the volume fraction of α-Al with increases in annealing temperature, while micro-hardness measurements revealed an increase in hardness with increasing amounts of α-Al. Specimens annealed with 940 MPa pressure exhibited further increases in both the volume fraction of α-Al and resulting micro-hardness.     

非调质钢的合金设计与热加工工艺及性能

论述了非调质钢的性能特点，分析了V、Nb、Ti、Mn、Cr、Si等常用合金元素对非调质钢组织和力学性能的影响，并对热加工工艺、热处理等因素个性能的影响作了分析和讨论。     

利用"正火液"作为高铬铸铁磨球淬火介质的生产实践

高铬铸铁件在没有添加贵重元素的条件下,利用"正火液"配入适量的水作为淬火介质进行了试验和生产.实践证明,产品在热处理淬火时从未发生炸裂现象,同时完全达到了要求的力学性能指标.生产的锤头其使用寿命为高锰钢的6～8倍,为低铬白口铸铁的4～6倍.     

Synthesis and characterization of mechanical-alloyed Ti–xMg alloys

The synthesis and characterization of Ti–xMg (x=4, 9, 12, 15, 21, 24 at%) alloys using mechanical alloying was investigated. A nanometer-sized Ti–24Mg alloy was produced. During mechanical alloying, the height of the XRD peaks of the Mg in the Ti–9Mg alloy decreased, and then disappeared, whereas the Ti XRD peaks broadened, and the grain size decreased with increasing milling time. The Mg firstly dissolved in the grain boundaries of the Ti, and then diffused into the Ti grain interiors. The grain boundaries played an important role in enhancing the solid solubility of Mg in Ti. With increasing Mg content the volume fraction of grain boundaries increased, and a decrease in grain size occurred after mechanical alloying for 48 h.     

PZT／Terfenol-D／PVDF层状复合磁电材料谐振特性

采用热压法制备出二层锆钛酸铅(PZT)／聚偏氟乙烯(PVDF)与1层Tb0.28Dy0.72Fe2(Terfenol-D)／PVDF叠层结构的三元复合磁电材料，研究了不同PVDF含量，以及不同层厚比tp／L对样品的介电常数、介电损耗、电阻率、谐振频率以及磁电转换系数αE33，αE31的影响规律，结果显示PVDF的含量和层厚比都存在最佳值(最佳值出现在产0．5，tp／L=2／7)，并且在这个最佳值处，磁电转换系数达到最大。     

Ti—Al二元合金的成分对组织和力学性能的影响

用金相、扫描电镜和X射线衍射研究了6种不同Al含量Ti-Al二元合金铸态和退火态的组织结构和相组成的特征和变化。从结晶动力学的观点,分析了合金的结晶凝固过程。采用三点弯曲方法研究了合金的抗弯性能同Al含量的关系。结果表明,Al含量为34 wt%,经1100℃/30 h退火的合金抗弯性能最好,Al含量偏离34wt%,都对合金的力学性能不利。     

Detection of water ingress in composite sandwich structures: a magnetic resonance approach

Water ingress inside honeycomb sandwich panels during service has been linked to in-flight failure in some aircraft. There is an ongoing effort to develop nondestructive testing methods to detect the presence of water within the panels. Magnetic resonance (MR) represents an attractive approach in that it is sensitive to moisture. Using a unilateral MR sensor, testing can be applied directly to the surface of the panel. The viability of MR is demonstrated through laboratory imaging of both water within sandwich panels, as well as the adhesive itself. The detection of water using a one-sided handheld MR sensor is presented. It is shown that simple detection, as well as spatial localization of water within sandwich panels is possible.     

丁基罗丹明B-AuI4-缔合纳米粒子体系的极谱猝灭效应研究

在0．1mol／LH2SO4介质中，丁基罗丹明B(RBB)在-0．59伏产生1个单扫描极谱峰。当有AuI^-4存在时，AuI^-4与RBB^ 主要通过静电引力形成疏水性的AuI4—2RBB缔合物分子。AuI4—2RBB存在较强的分子间作用力和疏水作用力而生成紫红色的(AuI4—RBB)n纳米微粒，在470nm处产生1个瑞利散射峰，在610nm处产生1个共振瑞利散射峰；而在-0．59伏处的极谱峰降低。这是由于该紫红色复合纳米微粒形成所致。当纳米微粒体系加入乙醇后，体系的瑞利散射峰和共振瑞利散射峰消失，极谱峰、同步荧光峰和颜色恢复，由于乙醇而致使紫红色的(AuI4-RBB)n纳米微粒分解为红色AuI4—RBB分子。研究结果表明，紫红色(AuI4-RBB)。纳米粒子的形成是其极谱猝灭和共振瑞利散射效应的根本原因。