研究了不同含量的碳纳米管及0.8%稀土Y对高Ni含量Ti(C,N)基金属陶瓷组织性能的影响.将不同成分的试样分别于1400℃、1410 ℃、1420℃真空烧结,测试抗弯强度、洛氏硬度,观察背散射电子形貌、断口形貌并做能谱分析.结果表明,加入质量分数(下同)为0.8%Y及0.3%～1.0%的碳纳米管时,碳纳米管含量为0.5%的组织较均匀,芯壳结构明显,抗弯强度及硬度均较高.     

石墨化率不同的自焙炭块的热膨胀

采用精密垂直拉杆膨胀仪在１４～１０００℃范围内测量了具有不同石墨化率的自焙炭块的相对热伸长量，并由此获得了热线膨胀系数α。结果表明：石墨化率一定时，α值在较低温度下随温度升高而增加，在较高温度下，α值随温度变化不明显；恒温时，石墨化率越高，α值越低。讨论了单位热应力下的弹性模量概念     

土壤中阴离子对碳钢腐蚀的影响

应用弱极化曲线技术和交流阻抗谱研究了土壤中C1-、SO4^2-、CO3^2-、NO3-离子对碳钢腐蚀的影响。结果表明：阴离子对碳钢腐蚀的影响是显著的。当土壤中分别添加Cl-、CO3^2-、NO3-离子时，随着阴离子含量的增大，碳钢的腐蚀速率增大，在某一离子含量时，腐蚀速率达到最大，然后腐蚀速率随着离子含量的增加而减小。在含SO4^2-离子的土壤中随着SO4^2-离子含量的增大，土壤中碳钢的腐蚀速率增大。在有四种阴离子土壤中，阻抗谱均为单容抗弧，且大都在低频区出现扩散弧。     

Spheroidization of medium-carbon steels

Spheroidization experiments were made on a medium- carbon AISI 4037 steel, using both intercritical and subcritical annealing cycles. The results indicate that in the subcritical cycle the spheroidization occurred much more quickly than expected, so that shorter times were sufficient to achieve high formability. On the other hand, the hardness dropped faster in the intercritical cycle. Although more work needs to be done, these results suggest that using a subcritical spheroidization process instead of an intercritical process could achieve considerable savings in time, energy, and cost.     

不同活化剂对石油焦基活性炭孔结构的影响

以石油焦为原料 ,Na OH,KOH和 Na2 CO3 为活化剂制备活性炭 ,采用氮气吸附考察了不同活化剂对活性炭的比表面积、中孔和微孔孔径分布、孔容积及平均孔径等孔结构的影响 .结果表明 :KOH活化制备的活性炭包含 1 nm的微孔和 4nm的中孔 ,总孔容 0 .648cm3 /g,比表面积大 ;Na OH制备的活性炭以 1 nm的微孔为主 ,占总孔容 ( 0 .1 65 cm3 /g)的 98% ,平均孔径 1 .83nm;Na2 CO3 制备的活性炭以 4nm的中孔为主 ,占总孔容 ( 0 .1 43cm3 /g)的 68.5 % ,平均孔径 3.42 nm,比表面积小 .3种样品的孔径都呈现出多峰分布特征 .KOH和 Na2 CO3 活化制备的活性炭的 N2 吸附脱附曲线属于 型 ,Na OH活化制备的活性炭吸附脱附曲线属于 型 .     

Influence of volatile matter and deposited carbon on coke yield from coals

The relations between coke yields and the volatile matter content of 30 individual and 30 blended coals were investigated. Coke yields and deposited carbon related to volatile matter content can be expressed in the following equations: CY (%) = 97.89?0.86 VMch+VMc; and DC (%)= ?2.24+0.16 VMch; where: CY=real coke yield; VMch = volatile matter content of charging coal; VMc=volatile matter content of coke, and in the case of <2%; DC = deposited carbon. The test results show excellent correlation with practice.     

活性炭吸附法处理麦麸膳食纤维废水的研究

采用活性炭吸附的方法来处理麦麸膳食纤维废水。实验结果表明,当活性炭的投入量为160 g/L,接触时间为20 m in,温度为55℃,pH值在小于5的条件下能有效处理该废水,CODC r的去除率最高达96.89%,BOD5的去除率最高达96.61%。     

High resolution XPS characterization of chemical functionalised MWCNTs and SWCNTs

High resolution XPS analysis of chemical functionalised multi-wall carbon nanotubes (MWCNTs) and single wall carbon nanotubes (SWCNT) was done with ESCA300 (overall instrument resolution of 0.35 eV). Information to the degree of functionalisation was ascertained by argon ion bombardment of the samples followed by XPS analysis to detect the functional groups, the percentage atomic concentration of various elements present and whether or not the detected functional groups imposed a chemical shift on the CNT atoms. The results show that true chemical functionalisation was achieved and by argon ion bombardment these functional groups can be altered relative to the C 1s carbon atoms of the CNT. The choice of chemicals used for functionalisation, the techniques employed and the types of nanotubes treated are important factors in chemical characterisation. The carbon atom on the nanotube ring to which the functional group (atom) is bonded, the chirality of the CNT, the electronegativity of the functional group, the bond type and whether the CNT is single-wall or multi-wall, or cut (short) could play a role in determining the chemical shift on the CNTs atoms. These investigations are relevant to chemical functionalisation of carbon nanotubes for various applications for example DNA sensors and other biomedical sensors.     

活性炭对含铬废水的吸附处理研究

研究了活性炭吸附处理实验室模拟含铬废水。实验结果表明,当活性炭用量为1 g,废水pH=4~5,吸附接触时间大于1 h,活性炭与铬含量比值大于5 mg Cr6+/g活性炭时,处理效果可达99%以上;吸附符合Freund lich等温模式,吸附等温方程式为logq=0.7780+0.9716 logc,以物理吸附为主;吸附穿透体积为25 mL,活性炭吸附Cr6+的工作吸附容量为14.59 mg Cr6+/g活性炭,工作饱和吸附容量为803.41 mg Cr6+/g活性炭。