Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.     

Relationship between the adhesion properties of UV-curable alumina suspensions and the functionalities and structures of UV-curable acrylate monomers for DLP-based ceramic stereolithography

Digital light processing (DLP)-based ceramic stereolithography has attracted significant attentions due to the high printing speed and high dimensional accuracy of DLP printers. However, undesired dropping of unfinished ceramic parts during printing, owing to inadequate adhesion between the first cured layer and the substrate of the building platform, still remains a challenge. In this study, the relationship between the adhesion properties of ultraviolet (UV)-curable alumina (α-Al₂O₃) suspensions and the functionalities and structures of UV-curable acrylate monomers was investigated. With an increase in the proportions of monofunctional monomers, the adhesion abilities of UV-curable alumina suspensions enhanced because of reduced volume shrinkage, however, inferior curing performances were observed due to a decrease in the double bond densities. Furthermore, the large-volume branched chain structures in monofunctional monomers and ethyoxyl groups in polyfunctional monomers effectively decreased the volume contraction, improving the adhesion performances of UV-curable alumina suspensions and facilitating the conversion of double bonds to provide excellent curing properties, further guaranteeing strong adhesion of these suspensions to the substrate.     

Copper–4,4′-dipyridyl coordination compound as solid reagent for spectrophotometric determination of reducing sugar employing a multicommutation approach

In this work a multicommuted flow system employing copper–4,4′- dipyridyl coordination compound as the solid-phase reagent for the spectrophotometric determination of reducing sugar was developed. The coordination compound was synthesized through a reaction of the 4,4′-dipyridyl and copper (II) nitrate, under hydrothermal conditions. The complex was characterized by infrared spectroscopy (FTIR), power X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and thermogravimetric analysis (TGA). Based on the characterization, a multicommuted spectrophotometric procedure for the determination of reducing sugar using copper (II) complex as solid reagent is proposed. The proposed method was based on the redox reaction between a monosaccharide, such as fructose and glucose (reducing sugar) and Cu(II). This reaction, mediated in an alkaline medium, produces a yellow compound that can be determined by absorption electronic spectroscopy (λ_ABS = 420 nm). Under optimum experimental conditions, a linear response ranging from 1.0 to 20.0 g L⁻¹ (R = 0.9978 and n = 5), a detection (3σ criterion) and quantification (10σ criterion) limit estimated at 0.23 and 0.75 g L⁻¹, respectively, a standard deviation relative of 4.7% (n = 7), for a reference solution of 10.0 g L⁻¹ reducing sugar, and a sampling rate of 75 determinations per hour were achieved. The proposed system was applied to the determination of reducing sugars in coconut water and juices. The analysis of ten samples and the application of the t-test to the results found, and those obtained using reference procedures (AOAC), provided no significant differences at a 95% confidence level. This system enabled the analysis of reducing sugar with ease and simplicity, providing a significant economy of the solid reagent (600 μg per determination) and reducing effluent generation.     

A new perspective of co-doping and Nd segregation effect on proton stability and transportation in Y and Nd co-doped BaCeO3

Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO₃ (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO₃ at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO₃ in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains.     

A novel Ag–CuAlO2 sealant for reactive air brazing of 3YSZ and AISI 310S

Based on reactive air brazing (RAB), we designed a new type of sealant (Ag–xCuAlO₂) for joining 3 mol.% yttria-stabilized zirconia (YSZ) ceramics and AISI 310S stainless steel. The CuAlO₂ content affected the wettability of the sealant on the YSZ surface, and the joints had a high shear strength when Ag–2 wt.%CuAlO₂, which had a small contact angle on the YSZ substrate, was used as the sealant. In addition, the thickness of the oxide layer was reduced compared to that for the Ag–CuO sealant. The effects of the processing parameters on the microstructure and shear strength of the joints were investigated, and the as-brazed joints reached their highest shear strength (93.7 MPa) when brazed at 1040 °C for 30 min. After high-temperature oxidation at 800 °C for 200 h, the shear strength of the joints remained at 50 MPa, and no apparent change in the microstructure was observed, proving that the joints possessed excellent oxidation resistance.     

DC conductivity and AC impedance of Mn doped magnesia alumina spinel (MgAl2-2xMn2xO4) over a large temperature range

MgAl_2-2xMn_2xO₄ (MAMO) with x = 0-0.12 was synthesized in a single-phase form by solid-state reaction. XRD analysis showed that the samples had the cubic center structure of the Fd-3 m space group. Electrical properties of the samples were studied over the temperature range of 300 K∼1073 K. The results showed that the DC conductivity (σ_DC) increased from 10⁻¹¹S/cm at 300 K (MAMO, x = 0) to 10^-3S/cm at 1073 K (MAMO, x = 0.12). The equivalent circuit of the complex impedance spectra suggested that the relaxation of charge carriers was of non-Debye type. The conduction was mainly caused by grain boundaries and the capacitance was mainly attributed to polarization. The complex permittivity values (ε’ and ε’’) were increased by two orders of magnitude with the increase in Mn content and temperature over the measured frequency range (1 Hz-1 MHz). Therefore, doping with Mn could be applied to modify the electrical properties of MAMO at high temperature.     

Rare-earth free sensitizer in NaLuCrF4:Er upconversion material

Upconversion phosphors are known as a material system that can convert near-infrared light into visible/ultraviolet emissions by sequentially absorbing multiple photons. The studies on upconversion materials often use two rare earth (RE) ions as a sensitizer-activator pair. We investigated the influences on luminescence intensity depending on Cr-doping content (x) of hexagonal NaLu_0.98–xCr_xF₄Er_0.02 (x = 0–0.9) upconversion material by substituting Lu³⁺ ions with Cr³⁺in the absence of Gd³⁺. The change in upconversion luminescence intensity appears with saddle-like shape. We suggest that Cr³⁺ ions play the dual role as a constituent in host lattice and a sensitizer in the upconversion process. Optimal conditions for gaining the strongest upconversion emission correspond to x = 0.3–0.5, where there are effective energy transfers between Cr³⁺ and Er³⁺ ions and CrEr dimers. Apart from these values, the emission intensity decreases rapidly which can be ascribed to the absence of multiple-photon absorption for the case of low Cr³⁺ contents, and to the coupling between Cr³⁺ and/or Er³⁺ ions for the case of high Cr³⁺ contents. Magnetization and electron-spin-resonant measurements were performed to understand the correlation between the optical and magnetic properties.     

Damage tolerance in additively manufactured ceramic architected materials

Technical ceramics exhibit exceptional high-temperature properties, but unfortunately their extreme crack sensitivity and high melting point make it challenging to manufacture geometrically complex structures with sufficient strength and toughness. Emerging additive manufacturing technologies enable the fabrication of large-scale complex-shape artifacts with architected internal topology; when such topology can be arranged at the microscale, the defect population can be controlled, thus improving the strength of the material. Here, ceramic micro-architected materials are fabricated using direct ink writing (DIW) of an alumina nanoparticle-loaded ink, followed by sintering. After characterizing the rheology of the ink and extracting optimal processing parameters, the microstructure of the sintered structures is investigated to assess composition, density, grain size and defect population. Mechanical experiments reveal that woodpile architected materials with relative densities of 0.38–0.73 exhibit higher strength and damage tolerance than fully dense ceramics printed under identical conditions, an intriguing feature that can be attributed to topological toughening.     

Effect of Ni/tubular g-C3N4 on hydrogen storage properties of MgH2

Additive doping is one of the effective methods to overcome the shortcomings of MgH₂ on the aspect of relatively high operating temperatures and slow desorption kinetics. In this paper, hollow g-C₃N₄ (TCN) tubes with a diameter of 2 μm are synthesized through the hydrothermal and high-temperature pyrolysis methods, and then nickel is chemically reduced onto TCN to form Ni/TCN composite at 278 K. Ni/TCN is then introduced into the MgH₂/Mg system by means of hydriding combustion and ball milling. The MgH₂–Ni/TCN composite starts to release hydrogen at 535 K, which is 116 K lower than the as-milled MgH₂ (651 K). The MgH₂–Ni/TCN composite absorbs 5.24 wt% H₂ within 3500 s at 423 K, and takes up 3.56 wt% H₂ within 3500 s, even at a temperature as low as 373 K. The apparent activation energy (E_a) of the MgH₂ decreases from 161.1 to 82.6 kJ/mol by the addition of Ni/TCN. Moreover, the MgH₂–Ni/TCN sample shows excellent cycle stability, with a dehydrogenation capacity retention rate of 98.0% after 10 cycles. The carbon material enhances sorption kinetics by dispersing and stabilizating MgH₂. Otherwise, the phase transformation between Mg₂NiH₄ and Mg₂NiH_0.3 accelerates the re/dehydrogenation reaction of the composite.     

Characterization of anisotropic gas permeability and thermomechanical properties of highly textured porous alumina

Porous alumina with a highly textured microstructure was fabricated by pulse electric current sintering (PECS) using alumina platelets. Highly oriented porous alumina with a porosity of 3%–50% was obtained by a pressure-controlled method of PECS. The properties of the highly textured porous alumina were measured in two directions. The nitrogen gas permeance and thermal conductivity at room temperature were higher in the direction along the platelet length due to the higher continuity of pores and the connectivity of alumina platelets, respectively. The anisotropy of the thermal conductivity at room temperature was investigated and explained by the effect of grain size of platelets as well as morphology and orientation of pores. The bending strength was higher with the loading direction along the platelet thickness. The thermal shock strength was clearly different in the two directions. The difference in the thermal shock strength was investigated by the measurement of properties and thermal stress analysis.