新型可见光固化口腔正畸粘合剂研制

介绍了一种新型可见光固化正畸粘合剂的组成、性能及正畸粘接的工艺。此粘合剂由一种单组分液体底胶和单组分糊剂组成。与化学固化粘合剂相比,其操作使用方便,固化时间短。这种新型粘合剂的粘接强度完全满足了正畸粘合剂的要求。     

支化型水性聚氨酯胶黏剂的合成及性能

采用异佛尔酮二异氰酸酯(IPDI)、聚四氢呋喃醚二醇2000(PTMG2000)为原料,二月桂酸二丁基锡、1,4-丁二醇和2,2-二羟甲基丙酸分别为催化剂、小分子扩链剂和亲水单体,制得水性聚氨酯预聚体(PPU);接着以丙烯酸甲酯、二乙醇胺和三羟甲基丙烷为原料合成了超支化聚(胺-酯)(HPAE);最后制备出不同HPAE含量(以IPDI与PTMG2000的总质量为基准,下同)的支化型水性聚氨酯(WPU)胶黏剂.采用FTIR和1HNMR对HPAE及胶黏剂的结构进行了表征;通过TGA、多功能材料试验机考察了胶膜的热力学性能和机械性能.结果表明,HPAE用量为IPDI与PTMG2000的总质量的1.0％时,制备的WPU2乳液及胶膜综合性能较好,其乳液固含量为33.67％,胶膜吸水率为11.22％,水接触角为90.32°;胶膜机械拉伸强度为10.33 MPa,断裂伸长率为533.73％;其粘结性能良好,剥离强度为4.063 N/mm.     

纸塑复膜胶的研究进展

介绍了双组分聚氨酯、SBS、EVA、聚丙烯酸酯等几种纸塑复膜胶的特点、性能和改性方法，指出水基化、高固含量及复膜胶的改性将是纸塑复膜胶的发展方向。     

高强度聚乙烯纤维绳索的制备研究

研究了纤维的捻度及浸胶处理对超高相对分子质量聚乙烯 (UHMWPE)纤维力学性能及摩擦磨损性能的影响。结果表明 ,UHMWPE纤维的断裂强力随着纤维捻度的增加而减小 ,纤维浸胶处理后的断裂强力增大 ;当UHMWPE纤维中改性氯丁胶粘剂或聚氨酯胶粘剂的含量为 6%时 ,其断裂强力分别增加 17.2 %或 13 .9% ,聚氨酯胶粘剂处理过的UHMWPE纤维的耐摩擦磨损性能最好。     

CR244粘接型粉末氯丁橡胶的制备

用凝聚法制备出粉末粘接型氯丁橡胶(PCR244)。研究了包覆剂性质对PCR244粒径分布的影响，并用SEM对所得PCR244的形貌及断面进行了观察分析。研究表明，在CR244粉末化体系中，包覆剂必须具有一定的交联程度才能起粉末化作用。在研究范围内，包覆剂的θg对粒径小于0．9mm产物的成粉率几乎无影响，均达到98．6％以上。SEM分析表明，PCR244宏观粒子表面粗糙，粒子内外均分布着大量空隙，其形成过程可分为三个主要阶段，即在包覆剂作用下，首先由胶乳初级粒子聚结成次级粒子，再由次级粒子凝聚成团粒，最后团粒相互结合成宏观粒子PCR244。     

葡萄糖对苯二酚树脂胶粘剂的合成

以葡萄糖代替甲醛,在碱性条件下合成了葡萄糖对苯二酚树脂胶粘剂。利用红外光谱(IR)及热重分析(TGA)对树脂的结构及热稳定性进行了分析,并通过正交实验获得了该树脂合成的最佳反应条件:pH=13,n(葡萄糖)n∶(对苯二酚)=101,∶反应温度110℃,催化剂用量2.0%,反应时间7h;同时对树脂的固化条件进行了系统研究。     

橡胶与金属的硫化粘接

本文综述了橡胶与金属粘接体系的发展现状，并对粘接性能的影响因素研究进行了归纳。     

Dynamic Mechanical Properties and Adhesive Strengths of Emulsion Polymer by Power Feed Technique, I

Dynamic mechanical properties and adhesive strengths of power feed copolymer and random copolymer synthesized using styrene or methyl methacrylate and n-butyl acrylate were investigated. Although the two systems were synthesized from the same raw materials, power feed copolymer had a very broad transition compared with random copolymer. This fact was explained by the fact that the system synthesized through power feed method was an alloy of copolymers which are a continuous series from monomer A rich copolymers to monomer B rich copolymers. The dynamic mechanical behavior of film cast from solution was almost the same as that of emulsion film, which indicated more extensive application of power feed copolymer. In the P(nBA/St) system, power feed copolymer maintained its adhesive strengths over a wide temperature range compared with random copolymer. The absolute value, however, was not so high. This was due to the low cohesive strengths of the films.     

水基(乳液)胶粘剂微生物污染及其罐内防腐效果测试

对广东省部分水基(乳液)胶粘剂生产企业微生物污染的来源和种群进行了调查,建立以微生物攻击挑战性试验来快速判定水基(乳液)胶粘剂罐内防腐效果的评价方法,探索该类胶粘剂微生物污染的有效防治技术。     

阳离子型双子表面活性剂的合成及表面活性

合成了一种季铵盐型双子表面活性剂Gem in i 12-3-12,采用红外光谱、元素分析和两相滴定法对其结构和纯度进行了分析,测定了不同浓度表面活性剂水溶液的表面张力,并得到临界胶束浓度(CMC)、饱和吸附量(Γm ax)、单分子饱和吸附面积(Am in)。结果表明,Gem in i 12-3-12的收率为77.2%,纯度为98.4%,它与相应的单尾基十二烷基三甲基溴化铵(DTAB)的表面活性相当,但CMC比DTAB低14倍左右。