采用DSC和FTIR对木材和API胶粘剂间反应的研究

采用差示扫描星热法(Differential Scanning Calormelry,简称DSC)和傅立叶变换红外吸收光谱(Fourier Transform Infrared Spectroscopy,简称FTIR)对木材和水性高分子异氰酸酯胶粘剂(Aqueous Polymer Isocyanate,简称API)的胶接机理进行了研究。DSC和FTIR的试验结果均表明:API胶粘剂和木材间发生了化学反应:API胶粘剂和木材间发生的反应所需活化能远小于API胶粘剂的主剂+固化剂的活化能,亦即用API 胶粘剂胶接木材时发生的反应要比API胶粘剂本身的固化反应容易得多,同时从理论上证明使用API胶粘剂胶接木材时装配时间最长不应超过其活性期的一半时间,且装配时间越短越好;文中还研究了升温速率对API胶粘剂DSC图谱的影响。     

秸秆黄腐酸包膜尿素在水稻上的应用效果

在石灰性土壤上进行田间小区试验，结果表明，秸秆黄腐酸包膜尿素能满足水稻生长最大效率期对营养的要求，有利于有效穗的分化，提高结实率。等氮量试验平均增产9．6％，等重量试验平均增产7．4％。     

用栲胶的新型木工胶粘剂的研制

介绍了以栲胶为原料代替苯酚制木工胶粘剂的新工艺 ,研制出的新型木工胶粘剂各项指标均达到 2BG 390 0 2 - 86FQ -H酚醛树脂的标准 ,应用于胶合板的生产中 ,各项指标均达Ⅰ类板标准 (GB 984 6 - 88)。     

环氧化SBS胶粘剂的研制

研究了环氧化SBS橡胶胶粘剂的合成及应用。试验结果表明环氧化SBS胶粘剂在粘接极性材料时的性能要优于SBS胶粘剂。     

四种环氧胶粘剂耐腐蚀性能研究

环氧树脂胶粘剂经常在腐蚀环境中使用,因此其耐蚀性能的研究就显得格外重要。配制四种不同的胶粘剂,测试其耐蚀性。腐蚀试验采用机油、NaOH水溶液、NaCl水溶液和HCl水溶液做腐蚀介质,测试腐蚀后的胶粘剂的拉伸剪切强度,通过与未腐蚀的胶粘剂的拉伸剪切强度比较,研究在不同介质中,不同组分的加入对胶粘剂耐腐蚀性的影响。推荐了具有较好耐介质腐蚀的环氧树脂纳米胶粘涂层的最佳配方,为其在胶粘剂领域推广应用积累基础数据。     

HT-730改性酚醛-丁腈胶粘剂的研制

对酚醛-丁腈胶粘剂进行改性，添加5．0％的硅烷偶联剂，改善了酚醛-丁腈胶粘剂的工艺性能，提高了粘接强度，特别是降低了酚醛-丁腈胶对环境湿度的敏感性。研制的HT-730胶在环境湿度90％时仍有很高的粘接强度，同时老化性能和适用期并没有受到影响。     

Dynamic Mechanical Properties and Adhesive Joint Strengths of Emulsion Polymers Produced by Power Feed Technique. III. Adhesive Joint Strengths of Grafted Power Feed Copolymer

Power feed copolymers were synthesized using styrene and n-butyl acrylate through non-uniform feeding emulsion polymerization. Poly(vinyl alcohol) (PVA) was used as a protective colloid, onto which vinyl monomers were grafted. Power feed copolymer had a very broad glass transition temperature compared with random copolymer, even if grafting and/or crosslinking were introduced to the system. This tendency was almost the same as the non-grafted power feed copolymer where only low molecular weight surfactant was used.

Adhesive joint strengths of power feed copolymers were evaluated compared with random copolymers. In the case of usual linear power feed copolymer, the adhesive joint strengths were not higher than those of random copolymer, which was considered to be due to the lower film strengths of the power feed copolymer. Power feed copolymer having grafting showed slightly higher adhesive joint strengths over a wide range of temperatures than random copolymer. When crosslinking was introduced to the system, power feed copolymer showed much higher adhesive joint strengths over a wide temperature range.     

刑事案件现场中微量玻璃的检验及应用

论述了刑事案件现场上微量玻璃检材的组成、提取与包装、检验方法以及在侦破刑事案件中的应用.     

NA—5聚氨酯胶粘剂对金属粘接强度的影响

以ＮＡ－５型氨酯胶粘剂作为金属五ＰＵ弹性胶料之间的胶粘剂，制作钢／ＰＵ橡胶／铝静件。研究了影响制件粘接强度的主要因素，给出了ＮＡ－５最佳粘接工艺。     

高含水率杨木单板室温胶合的脲醛树脂胶研究

在实验室条件下 ,以传统脲醛树脂胶的生产工艺为基础 ,加用氨基取代羧酸类化合物。新配方制得脲醛树脂胶 ,用DSC分析了树脂固化反应热过程 ,对含水率在 12 % -2 0 %杨木单板进行了室温胶合研究