用壳聚糖和粉煤灰对含间甲酚的废水进行吸附处理,考察了壳聚糖的用量、振荡时间、振荡速度以及粉煤灰与壳聚糖的混合比对处理效果的影响.结果表明:在常温下,对于初始质量浓度为56 mg/L的间甲酚,当壳聚糖用量为3 g/L,以170 r/min的转速吸附振荡0.5 h,去除率可达到88%以上;在上述条件下,加入质量比4:1的粉煤灰与壳聚糖混合物5g/L时,间甲酚的去除率可达到91%.     

Internal-corrosion inhibitors for pipelines carrying deaerated heating water

The effect of internal-corrosion inhibitors on heating-system pipelines is investigated. Tests were conducted on a testing device for polarization measurements under conditions corresponding to the Rostov Heat-Supply System. The concentration of OEDP-zinc, which provides a high degree of protection from general corrosion, is determined. The reagent has been successfully incorporated into the Rostov No. 2 TPP. __________ Translated from élektricheskie Stantsii, No. 7, July 2007, pp. 37–43.     

Internal-corrosion inhibitors for pipelines in heat-supply systems carrying water with a high oxygen content

The reliability of heat-supply systems is determined primarily by internal corrosion of the pipelines. The concentration of oxygen in the water exerts a major influence on the corrosion. In systems with a standard oxygen content, OéDF-Zn is a highly effective corrosion inhibitor. However, there are systems in which the quality of deaeration of the make-up water of the heat-supply system is low (or deaeration is nonexistent), and the concentration of oxygen is considerably above the standard value. Classed among these systems, for example, are the HWS systems, which are incorporated into closed heat-supply systems. The oxygen concentration in these systems is analyzed to assess the situation. __________ Translated from élektricheskie Stantsii, No. 6, June 2007, pp. 35–39.     

硫脲树脂对Cu~(2+)吸附性能研究

考察了不同吸附时间、pH值和吸附温度下,聚对苯甲酰基硫脲树脂和聚酯基硫脲树脂对Cu2+的吸附性能影响;并对吸附动力学和热力学进行了研究。     

变压吸附制氧设备真空风机入口压力低分析和处理

介绍了邯钢动力厂真空变压吸附制氧设备的工艺流程,从切换阀本体、电磁阀及仪表气源等方面分析和总结了真空风机入口压力低引起系统联锁停车故障原因,并介绍了相应的处理措施。     

Study on Adsorption Behavior of Rare Earth Complexes on Nanometer-Size Titanium Dioxide with ICP-AES

Inrecentyears ,rareearthelements (REEs)havebeenwidelyusedinfunctionalmaterials ,cata lystsandotherproductsinindustry ,diagnosisreagentsofmagneticresonanceimaging (MRI)inmedicineandsomefertilizersinagricultureespeciallyinChina .However,asaresultoftheirusage ,moreandmoreREEsaregettingintotheenvironment,andalsointohumanbodyviafoodchain[1,2 ] .Itisnotclearwhetherrareearthelementsareessentialforman ,soitisveryurgenttostudythebiologicaleffectofrareearthelementsinhumanhealthandenvironment .Inthes…     

活性炭吸附法脱除加氢催化柴油中的硫化物

采用5种活性炭对加氢催化柴油进行吸附脱硫,通过对活性炭的吸附效果及工艺参数的研究,探索了活性炭吸附脱硫最适宜的工艺条件。实验结果表明,分别选用比表面积为854.97,1 108.61 m2/g,相应微孔平均孔径为0.581 4,0.627 4 nm的活性炭,在粒度为40~80目,流速为0.25 mL/m in,吸附柱高径比为30/1的条件,可将不同原料油中有机硫含量分别从1 354.96,665.50μg/g降至360.40,69.61μg/g,脱硫率分别为73.40%和89.54%;在20~100℃时,随着温度的升高,活性炭吸附脱硫效果增强。     

Copper(II) removal from aqueous solutions by fly ash

The removal of Cu(II) by adsorption on fly ash has been found to be concentration, pH and temperature dependent. The kinetics of adsorption indicates the process to be diffusion controlled. The Langmuir constants have been calculated at different temperatures, and the adsorption has been found to be endothermic (ΔH = 15.652 kcal mol^?1). The maximum removal is observed at pH 8.0, and variation in adsorption with pH has been explained on the basis of surface ionisation and complexation.     

乙炔黑吸附聚合制导电聚苯胺

用乙炔黑吸附化学聚合新工艺制备导电聚苯胺，可保持电导率不变，但转化率和堆密度提高，并明显改善了聚苯胺的颗粒形态和制膜加工性，使由其制备的聚苯胺复合正极膜和固体聚苯胺锂蓄电池的电化学性能得以改进。     

Copper phthalocyanine as corrosion inhibitor for ASTM A606-4 steel in 16% hydrochloric acid

A study based on the corrosion inhibition properties of copper phthalocyanine is described. Coverage degrees of copper phthalocyanine (Cu-phcy) on ASTM-A606-4 steel, obtained by weight loss measurements, were fitted to Langmuir, Frumkin, Temkin and Flory–Huggins adsorption isotherms. A better fit to the Langmuir isotherm was obtained. The polarization curves showed that polarization of both the anodic and cathodic reactions were verified for concentrations higher than 10^–4 M, indicating a mixed type action. Only the anodic reactions were polarized for lower concentrations. At high frequencies the Nyquist diagrams showed one capacitive loop attributable to double layer charging and a small one at intermediary frequencies attributable to the faradaic process of hydrogen evolution. The formation of an adsorbed film was characterized by increasing charge transfer resistance values in the low frequency range for increasing inhibitor concentrations. According to the techniques used in this study, copper phthalocyanines showed a high corrosion inhibiting efficiency for all concentrations.