一种制备插层和无定形高岭土的新方法

利用甲醇钠强烈的夺氢作用 ,介绍了一种制备插层和无定形高岭土的方法。利用XRD为主要检测手段研究了甲醇钠的质量分数、反应温度等因素对反应的影响。结果表明 :在反应温度较低、质量分数较低的甲醇钠溶液中 ,高岭土容易被插层而膨胀 ,反之高岭土的层状结构被破坏而无定形化。红外光谱分析进一步证明了插层和无定形高岭土结构的变化     

Al的添加对Gd-Co合金的影响

用X射线衍射、扫描电镜和磁性测量等方法研究了Al的添加对Gd-Co合金的影响。研究结果表明：在一定范围内掺杂Al导致GdCo2、GdCo5和Gd2Co17晶格常数增大，但仍保持各自的晶体结构；Al的添加使GdCo2和Gd2Co17的居里温度降低，但是对于GdCo2却是先增后减。该结论为寻找新的磁性材料提供了有价值的参考。     

CVD金刚石膜生长过程的Raman分析

采用激光Raman散射分析法对CVD金刚石膜的生长过程进行研究 ,讨论在金刚石膜生长的不同阶段 ,膜内金刚石和非金刚石成分的相对含量及其残余应力的变化情况     

Thermally stimulated shrinkage forces in oriented polymers: 1. Temperature dependence

Temperature dependences of shrinkage forces appearing in oriented polymer samples when heated at constant length were recorded for polycarbonate, polyethylene terephthalate, polyethylene and polypropylene. The influence of various processing conditions on thermally stimulated shrinkage forces is demonstrated. A four-state model is proposed which qualitatively describes the temperature dependences of shrinkage forces in amorphous polymers.     

Rapid determination of the fracture toughness of metallic materials using circumferentially notched bars

Three types of material whose fracture toughness tests were previously performed by using circumferentially notched bars, namely (1) a dual-phase steel with three different morphologies; (2) an Al-Zn-Mg-Cu-wrought alloy; and (3) Al-Si-cast alloys with three different Si contents, were investigated in terms of accuracy and reliability of the testing method. Also, the advantages of using circumferentially notched bars for fracture toughness determination of metallic materials were discussed. With the help of stress concentration factors, which are associated with the bluntness of the notch, correction factors for the fracture toughness calculations are derived. The corrected fracture toughness values are found to be close to the uncorrected ones, implying that the testing procedure is reliable.     

Oscillating Cup Viscosity Measurements of Aluminum Alloys: A201, A319 and A356

An oscillating cup viscometer was developed to measure the absolute viscosities of molten metals. Previous experiments established the capability of the apparatus to characterize the viscosities of molten nickel-based superalloys. However, modifications to the instrument and its theoretical analysis were required for reliable measurements on molten aluminum alloys, presumably due to their lower densities and lower viscosities. The theoretical literature for the fluid flow inside an oscillating cup is reviewed, and a working equation without any correction factor is developed for the improved viscometer. Some design parameters of the viscometer that directly affect the accuracy of viscosity estimation by using the working equation are discussed. A special vertical furnace was adopted to uniformly heat a longer cylindrical sample (10 mm inner diameter and 120 mm length) with a temperature difference of less than 2°C over the sample length. The measuring procedure was also improved to get more accurate motion parameters. It is estimated that the working equation and improved instrument provide an uncertainty of less than 4%. In addition, applications and experimental data are presented for pure aluminum and three aluminum alloys: A201, A319, and A356.     

Electroplating of nickel-cadmium alloys from alkaline solutions

The electroplating of Ni-Cd alloy coatings was carried out from alkaline baths (pH 10). For comparison, electroplating of the parent metals, Ni and Cd, was performed individually under the same conditions. The cathodic current efficiency for codeposition was high and decreased with increasing current density. The codeposition process is an anomalous type of plating with Cd being the preferentially deposited metal. The Ni content in the deposits increased with increasing current density. This increase in Ni content improves the corrosion resistance and microhardness of the deposits. X-ray diffraction analysis showed that the deposits consist of a mixture of Ni, β, γ, γ¹ phases.     

非晶软磁合金的巨磁阻抗效应及应用

近来在ＦｅＣｏＳｉＢ等Ｃｏ基非晶体丝带中现了巨磁阻抗效应，由于在一小的直流纵向偏置场下该效应能使丝带两端的交流电压发生大而灵敏的变化，因而在磁记录头和传顺技术中具有巨大的应用科学潜能，受到各国学者的关注，本文简单介绍了巨磁阻抗效应的来源，并综述了近年来非晶体软磁合金材料的的巨磁阻抗效应及应用的研究进展，文章最后说明了尚待深入解决的问题。     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

氢化非晶硅磷掺杂工艺条件的研究

本文对氧化非晶硅磷掺杂的工艺条件进行了研究，得出掺磷氢化非晶硅的电导率随衬底温度、气体流量、气体压力、射频功率、淀积时间的变化关系，为非晶硅的有效掺杂和器件研究提供了依据。