Thermodynamic state of reinforced interpenetrating polymer networks

The free energies of mixing of two networks in the interpenetrating polymer network based on crosslinked polyurethane and poly(ester acrylate) have been determined by the vapour sorption method. It was established that the constituent networks in the IPN are not miscible. The introduction of fillers of different chemical nature increases the compatibility. The thermodynamic affinity of the fillers to the individual networks and IPN was estimated. It was established that when the free energy of interaction of one or both components of the IPN with the filler is negative, reinforcement leads to the formation of a compatible and equilibrium system. For fillers having no affinity to the polymers, compatibilization is observed, which is connected with slowing down of phase separation in the system in the presence of filler.     

中原高温高盐油藏疏水缔合聚合物凝胶调剖剂研究

针对中原油田高温(>80℃)、高盐度(>50 g/L)、高硬度(>1 g/L)砂岩油藏,研制了地下成胶的高热稳定性聚合物凝胶调剖剂。所用聚合物为疏水缔合聚合物AP-P4,M=9.0×106,HD=27%,疏水基摩尔分数0.2%;交联剂为可生成酚醛树脂的3种化合物;调剖剂胶液用矿化度160 g/L的马寨油田污水配制;实验温度95℃。根据形成的凝胶黏度(95℃,1.1 s-1)确定交联剂各组分用量为:MZ-YL 0.429%,MZ-BE 0.060%,MZ-XS 0.012%;酸度调整剂用量0.12%;成胶时间10~15小时。2.5、3.0、3.5 g/L AP-P4的凝胶在95℃老化100天后黏度保持在~40 Pa.s及以上。初配制胶液在3000 r/min下剪切15分钟后黏度降低87.5%~89.0%,但成胶后和老化过程中凝胶黏度只比未剪切样降低17.1%~6.6%。3.5 g/L AP-P4的调剖剂对~1μm2的6支储层岩心的堵塞率在88.1%~95.8%范围,平均93.3%,造成的残余阻力系数在15.2~28.6范围,平均19.8,使渗透率级差2.3~8.0的4组双人造岩心的注水流量比发生不同程度的反转。认为该凝胶调剖剂高温下稳定性好的原因,是强化学交联密度低,因而凝胶脱水收缩作用弱。图2表5参5。     

用两亲聚合物制备大颗粒苯丙乳液

分别以两亲聚合物P(C9-AA)和P(DCPD-St-α-St-AA)作乳化荆，研究了制备大颗粒(约1μm)及具有一定稳定性的苯丙乳液的方法，讨论了乳化剂，温度及引发剂用量对乳液性能的影响。结果表明，以P(C9-AA)作乳化剂时，引发剂用量为单体质量的1．2％，90℃时可以合成性能良好的苯丙乳液；以P(DCPD-St-α-St-AA)作乳化荆时，引发剂用量为单体质量的1．2％，80℃时可以合成性能良好的苯丙乳液。     

凝胶过滤色谱测定高分子量聚乙烯醇分子量和分子量分布

用凝胶过滤色谱对高分子量聚乙烯醇分子量、分子量分布进行剖析。采用Plaquagel-OH色谱柱,0.25mol/LNaNO3,0.01mol/L Na2HPO4-NaH2PO,pH=7的缓冲溶液流动相,流速1ml/min,示差折光检测器,柱温30℃,聚环氧乙烷作标准物。该方法能显著缩短分析时间,提高准确性,可用于对高聚合度聚乙烯醇进行研究和指导生产。     

A novel poly(p-phenylene vinylene)-b-poly(methyl methacrylate) rod-coil diblock copolymer

In this letter, a novel well-defined PPV-b-PMMA rod-coil diblock copolymer, consisting of PPV oligomer as its rod block and PMMA as its coil block, respectively, was prepared via ATRP for the first time. The structure of the copolymer was determined by the measurements of FTIR, ¹H NMR and gel permeation chromatography (GPC). The thermal and optical properties of the copolymers are investigated by DSC, TGA, UV-Vis and photoluminescence (PL) spectra. The results showed that, the introduction of PMMA coil block can improve both the thermal stability and optical properties of PPV oligomer. The highly ordered hexagonally honeycomb-structured film of the copolymer fabricated by vaporizing solvent is also investigated by optical microscope and SEM.     

疏水缔合型聚丙烯酰胺的合成与性能评价

为了提高高相对分子质量的聚丙烯酰胺的抗温抗盐性能,利用自制的两亲表面活性单体与丙烯酰胺共聚合成了疏水缔合型聚丙烯酰胺并进行室内评价。结果表明,在高温、高盐、高钙条件下,合成的疏水缔合型聚丙烯酰胺具有良好的增粘性和较强的热稳定性;克服了疏水缔合型聚合物在盐水中溶解性差的问题,可用各种矿化度的盐水和油田产出污水配制;具有良好的无机盐增粘性能和抗温性能。     

PAN聚合物一次性溶解新技术

阐述了一个全新的聚丙烯腈高聚物溶解理论，取代了以往人们思维中的高聚物大分子必须经过先溶胀再溶解的漫长的静态溶解过程。对于年产50kt/a腈纶装置可减少一次性投资约1500万元，减少运转费用360万元／a，在现有腈纶大装置上实施，经济效益十分可观。     

N,N′-二(β-十八酰氧基)乙基乙二胺二乙酸钠的合成及性能研究

用 N,N′-二羟乙基乙二胺、氯乙酸钠合成了 N,N′-二羟乙基乙二胺二乙酸钠(中间体),中间体再与硬脂酰氯反应制备了一种新型 Gemini 两性表面活性剂 N,N′-二(β-十八酰氧基)乙基乙二胺二乙酸钠。对产物合成条件进行了考察,优化的反应条件为:n(硬脂酰氯):n(中间体)=2.5,溶剂 V(水):V(氯仿)=1:2,pH=9.0～10.0,反应温度15～20℃,反应时间5 h。通过红外光谱和质谱分析确定了产物结构,并测试了产物的表面性能。结果表明,在25℃时,该产物的临界胶束浓度为0.24 mmol/L,临界胶束浓度下的表面张力为35.7 mN/m;即时泡沫高度为250 mm,5 min 后泡沫高度为220 mm;乳化时间为22.48 min(甲苯-水物系)和4.65 min(正己烷-水物系),亲水-亲油平衡值为5.4,等电点为 pH 3.3～6.5。     

钢纤维聚合物混凝土抗压本构关系

钢纤维聚合物混凝土是由聚合物混凝土基体和钢纤维共同组成的纤维增强复合材料，它的力学行为不仅依赖于聚合物混凝土基体的行为，而且与钢纤维的掺量、分散特征以及钢纤维的几何尺寸有关，本文将基于损伤力学原理研究在不同纤维掺量下的钢纤维聚合物混凝土的全程压力-应变曲线及其本构模型。     

Microstructural investigation of long-term degradation mechanisms in GFRP dowel bars for jointed concrete pavement

Steel dowel bar is used to transfer loads in concrete pavement slab. However, once the steel dowel bar corrodes, it may cause faults, such as joint freezing in concrete pavement, level differences resulting from spalling or decreased efficiency of load transfer, etc., which are the same problems experienced by typical reinforcing steel. This study evaluated the applicability of glass fiber-reinforced polymer (GFRP) dowel bar as a substitute for steel dowel bar. A microstructural analysis was conducted to examine the decrease in durability of GFRP dowel bar exposed to deterioration environments. To analyze the deterioration mechanism of GFRP dowel bar, scanning electron microscopy was employed and the porosity was measured by the gas absorption method. It was concluded that the longer the GFRP dowel bar was exposed to deterioration environments, the more the interlaminar shear stress decreased. This result was validated by the microstructural analysis. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008