化学成分和固溶温度对1Cr17Mn9Ni4N不锈钢组织和性能的影响

为提高1Crl7Mn9Ni4N钢固溶处理后的力学性能(特别是钢的强度)，研究了化学成分及固溶处理温度对其组织和性能的影响。结果表明，1000—1125℃固溶处理后，该钢的组织为单相奥氏体。在标准成分范围内，随着镍、锰含量的增加，该钢的强度降低，塑性有所改善。氮明显提高该钢的强度。根据试验结果，每增加0．01％的氮钢的室温强度可提高大约5MPa，且塑性基本上不受影响。当合金成分(质量分数，％)控制在C0．08—0．12、Crl6．5—17．5、Ni3．5—4．2、Mn8．0—9．0、N0．22—0．28时，1Crl7Mn9Ni4N钢经1050—1100℃固溶处理后强度较高、塑性好，室温强度σ0．2和σb可分别达到400MPa和800MPa。     

Facile synthesis of nanocrystalline zinc ferrite via a self-propagating combustion method

Macroporous nanocrystalline zinc ferrite with single spinel-phase was prepared by a facile self-propagating combustion method using zinc nitrate, iron nitrate and glycine. The as-prepared ZnFe₂O₄ were characterized by X-ray diffraction (XRD) analysis, N₂ adsorption, scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED) and energy dispersive X-ray spectrum (EDS). The magnetic properties of the prepared ZnFe₂O₄ were also studied.     

巴彦浩特探区钻井液技术初探

巴彦浩特探区钻井液工艺技术的重点是，解决疏松砂砾岩地层水涌漏同层、侏罗系地层水的HCO3^-污染及可能出现的火成岩地层井塌复杂。结合内蒙古巴彦浩特探区地层和井身结构特点，采用了两性聚合物／氯化钾钻井液和氯化钾／石膏-聚磺钻井液体系。该体系抑制能力强，性能稳定．容易实现低固相、低密度近平衡钻井，保护储层效果好。对复杂情况采取了有针对性的处理办法：平稳操作和合理的钻井工程措施是预防水层涌漏同层和火成岩井塌复杂的重要手段；用井场易得的固井水泥或石膏配合烧碱处理HCO3^-污染简便易行；处理火成岩井塌复杂，控制合适的钻井液性能是必要的。     

钢带试样位向及拉伸性能的探讨

从碳素结构钢热轧钢带各向异性的事实出发 ,阐述不同试样位向导致同一钢带不同的拉伸性能 ,因而影响钢带合格与否的判定。在全面考虑钢带和焊管标准的基础上 ,提出解决钢带判定的两种方法。同时 ,还对标准中存在的缺点作了说明 ,提出改进意见 ,供标准修订时参考。     

模拟焊后热处理对锅炉用钢板SA-299力学性能的影响

对新日铁供货的SA-299钢板取样进行了供货状态及610～650℃/8h炉冷的模拟焊后热处理,以进行力学性能对比试验。试验结果表明,经过630℃/8h炉冷的模拟焊后热处理后σs降低25～40MPa、σb降低55～65MPa,但力学性能符合ASMESA-299标准和采购规程C1F19-98的要求。     

球式热风炉球床结构的热工讨论

球式热风炉作为低成本，高效率的冶金炉已被越来越多的钢铁企业所采用，广钢新3号高炉首次采用球式热风炉，炉子的球床结构，球径大小，材质的选择都将对球式热风炉的热工性能产生重要的影响。本文主要从热工理论方面探讨了球床结构的合理性。     

纤维体积分数对K3D/MCPA复合材料力学性能的影响

本文研究了纤维体积分数对三维编织芳纶纤维增强铸性尼龙(简称K3D／MCPA)复合材料力学性能的影响。研究表明，K3D／MCPA复合材料有优异的抗冲击性能，冲击强度比三维编织芳纶纤维增强铸性尼龙(简称C3D／MCPA)和纯基体均有大幅度的提高，且随着纤维体积的提高而升高。K3D／MCPA复合材料剪切强度随纤维体积比的增大而增大，其纵向剪切强度低于纯基体和C3D／MCPA复合材料，但其横向剪切强度高于它们。K3D／MCPA复合材料弯曲强度与弯曲模量随纤维体积比的提高而提高，但与相同体积比的C3D／MCPA相比，K3D／MCPA的弯曲强度与弯曲模量均较低。     

Crystalline Behavior and Magnetic Properties of Nd60Fe30-x Al10Cox（x = 0,5,10） Bulk Amorphous Alloys

Crystalline behavior and magnetic properties of Nd60Fe30-xAl10Cox( x = 0, 5, 10) bulk amorphous alloys were investigated by differential scanning calorimeter (DSC), X-ray diffraction (XRD) and the vibrating sample magnetometer (VSM). Neither glass transition nor supercooled liquid region before crystallization was observed for the as-cast Nd60Fe30-xAl10Cox ( x = 0,5,10) bulk amorphous alloys. The glass forming ability can be improved significantly by the addition of Co. The as-cast Nd60Fe30-xAl10Cox (x = 0,5,10) alloys show hard magnetic behavior. With the addition of Co content, intrinsic coercivity (iHc) increases while the saturation magnetization(σs) and remanence (σr) decrease. The Curie temperature for the as-cast Nd60Fe30-xAl10Cox alloys increases from 451 K for x =0 to 468 K for x = 10. Some pre-cipitation of crystalline phases does not affect the hard magnetic properties of Nd60Fe30-xAl10Cox(x = 0,5,10) alloys, while the hard magnetic behavior disappears quickly after the alloys being completely crystallized.     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

富县探区长6段油藏特征与勘探对策分析

富县探区三叠系延长组长6段普遍见到不同级别的油气显示,但试油未能获得工业油流.据分析,该区白垩纪末的抬升和翘倾运动使油气发生了第三次运移成藏,油、气、水重新分布并受储层物性控制.正确勾画出有利沉积相带、针对油藏特征采取更有效的工艺技术,是实现该区勘探突破的关键.